Oxidation of CrAlN thin films at 800 οC and 900 οC in air
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
CrAlN films with a composition of 31.3Cr-12.9Al-55.3 N (at.%) were deposited on steels by closed field unbalanced magnetron sputtering to a thickness of 1.2 µm. They consisted of dense, polycrystalline CrN and AlN fine columns. Their oxidation characteristics were studied at 800 ο C and 900 ο C for up to 20 h in air. The formed oxides consisted primarily of crystalline Cr2O3 incorporated with Al2O3. The amount of Al in the film was not large enough to precipitate out Al2O3 from Cr2O3. The oxide layers were thin and compact so as to make CrAlN films more protective than CrN films. During oxidation, Cr, Al and nitrogen diffused outward, whereas oxygen diffused inward. At the same time, Fe diffused outward from the substrate toward the outermost oxide surface owing to the concentration gradient.
Abstract
CrAlN films with a composition of 31.3Cr-12.9Al-55.3 N (at.%) were deposited on steels by closed field unbalanced magnetron sputtering to a thickness of 1.2 µm. They consisted of dense, polycrystalline CrN and AlN fine columns. Their oxidation characteristics were studied at 800 ο C and 900 ο C for up to 20 h in air. The formed oxides consisted primarily of crystalline Cr2O3 incorporated with Al2O3. The amount of Al in the film was not large enough to precipitate out Al2O3 from Cr2O3. The oxide layers were thin and compact so as to make CrAlN films more protective than CrN films. During oxidation, Cr, Al and nitrogen diffused outward, whereas oxygen diffused inward. At the same time, Fe diffused outward from the substrate toward the outermost oxide surface owing to the concentration gradient.
참고문헌 (17)
- 김명근, "Synthesis and Characterization of Multilayer CrN", ZrN Coatings, 2008, pp.14(4), 465~470[DOI]
- 김광호, "Fabrication and Properties of AlN Film on GaN Substrate by Using Remote Plasma Atomic Layer Deposition Method", Electronic Materials Letters, 5(2), pp.83~86 (2009), 대한금속·재료학회
- A. Aubert, , Thin Solid Films, 126, pp.61~ (1985)
- W. D. Münz, , Surf. Eng, 3, pp.47~ (1987)
- B. Navinšek, , Surf. Coat. Technol, 74, pp.155~ (1995)
- I. Milosev, , Surf. Coat. Technol, 74, pp.897~ (1995)
- O. Banakh, , Surf. Coat. Technol, 163, pp.57~ (2003)
- M. Zhu, , Surf. Coat. Technol, 201, pp.2878~ (2006)
- A. E. Reiter, , J. Vac. Sci. Technol. A, 25, pp.711~ (2007)
- M. Kawate, , Surf. Coat. Technol, 165, pp.163~ (2003)
- Y. C. Chim, , Thin Solid Films, 517, pp.4845~ (2009)
- J. Lin, , Surf. Coat. Technol, 202, pp.3272~ (2008)
- K. Yamamoto, , Surf. Coat. Technol, 200, pp.1383~ (2005)
- Y. Makino, , Surf. Coat. Technol, 98, pp.1008~ (1998)
- N. Birbilis, , Surf. Coat. Technol, 201, pp.4505~ (2007)
- G. Simkovich, , Oxid. Met, 44, pp.501~ (1995)
- N. Birks, "Introduction to the High-Temperature of Metals" (2006), Cambridge University Press