금속분말사출성형법으로 제조된 WC-10Co계 초경합금 소결체의 탄소첨가량에 따른 특성변화
The Characteristic Changes of Sintered WC-10Co Fabricated by PIM Method with Different Carbon Content
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In order to investigate the microstructure and mechanical properties of WC-10 wt% Co insert tool alloy fabricated by PIM (Powder Injection Molding) process, the feedstock of WC-10 wt% and wax used as a kind of binder were mixed together by two blade mixer. After injection molding, the debinding process was carried out by two-steps. First, solvent extraction, in which the binder was eliminated by putting the specimen into normal hexane for 24 hrs at 60℃, and subsequently thermal debinding which was conducted at 260℃ and 480℃ for 6 hrs in the mixed gas of H_2/N_2, respectively. Meantime, in order to compensate the decarburization due to hydrogen,1.2~1.8% of carbon was added to ensure the integrity of the phase. Finally, the specimens were sintered in vacuum under different temperatures, and the relative density of 99.8% and hardness of 2100 Hv can be achieved when sintered at 1380℃, even the TRS is lower than the conventional sintering process.
Abstract
In order to investigate the microstructure and mechanical properties of WC-10 wt% Co insert tool alloy fabricated by PIM (Powder Injection Molding) process, the feedstock of WC-10 wt% and wax used as a kind of binder were mixed together by two blade mixer. After injection molding, the debinding process was carried out by two-steps. First, solvent extraction, in which the binder was eliminated by putting the specimen into normal hexane for 24 hrs at 60℃, and subsequently thermal debinding which was conducted at 260℃ and 480℃ for 6 hrs in the mixed gas of H_2/N_2, respectively. Meantime, in order to compensate the decarburization due to hydrogen,1.2~1.8% of carbon was added to ensure the integrity of the phase. Finally, the specimens were sintered in vacuum under different temperatures, and the relative density of 99.8% and hardness of 2100 Hv can be achieved when sintered at 1380℃, even the TRS is lower than the conventional sintering process.
참고문헌 (12)
- Baiyun Huang, , J. Mater. Proc. Tech, 137, pp.132~ (2003)
- ASM International, "ASM Metals Handbook-Powder Metal Technologies and Applications (9th ed.), 7", pp.385~ (1998)
- MPIF, "Standard Test Methods for Metal Powders and Powder Metallurgy Products-standard 41, (2010 ed.)" (2010), MPIF
- R. Kitakawa, "Recent trends of coated tool", Mach. Tool, 33, pp.27~ (1989)
- H. S. Kalish, "Status report: cutting tool materials", Met. Prog, 124, pp.21~ (1983)
- Yoshimitsu Kankawa, "USA, US 6051184", ~ (2000)
- D.-G. Ahn, , J. Korean Society for Nondestructive Testing, 20, pp.438~ (2000)
- R. M. German, "Powder Injection Molding" (1990), MPIF
- R. M. German, "Sintering Theory and Practice" (1996), John Wiley & Sons, INC
- M. Leiderman, , Powder Metall, 4, pp.219~ (1997)
- O. Pacher, , Powder Metall, 4, pp.189~ (1980)
- S. H. Choi, , Research on Chemical Intermediates, 36, pp.743~ (2010)