Effects of rod-like BN on dielectric and mechanical properties of Si3N4 porous composite prepared via gelcasting method
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Gel-casting is an appropriate method for manufacturing porous parts with complicated forms, which has also been used in shaping Si3N4 bodies. In the present study, porous bulk Si3N4 samples were fabricated using gel-casting. To this aim Si3N4 slurries were prepared with solid loading of 35 vol%. To the slurry was added 1 and 3 wt% rod-like BN to enhance the mechanical properties. BN was selected to further reduce the dielectric constant and loss of the prepared porous Si3N4 samples. The findings suggested that employing rod-like BN increased the porosity from 38 % to 41 %, reducing the flexural strength from 77 MPa in the part without BN to 56 MPa in the part containing 3 wt% BN. On the other hand, dielectric properties reduced in the parts with BN compared with the part without BN.
Abstract
Gel-casting is an appropriate method for manufacturing porous parts with complicated forms, which has also been used in shaping Si3N4 bodies. In the present study, porous bulk Si3N4 samples were fabricated using gel-casting. To this aim Si3N4 slurries were prepared with solid loading of 35 vol%. To the slurry was added 1 and 3 wt% rod-like BN to enhance the mechanical properties. BN was selected to further reduce the dielectric constant and loss of the prepared porous Si3N4 samples. The findings suggested that employing rod-like BN increased the porosity from 38 % to 41 %, reducing the flexural strength from 77 MPa in the part without BN to 56 MPa in the part containing 3 wt% BN. On the other hand, dielectric properties reduced in the parts with BN compared with the part without BN.
참고문헌 (14)
- G. Ziegler, , Journal of Material Science, 22(9), pp.3041~3086 (1987)
- Aleksander J. Pyzik, "Microstructure and Properties of Self-Reinforced Silicon Nitride", Journal of the American Ceramic Society, 76(11), pp.2737~2744 (1993), Wiley[DOI]
- T. Wan, , Internatinal Journal Application Ceramics Technology, 12(5), pp.932~938 (2015)
- D. Zhao, , Journal of Nanomaterials (2011)[DOI]
- A. Kovalcková, , Journal of the European Ceramic Society, 34, pp.3319~3328 (2014)
- S. Wang, , Ceramics International, 3, pp.4231~4237 (2013)
- X. Li, , International Journal of Applied Ceramic Technology, 8(3), pp.627~636 (2011)
- N. Long, , Ceramics International, 38, pp.2381~2387 (2012)
- M. Vaseghi, "Effect of BN whisker-like additive on the flexural strength of Si3N4 ceramics prepared by gel casting method", Journal of Ceramic Processing Research, 20(2), pp.121~126 (2019), 청정에너지연구소[DOI]
- D. Yao, , Journal of the American Ceramic Society, 94(3), pp.666~670 (2011)
- T. Wan, , International Journal of Applied Ceramic Technology, 12(5), pp.932~938 (2015)
- D. Zhao, , Journal of Nanomaterials (2011)[DOI]
- D. Bučevac, , Science of Sintering, 40, pp.263~270 (2008)
- L. Shuqin, , Ceramics International, 35, pp.1851~1854 (2009)