Consolidation and mechanical properties of ultra fine WC-5 wt.% carbides hard materials by a rapid sintering method
2
조회
0
다운로드
4
인용
0
참고문헌
키워드
초록
Using the pulsed current activated sintering method, WC-5 wt.% carbides hard materials were densified using an ultra-fine WC-NbC, TaC, TiC and ZrC powder. The WC-carbides were nearly completely dense with a relative density of up to 99% after the simultaneous application of 60 MPa of pressure and about 10 minutes of electric current without significant change in the grain size. The average grain size of WC that was produced through PCAS was approximately 500 nm. The hardness and fracture toughness of the dense WC-Carbide composites were also investigated.
Abstract
Using the pulsed current activated sintering method, WC-5 wt.% carbides hard materials were densified using an ultra-fine WC-NbC, TaC, TiC and ZrC powder. The WC-carbides were nearly completely dense with a relative density of up to 99% after the simultaneous application of 60 MPa of pressure and about 10 minutes of electric current without significant change in the grain size. The average grain size of WC that was produced through PCAS was approximately 500 nm. The hardness and fracture toughness of the dense WC-Carbide composites were also investigated.
참고문헌 (21)
- P. Schwartzkopf, "Refractory Hard MetalsBoride, Carbide, Nitride and Silicide" (1953), MacMillan
- L.E. Toth, "Transition Metal Carbides and Nitrides" (1971), Academic Press
- L. Leclercq, , J. Catalysis, 117, pp.371~383 (1989)
- M.J. Ledoux, , J. Catalysis, 134, pp.383~398 (1992)
- L. Volpe, , J. Solid State Chem, 59, pp.348~356 (1985)
- R. Koc, , J. Eur. Ceram. Soc, 20, pp.1859~1869 (2000)
- S. Imasato, , Int. Refract. Met. Hard Mater, 13, pp.305~312 (1995)
- H. Engqvist, , Tribol. Lett, 4, pp.251~258 (1998)
- M. P. Harmer, , J. Br. Ceram. Soc, 80, pp.147~149 (1981)
- A. Morell, , Bull. Am. Ceram. Soc, 59, pp.626~629 (1980)
- 김원백, "기계적 합성된 분말로부터 펄스전류활성 소결에 의한 나노구조 1.5TiAl-Al_2O_3 복합재료 제조 및 기계적 특성", 대한금속·재료학회지, 50(4), pp.310~315 (2012), 대한금속·재료학회[DOI]
- 두송이, "기계적 합성된 분말로부터 펄스전류 활성 소결에 의한 나노구조 3FeAl-Al_2O_3 복합재료 제조 및 기계적 특성", 대한금속·재료학회지, 50(6), pp.449~454 (2012), 대한금속·재료학회[DOI]
- 고인용, "고주파유도 가열에 의한 나노구조 MoSi_2-TaSi_2 복합재료 제조 및 기계적 특성", 대한금속·재료학회지, 50(5), pp.369~374 (2012), 대한금속·재료학회[DOI]
- F.L. Zhang, , Scripta Mater, 49, pp.1123~1128 (2003)
- Jia K, , Nanostruct Mater, 10, pp.875~891 (1998)
- J. H. Han, , Acta Mater, 46, pp.2021~2028 (1998)
- H. C. Kim, , International Journal of Refractory Metals & Hard Materials, 26, pp.48~54 (2008)
- S. Imasato, , International Journal of Refractory Metals & Hard Materials, 13, pp.305~312 (1997)
- K. Niihara, , J. Mater. Sci. Lett, 1, pp.12~16 (1982)
- E. A. Almond, , Mat. Sci. Eng. A, 105, pp.237~248 (1988)
- H. C. Kim, , Int. J. Ref. Met. & Hard Mat, 24, pp.427~431 (2006)