진공 플라즈마 스프레이 공정을 이용한 W계 복합 코팅층의 제조 및 특성 연구
Manufacturing and Properties of Low Vacuum Plasma Sprayed W-Carbide Hybrid Coating Layer
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
W-ZrC and W-HfC composite powders were fabricated by the Plasma Alloying & Spheroidization (PAS) method and the powders were sprayed into hybrid coating layers by using Low Vacuum Plasma Spray (LVPS) process, respectively. Microstructure, mechanical properties, and ablation characteristics of the fabricated coating layers were investigated. The LVPS process led to successful production of W-Carbide hybrid coatings,approximately 400 μm or above in thickness. As the substrate preheating temperature increased from 870℃ to 917℃, the hardness of the W-ZrC coating layer increased due to decreased porosity. Vickers hardness showed higher value (about 108.4 HV) in W-ZrC hybrid coating material compared to that of W-HfC while adhesive strength was found to be similar in both coating layers. The plasma torch test revealed good ablation resistance of the W-Carbide hybrid coating layers. The relatively high performance W-ZrC coating layer at the elevated temperature is thought to be attributed to both the strengthening effect of ZrC particle remained in the layer and the formation of ZrO_2 phase with high temperature stability.
Abstract
W-ZrC and W-HfC composite powders were fabricated by the Plasma Alloying & Spheroidization (PAS) method and the powders were sprayed into hybrid coating layers by using Low Vacuum Plasma Spray (LVPS) process, respectively. Microstructure, mechanical properties, and ablation characteristics of the fabricated coating layers were investigated. The LVPS process led to successful production of W-Carbide hybrid coatings,approximately 400 μm or above in thickness. As the substrate preheating temperature increased from 870℃ to 917℃, the hardness of the W-ZrC coating layer increased due to decreased porosity. Vickers hardness showed higher value (about 108.4 HV) in W-ZrC hybrid coating material compared to that of W-HfC while adhesive strength was found to be similar in both coating layers. The plasma torch test revealed good ablation resistance of the W-Carbide hybrid coating layers. The relatively high performance W-ZrC coating layer at the elevated temperature is thought to be attributed to both the strengthening effect of ZrC particle remained in the layer and the formation of ZrO_2 phase with high temperature stability.
참고문헌 (25)
- M. M. Opeka, , J. Mater. Sci, 39, pp.5887~ (2004)
- M. Gasch, , J. Mater. Sci, 39, pp.5925~ (2004)
- Stephen W. H. Yih, "Tungsten: Sources, Metallurgy, Properties and Application", pp.35~ (1979), Springer
- T. Zhang, , Mater. Sci. Eng, A474, pp.382~ (2008)
- G. M. Song, , Mater. Charact, 50, pp.293~ (2003)
- Chen B. L, , pp.65~ (1989), The Minerals, Metals and Materials Society
- A. Luo, , Acta metal, 40, pp.2225~ (1992)
- M. Q. Liu, , Mater. Sci. Eng, A160, pp.159~ (1993)
- T. Zhang, , Journal of Refractory Metals & Hard Materials, 27, pp.14~ (2009)
- M. M. Opeka, , J. of European Ceramic Society, 19, pp.2405~ (1999)
- G. M. Song, , Mater. Sci. Eng, A334 (2002)
- X. Liu, , J. Nuclear. Mater, 329, pp.687~ (2004)
- D. J. Varacalle, Jr., , Surf. Coat. Technol, 68, pp.86~ (1994)
- G. M. Song, , J. Mater. Sci. Eng, 36, pp.4625~ (2001)
- S. Tang, , Mater. Sci. Eng, 465, pp.1~ (2007)
- J. S. O’Dell, , PM2Tec Conference, pp.1~ (2001)
- K. A. Lee, , Proceedings of the 4th Asian Thermal Spray Conference, pp.350~ (2009), Asian Thermal Spray Society
- Sampath, S., , Mat. Sci. Eng, A348, pp.54~ (2003)
- Sampath, S., , Mat. Sci. Eng, A272, pp.181~ (1999)
- Staia, M. H., , Surf. Coat. Techno, 146, pp.563~ (2001)
- Ozkan Sarikaya, , Mater. Des, 26, pp.53~ (2005)
- 강현기, "대기 플라즈마 용사 공정으로 제조한 텅스턴 구리 복합재료", 대한금속·재료학회지, 42(1), pp.58~63 (2004), 대한금속·재료학회
- A. Sayir, , J. Mater. Sci, 39, pp.5995~ (2004)
- C. Z. Ke, , Applied Surf. Sci, 255, pp.9217~ (2009)
- X. Li, , Materials Letters, 60, pp.892~ (2006)