소결조제 변화에 따른 텅스텐카바이드 소결체 특성평가
Property Evaluation of Tungsten-Carbide Hard Materials as a Function of Binder
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Tungsten carbide (WC) hard materials are used in various industries and possess a superior hardness compared to other hard materials. They have particularly high melting points, high strength, and abrasion resistance. Accordingly, tungsten carbide hard materials are used for wear-resistant tools, cutting tools, machining tools, and other tooling materials. In this study, the WC-5wt.%Co, Fe, Ni hard materials are densified using the horizontal ball milled WC-Co, WC-Fe, and WC-Ni powders by a spark plasma sintering process. The WC-5Co, WC-5Fe, and WC-5Ni hard materials are almost completely densified with a relative density of up to 99.6% after simultaneous application of a pressure of 60 MPa and an electric current for about 15 min without any significant change in the grain size. The average grain size of WC-5Co, WC-5Fe, and WC-5Ni that was produced through SPS was about 0.421, 0.779, and 0.429 μm, respectively. The hardness and fracture toughness of the dense WC-5Co, WC-5Fe, WC-5Ni hard materials were also investigated.
Abstract
Tungsten carbide (WC) hard materials are used in various industries and possess a superior hardness compared to other hard materials. They have particularly high melting points, high strength, and abrasion resistance. Accordingly, tungsten carbide hard materials are used for wear-resistant tools, cutting tools, machining tools, and other tooling materials. In this study, the WC-5wt.%Co, Fe, Ni hard materials are densified using the horizontal ball milled WC-Co, WC-Fe, and WC-Ni powders by a spark plasma sintering process. The WC-5Co, WC-5Fe, and WC-5Ni hard materials are almost completely densified with a relative density of up to 99.6% after simultaneous application of a pressure of 60 MPa and an electric current for about 15 min without any significant change in the grain size. The average grain size of WC-5Co, WC-5Fe, and WC-5Ni that was produced through SPS was about 0.421, 0.779, and 0.429 μm, respectively. The hardness and fracture toughness of the dense WC-5Co, WC-5Fe, WC-5Ni hard materials were also investigated.
참고문헌 (15)
- H. C. Kim, , Ph D., pp.2005
- H. C. Kim, , J. Mater. Sci, 40, pp.2849~ (2005)
- H. C. Kim, , Int. J. Refract. Met. and Hard Mater, 22, pp.197~ (2004)
- H. C. Kim, , Ceram. Int, 34, pp.1419~ (2008)
- Z. Shen, , J. Am. Ceram. Soc, 85, pp.1921~ (2002)
- J. E. Garay, , Appl. Phys. Lett, 85, pp.573~ (2004)
- J. R. Friedman, , Intermetallics, 12, pp.589~ (2004)
- J. E. Garay, , Acta Mater, 51, pp.4487~ (2003)
- Hwan-Cheol Kim, "Rapid Sintering of Nanocrystalline 8 mol.%Y2O3-Stabilized ZrO2 by High-Frequency Induction Heating Method", Metals and Materials International, 12(5), pp.393~398 (2006), 대한금속·재료학회
- K. Jia, , Nanostruct. Mater, 10, pp.875~ (1998)
- J. H. Han, , Acta Mater, 46, pp.2021~ (1998)
- 정인균, "급속 소결 공정에 의한 초미립 WC_10Co와 WC-10Fe 초경재료 제조와 기계적 성질", 대한금속·재료학회지, 46(4), pp.223~226 (2008), 대한금속·재료학회
- M. J. Ledoux, , J. Catal, 134, pp.383~ (1992)
- C. Suryanarayana, "X-ray diffraction a practical approach" (1998), Plenum Press
- G. R. Anstis, , J. Am. Ceram. Soc, 64, pp.533~ (1981)