Fabrication of Fe-TiC Composite by High-Energy Milling and Spark-Plasma Sintering
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Fe-TiC composite was fabricated from Fe and TiC powders by high-energy milling and subsequent sparkplasma sintering. The microstructure, particle size and phase of Fe-TiC composite powders were investigated by field emission scanning electron microscopy and X-ray diffraction to evaluate the effect of milling conditions on the size and distribution of TiC particles in Fe matrix. TiC particle size decreased with milling time. The average TiC particle size of 38 nm was obtained after 60 minutes of milling at 1000 rpm. Prepared Fe-TiC powder mixture was densified by sparkplasma sintering. Sintered Fe-TiC compacts showed a relative density of 91.7~96.2%. The average TiC particle size of 150 nm was observed from the FE-SEM image. The microstructure, densification behavior, Vickers hardness, and fracture toughness of Fe-TiC sintered compact were investigated.
Abstract
Fe-TiC composite was fabricated from Fe and TiC powders by high-energy milling and subsequent sparkplasma sintering. The microstructure, particle size and phase of Fe-TiC composite powders were investigated by field emission scanning electron microscopy and X-ray diffraction to evaluate the effect of milling conditions on the size and distribution of TiC particles in Fe matrix. TiC particle size decreased with milling time. The average TiC particle size of 38 nm was obtained after 60 minutes of milling at 1000 rpm. Prepared Fe-TiC powder mixture was densified by sparkplasma sintering. Sintered Fe-TiC compacts showed a relative density of 91.7~96.2%. The average TiC particle size of 150 nm was observed from the FE-SEM image. The microstructure, densification behavior, Vickers hardness, and fracture toughness of Fe-TiC sintered compact were investigated.
참고문헌 (22)
- Hugh O. Pierson, "Handbook of Refractory Carbides and Nitrides: properties, characteristics, processing, and applications", pp.1996, William Andrew Publishing
- T. K. Bandyopadhyay., , J. Mater. Sci, 39, pp.6503~ (2004)
- E. Pagounis., , Metall. Mater. Trans. A, 27A, pp.4171~ (1996)
- Wang Jing., , Materials Letters, 61(22), pp.4393~ (2007)
- B. S. Terry., , J. Mater. Sci. Lett, 10, pp.628~ (1991)
- M. Razavi., , Int. J. Miner. Process, 94, pp.97~ (2010)
- I. W. M. Brown, "Fabrication, microstructure and properties of Fe-TiC ceramic-metal composites", Current Applied Physics, 4(2-4), pp.171~174 (2004), 한국물리학회
- K. S. Vecchio., , Metall. Trans. A, 23, pp.87~ (1992)
- Y. Choi., , J. Mater. Sci, 28, pp.6669~ (1993)
- L. L. Wang., , J. Mater. Sci, 28, pp.3693~ (1993)
- J. D. Ayers., "Laser Application in Material Processing", pp.57~ (1979), Society of Photo-Optical Instrumentation Engineers
- J. Lee., , Mater. Sci. Eng. A, 323, pp.251~ (2002)
- A. Y. Fasasi., , J. Mater. Sci, 29, pp.5121~ (1994)
- R. Licheri., , Ceramics International, 29, pp.519~ (2003)
- Y. B. Liu., "Metal Matrix Composites", pp.770~ (1993), Woodhead Publishing
- Roberto Orr., , Materials Science and Engineering: R: Reports, 63(4-6), pp.127~287 (2009)
- G. D. Quinn., , J. Am. Ceram. Soc, 90, pp.673~ (2007)
- F. Sergejev., "Comparative study on indentation fracture toughness measurements of cemented carbides", Proc. Estonian Acad. Sci. Eng, 12, pp.388~ (2006)
- C. Suryanarayana., "Mechanical Alloying and Milling", pp.83~ (2003), Marcel Dekker publishing
- R. M. German., "Powder Metallurgy of Iron and Steel", pp.385~396 (1998), John Wiley & Sons, Inc.
- R. M. Hathaway., , Proc. Int. Conf. HIGH TEMPERATURE CAPILLARITY(Edited by N. Eustathopoulos and N. Sobczak), Cracow, Poland, 26, pp.7~ (1997)