Electrocaloric properties of BaTiO3/La0.7Sr0.3MnO3/BaTiO3 multilayer thin films prepared by chemical solution deposition
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
BaTiO3/La0.7Sr0.3MnOs/BaTiO3 multilayer films are fabricated using the chemical solution deposition and spin-coatingmethod. The upper BT film exhibits an average grain size of approximately 42 nm, indicating a uniform and dense microstructure. The single-coated film has an average thickness ranging from 40 to 45 nm. A phase transition temperature of approximately4 °C is observed in all films. The BT/LSMO/BT multilayer film, coated with LSMO four times, demonstrates amaximum dielectric constant of 2008 at 20 °C. The BT/LSMO/BT multilayer film, coated with LSMO two times, shows a ΔTof 0.59 K at 24 °C. The remnant polarization, coercive field, and ΔT/ΔE of the BT/LSMO/BT multilayer film, coated withLSMO four times, are 19.8 μC/cm2, 42 kV/cm, and 4.56 mKcm/kV, respectively.
Abstract
BaTiO3/La0.7Sr0.3MnOs/BaTiO3 multilayer films are fabricated using the chemical solution deposition and spin-coatingmethod. The upper BT film exhibits an average grain size of approximately 42 nm, indicating a uniform and dense microstructure. The single-coated film has an average thickness ranging from 40 to 45 nm. A phase transition temperature of approximately4 °C is observed in all films. The BT/LSMO/BT multilayer film, coated with LSMO four times, demonstrates amaximum dielectric constant of 2008 at 20 °C. The BT/LSMO/BT multilayer film, coated with LSMO two times, shows a ΔTof 0.59 K at 24 °C. The remnant polarization, coercive field, and ΔT/ΔE of the BT/LSMO/BT multilayer film, coated withLSMO four times, are 19.8 μC/cm2, 42 kV/cm, and 4.56 mKcm/kV, respectively.
참고문헌 (21)
- P. Kobeko, , Z. Phys, 66(3-4), pp.195~205 (1930)
- A. S. Mischenko, , Science, 311(5765), pp.1270~1271 (2006)
- X. Wei, , Acta Materialia, 227, pp.117735~ (2022)
- Jeong-Eun Lim, "Structural and electrical properties of K(Ta0.62Nb0.38)O3", BiFeO3 multilayer films for electrocaloric devices, 2022, pp.23(5), 583~588[DOI]
- N. Tanwar, , J. of Solid State Chem, 317(1), pp.123674~ (2023)
- Dwita Suastiyanti, "Enhancing the electrical properties of multiferroic materials based on variations in BiFeO3-BaTiO3 weight ratio", Journal of Ceramic Processing Research, 22(1), pp.61~65 (2021), 청정에너지연구소[DOI]
- J. Heremans, , J. Phys. D : Appl. Phys, 26(8), pp.1149~1168 (1993)
- Y. Kim, , Nat. Mater, 13(11), pp.1019~1025 (2014)
- K. Das, , Sci. Rep, 6(3), pp.20351~ (2016)
- 임정은, "서미스터로의 응용을 위한 La0.7Sr0.3MnO3 박막의 구조적, 전기적 특성", 전기전자재료학회논문지, 35(5), pp.499~503 (2022), 한국전기전자재료학회
- G. Akcay, , Jr. Appl. Phys. Lett, 90(25), pp.252909~ (2007)
- Min-Su Kwon, "Structural and electrical properties of K(Ta,Nb)O3 thin film prepared by sol-gel method for electrocaloric devices", Journal of Ceramic Processing Research, 21(6), pp.725~730 (2020), 청정에너지연구소[DOI]
- R. A. Rao, , J. Appl. Phys, 85(8), pp.4794~4796 (1999)
- B. Jaffe, "Piezoelectric Ceramics", pp.54~ (1971), Academic press
- W. Chung, , Jap. J. Appl. Phys, 45(10R), pp.7801~7805 (2006)
- S. B. Majumder, , A. Phys. Lett, 79(2), pp.239~241 (2001)
- J. Guo, , J. Alloys and Comp, 910, pp.164928~ (2022)
- Y. He, , Thermochemica Acta, 419(1-2), pp.135~141 (2004)
- M. Saleem, , RSC Adv, 8, pp.1600~1609 (2018)
- H. Maiwa, , Jap. J. Appl. Phys, 56(10S), pp.10PC05~ (2017)
- B. Neese, , Science, 321(5890), pp.821~823 (2008)