A study of SiC/Al composites fabricated by pressureless infiltration
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
SiC/Al composites with a high volume fraction of SiC were prepared at 1,150 oC by pressureless infiltration. The volume fraction of SiC was increased by decreasing the amount of starch in the green body. Both the microstructure and the strength of the composites were investigated. The results showed that the strength decreased with an increase of the particle size and volume fraction of SiC. It is suggested that the interface between the SiC particles, which were not sintered, are the cause of defects in the composites. The defects led to a decrease of the strength with an increase of the volume fraction of SiC.
Abstract
SiC/Al composites with a high volume fraction of SiC were prepared at 1,150 oC by pressureless infiltration. The volume fraction of SiC was increased by decreasing the amount of starch in the green body. Both the microstructure and the strength of the composites were investigated. The results showed that the strength decreased with an increase of the particle size and volume fraction of SiC. It is suggested that the interface between the SiC particles, which were not sintered, are the cause of defects in the composites. The defects led to a decrease of the strength with an increase of the volume fraction of SiC.
참고문헌 (7)
- H.S. Lee, , Mater.Sci. and Tech, 19(8), pp.1057~1064 (2003)
- Y. Cui, , Key Engineering Materials, 249, pp.45~48 (2003)
- N. Altinkok, , Composites Part A: Applied Science Manufacturing, 34(7), pp.577~582 (2003)
- B.S. Murty, , Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, pp.319~325 (2000)
- X. Sui, , The Chinese Journal of Nonferrous Metals, 9(1), pp.20~24 (1999)
- J.C. Romero, , Acta Metallurgica et Materialia, 43(2), pp.849~857 (1995)
- J.C. Viala, , J. Mater. Sci, 25(3), pp.1842~1850 (1990)