Properties and rapid consolidation of binderless nanostuctured Ti (C, N) by pulsed current activated sintering
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The grain size of Ti (C, N) decreases with an increase in ball milling time. Ti (C, N) nanopowder was fabricated by high energy ball milling for 10 h. The rapid sintering of nanostuctured Ti (C, N) hard materials was investigated with pulsed current activated sintering via a heating sintering process. The advantage of this process is that it allows very quick densification to near theoretical density and prohibition of grain growth in nanostuctured materials. A dense nanostructured Ti (C, N) hard material with a relative density of up to 98% was produced with simultaneous application of 80 MPa pressure and a pulsed current of 2700 A within 3 minutes. The effect of ball milling time on the sintering behavior, grain size and mechanical properties of binderless Ti (C, N) was investigated.
Abstract
The grain size of Ti (C, N) decreases with an increase in ball milling time. Ti (C, N) nanopowder was fabricated by high energy ball milling for 10 h. The rapid sintering of nanostuctured Ti (C, N) hard materials was investigated with pulsed current activated sintering via a heating sintering process. The advantage of this process is that it allows very quick densification to near theoretical density and prohibition of grain growth in nanostuctured materials. A dense nanostructured Ti (C, N) hard material with a relative density of up to 98% was produced with simultaneous application of 80 MPa pressure and a pulsed current of 2700 A within 3 minutes. The effect of ball milling time on the sintering behavior, grain size and mechanical properties of binderless Ti (C, N) was investigated.
참고문헌 (22)
- O. Yu. Khyzhun, , J. Electron Spectrosc. Relat. Phenom, 82, pp.179~185 (1996)
- S.T. Oyama, "Introduction to the chemistry of transition metal carbides and nitrides" (1996), Blackie Academic and Professional
- S. Imasato, , Int. J. of Refract. Met. and Hard Mater, 13, pp.305~312 (1995)
- H. Suzuki, "Cemented Carbide and Sintered Hard Materials" (1986), Maruzen
- M. Sherif El-Eskandarany, , J. Alloys & Compounds, 305, pp.225~230 (2000)
- L. Fu, , Scripta Materialia, 44, pp.1061~1065 (2001)
- K. Niihara, "Advanced structural Inorganic Composite" (1990), Elsevier Scientific Publishing Co.
- S. Berger, , Progress in Materials, 42, pp.311~322 (1997)
- Z. Fang, , Int. J. of Refractory Met. & Hard Mater., 13, pp.297~302 (1995)
- S. L. Du, , 49, pp.231~236 (2011)
- Byung-Ryang Kim, "Rapid synthesis and consolidation of TiSi2 by pulsed current activated combustion", Journal of Ceramic Processing Research, 10(2), pp.171~175 (2009), 세라믹공정연구센터
- S. C. Liao, , Acta Mater, 45, pp.4027~4032 (1997)
- Z.Q. Jin, , Mater Sci Forum, 465-466, pp.93~97 (2004)
- V. Ivanov, , Key Eng Mater, 206-213, pp.377~381 (2002)
- 강현수, "Properties and Rapid Low-Temperature Consolidation of Nanocrystalline Fe-ZrO_2 Composite by Pulsed Current Activated Sintering", Metals and Materials International, 17(1), pp.57~62 (2011), 대한금속·재료학회
- 고인용, "Consolidation of a nanostructured Al2O3 reinforced Fe- Cr composite by rapid sintering and its mechanical properties", Journal of Ceramic Processing Research, 12(1), pp.70~73 (2011), 세라믹공정연구센터
- C. Suryanarayana, "X-ray Diffraction A Practical Approach" (1998), Plenum Press
- Z. Shen, , J. Am. Ceram. Soc., 85, pp.1921~1927 (2002)
- J. E. Garay, , Appl. Phys. Lett., 85, pp.573~577 (2004)
- J. R. Friedman, , Intermetallics., 12, pp.589~596 (2004)
- J. E. Garay, , Acta Mater., 51, pp.4487~4493 (2003)
- K. Niihara, , J. Mater. Sci. Lett., 1, pp.12~16 (1982)