Microstructure and Hardness of TiC Particle-reinforced Fe Self-fluxing Alloy Powders Based Hybrid Composite Prepared by High Energy Ball Milling
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The Fe-based self-fluxing alloy powders and TiC particles were ball-milled and subsequently compacted and sintered at various temperatures, resulting in the TiC particle-reinforced Fe self-fluxing alloy hybrid composite, and the microstructure and micro-hardness were investigated. The initial Fe-based self-fluxing alloy powders and TiC particles showed the spherical shape with a mean size of approximately 80 μm and the irregular shape of less than 5 μm,respectively. After ball-milling at 800 rpm for 5 h, the powder mixture of Fe-based self-fluxing alloy powders and TiC particles formed into the agglomerated powders with the size of approximately 10 μm that was composed of the nanosized TiC particles and nano-sized alloy particles. The TiC particle-reinforced Fe-based self-fluxing alloy hybrid composite sintered at 1173 K revealed a much denser microstructure and higher micro-hardness than that sintered at 1073 K and 1273 K.
Abstract
The Fe-based self-fluxing alloy powders and TiC particles were ball-milled and subsequently compacted and sintered at various temperatures, resulting in the TiC particle-reinforced Fe self-fluxing alloy hybrid composite, and the microstructure and micro-hardness were investigated. The initial Fe-based self-fluxing alloy powders and TiC particles showed the spherical shape with a mean size of approximately 80 μm and the irregular shape of less than 5 μm,respectively. After ball-milling at 800 rpm for 5 h, the powder mixture of Fe-based self-fluxing alloy powders and TiC particles formed into the agglomerated powders with the size of approximately 10 μm that was composed of the nanosized TiC particles and nano-sized alloy particles. The TiC particle-reinforced Fe-based self-fluxing alloy hybrid composite sintered at 1173 K revealed a much denser microstructure and higher micro-hardness than that sintered at 1073 K and 1273 K.
참고문헌 (7)
- Shane A. Catledge, , J. Nanosci. Nanotech, 4, pp.986~ (2004)
- R. L. Trumper, , Met. Mater, 3, pp.662~ (1987)
- J. S. Benjamin, , Metall. Trans, 1, pp.2943~ (1970)
- S. R. Mishra, , J. Nanosci.Nanotech, 3, pp.227~ (2003)
- Y. Sahin, , Materials and Design, 24, pp.671~ (2003)
- J. F. Shackelford, "CRC Materials Science and Engineering Handbook (3rd)", pp.471~ (2000), CRC press
- S. Y. Chang, , J. Nanosci. Nanotech, 12 (2012)