WC/Co 초경합금 스크랩 산화물로부터 환원/침탄공정에 의한 WC/Co 복합분말 제조
Fabrication of WC/Co composite powder from oxide of WC/Co hardmetal scrap by carbothermal reduction process
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
This study focuses on the fabrication of a WC/Co composite powder from the oxide of WC/Co hardmetal scrap using solid carbon in a hydrogen gas atmosphere for the recycling of WC/Co hardmetal. Mixed powders are manufactured by mechanically milling the oxide powder of WC-13 wt% Co hardmetal scrap and carbon black with varying powder/ball weight ratios. The oxide powder of WC-13 wt% Co hardmetal scrap consists of WO3 and CoWO4. The mixed powder mechanically milled at a lower powder/ball weight ratio (high mechanical milling energy) has a more rapid carbothermal reduction reaction in the formation of WC and Co phases compared with that mechanically milled at a higher powder/ball weight ratio (lower mechanical milling energy). The WC/Co composite powder is fabricated at 900oC for 6 h from the oxide of WC/Co hardmetal scrap using solid carbon in a hydrogen gas atmosphere. The fabricated WC/Co composite powder has a particle size of approximately 0.25-0.5 μm.
Abstract
This study focuses on the fabrication of a WC/Co composite powder from the oxide of WC/Co hardmetal scrap using solid carbon in a hydrogen gas atmosphere for the recycling of WC/Co hardmetal. Mixed powders are manufactured by mechanically milling the oxide powder of WC-13 wt% Co hardmetal scrap and carbon black with varying powder/ball weight ratios. The oxide powder of WC-13 wt% Co hardmetal scrap consists of WO3 and CoWO4. The mixed powder mechanically milled at a lower powder/ball weight ratio (high mechanical milling energy) has a more rapid carbothermal reduction reaction in the formation of WC and Co phases compared with that mechanically milled at a higher powder/ball weight ratio (lower mechanical milling energy). The WC/Co composite powder is fabricated at 900oC for 6 h from the oxide of WC/Co hardmetal scrap using solid carbon in a hydrogen gas atmosphere. The fabricated WC/Co composite powder has a particle size of approximately 0.25-0.5 μm.
참고문헌 (21)
- K. J. A. Brookes, "World Directory and Handbook of Hardmetals and Hard Materials", pp.9~ (1996), International Carbide Data
- K. Halada, , J. Jpn. Soc. Powder & Powder Metall., 57, pp.87~ (2010)[DOI]
- 정진기, "特許와 論文으로 본 텅스텐카바이드(WC) 再活用 技術 動向", 자원리싸이클링, 21(1), pp.82~92 (2012), 한국자원리싸이클링학회
- C. S. Freemantle, , Int. J. Refract. Met. Hard Mater., 44, pp.94~ (2014)[DOI]
- E. Lassner, "Tungsten. Properties, Chemistry, Technology of the Element, Alloys and Chemical Compound", pp.137~ (1999), Kluwer Academic
- T. Kojima, , J. Mater. Sci., 40, pp.5167~ (2005)[DOI]
- V. V. Malyshev, , Theor. Found. Chem. Eng., 41, pp.436~ (2007)[DOI]
- S. Wongsisa, , Mater. Trans., 56, pp.70~ (2015)[DOI]
- 이길근, "WC", Co 초경 스크랩 산화물의 고체탄소에 의한 환원, 한국분말재료학회지, pp.2005, 12(2)[DOI]
- G. G. Lee, "PM Tool Materials", Euro PM2004 Proc., 3, pp.403~ (2004)
- 이길근, "Effects of Mechanical Milling on the Carbothermal Reduction of Oxide of WC", Co Hardmetal Scrap, 2016, pp.22(2), 260~266[DOI]
- 권철민, "WC", Co 초경 스크랩 산화물의 환원, 대한금속·재료학회지, pp.2016, 54(10)[DOI]
- G. K. Williamson, , Acta Metall., 1, pp.22~ (1953)[DOI]
- K. Venkateswarlu, , Physica B, 405, pp.4256~ (2010)[DOI]
- N. Burgio, , Il Nuovo Cimento D, 13, pp.459~ (1991)[DOI]
- H. K. Khoa, , J. Korean Powder. Metall. Inst., 21, pp.155~ (2014)[DOI]
- P. R. Santhanam, , Chem. Eng. Sci., 101, pp.366~ (2013)[DOI]
- P. R. Santhanam, , Powder. Technol., 221, pp.403~ (2012)[DOI]
- 정해영, "기계적 밀링공정에 의한 은 플레이크 분말 제조", 한국분말재료학회지, 23(1), pp.54~60 (2016), 한국분말재료학회
- R. Abbaschian, "Physical Metallurgy Principles", pp.348~ (2010), Cengage Learning
- Zoya Sadighi, "Synthesis of Nano-Structured La0.8Ba0.2MnO3 Perovskite via a Mechano-Thermal Route", Metals and Materials International, 20(1), pp.77~81 (2014), 대한금속·재료학회[DOI]