Properties and rapid consolidation of binderless nanostuctured tantalum carbide by pulsed current activated sintering
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The grain size of TaC decreases with an increase in ball mliing time. Nanopowder of TaC was fabricated by high energy ball milling for 10 h. A densely pure TaC hard material with a relative density of up to 96% was produced with simultaneous application of 80 MPa pressure and pulsed current within 2 minutes. The density and hardness of TaC increased with a decrease in the initial TaC powder size. The fracture toughness and hardness values of TaC obtained from 10 h milled powder were 6.8MPa.m1/2 and 2076 kg/mm2, respectively under 80 MPa pressure and with a pulsed current of 2800A.
Abstract
The grain size of TaC decreases with an increase in ball mliing time. Nanopowder of TaC was fabricated by high energy ball milling for 10 h. A densely pure TaC hard material with a relative density of up to 96% was produced with simultaneous application of 80 MPa pressure and pulsed current within 2 minutes. The density and hardness of TaC increased with a decrease in the initial TaC powder size. The fracture toughness and hardness values of TaC obtained from 10 h milled powder were 6.8MPa.m1/2 and 2076 kg/mm2, respectively under 80 MPa pressure and with a pulsed current of 2800A.
참고문헌 (20)
- O.Y. Khyzhun, , J. Electron Spectrosc. Relat. Phenom., 82, pp.179~185 (1996)
- S.T. Oyama, "Introduction to the chemistry of transition metal carbides and nitrides" (1996), Blackie Academic and Professional
- Y.J. Chen, , Mater. Lett., 56, pp.279~284 (2002)
- H. Suzuki, "Cemented Carbide and Sintered Hard Materials" (1986), Maruzen
- M. Sherif El-Eskandarany, , J. Alloys & Compounds, 305, pp.225~230 (2000)
- L. Fu, , Scripta Materialia, 44, pp.1061~1065 (2001)
- K. Niihara, "Advanced structural Inorganic Composite" (1990), Elsevier Scientific Publishing Co.
- S. Berger, , Progress in Materials, 42, pp.311~322 (1997)
- Z. Fang, , Int. J. of Refractory Met. & Hard Mater., 13, pp.297~302 (1995)
- 손인진, "Properties and Consolidation of Nanostructured Ce0.8Gd0.2O1.9 by Pulsed-Current-Activated Sintering", Metals and Materials International, 14(5), pp.593~598 (2008), 대한금속·재료학회
- Byung-Ryang Kim, "Rapid synthesis and consolidation of TiSi2 by pulsed current activated combustion", Journal of Ceramic Processing Research, 10(2), pp.171~175 (2009), 세라믹공정연구센터
- M. Sommer, , Int. J. of Refractory Met. & Hard Mater, 20, pp.41~46 (2002)
- 손인진, "Properties and Consolidation of Nanostructured Ce0.8Gd0.2O1.9 by Pulsed-Current-Activated Sintering", Metals and Materials International, 14(5), pp.593~598 (2008), 대한금속·재료학회
- S.K Bae, , Scripta Materialia, 58, pp.425~429 (2008)
- C. Suryanarayana, "X-ray Diffraction A Practical Approach" (1998), Plenum Press
- Z. Shen, , J. Am. Ceram. Soc., 85, pp.1921~1927 (2002)
- J.E. Garay, , Appl. Phys. Lett, 85, pp.573~577 (2004)
- J.R. Friedman, , Intermetallics, 12, pp.589~596 (2004)
- J.E. Garay, , Acta Mater, 51, pp.4487~4493 (2003)
- G.R. Anstis, , J. Am. Ceram. Soc., 64, pp.533~539 (1981)