Warm Spray 공정과 Cu-Ga 및 Cu-In 혼합 분말을 이용한 CGI계 복합 코팅층의 제조 및 특성
Manufacturing and Properties of CGI-based Composite Coating Layer Utilizing a Warm Spray Process and Cu-Ga and Cu-In Mixed Powders
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
This study manufactured a CIG-based composite coating layer utilizing a new warm spray process, and amixed powder of Cu-20at.%Ga and Cu-20at.%In. In order to obtain the mixed powder with desired composition, theCu-20at.%Ga and Cu-20at.%In powders were mixed with a 7:1 ratio. The mixed powder had an average particle size of35.4 μm. Through the utilization of a warm spray process, a CIG-based composite coating layer of 180 μm thicknesscould be manufactured on a pure Al matrix. To analyze the microstructure and phase, the warm sprayed coating layerunderwent XRD, SEM/EDS and EMPA analyses. In addition, to improve the physical properties of the coating layer, anannealing heat treatment was conducted at temperatures of 200oC, 400oC and 600oC for 1 hour each. The microstructureanalysis identified α-Cu, Cu4In and Cu3Ga phases in the early mixed powder, while Cu4In disappeared, and additionalCu9In4 and Cu9Ga4 phases were identified in the warm sprayed coating layer. Porosity after annealing heat treatmentreduced from 0.75% (warm sprayed coating layer) to 0.6% (after 600oC/1 hr. heat treatment), and hardness reducedfrom 288 Hv to 190 Hv. No significant phase changes were found after annealing heat treatment.
Abstract
This study manufactured a CIG-based composite coating layer utilizing a new warm spray process, and amixed powder of Cu-20at.%Ga and Cu-20at.%In. In order to obtain the mixed powder with desired composition, theCu-20at.%Ga and Cu-20at.%In powders were mixed with a 7:1 ratio. The mixed powder had an average particle size of35.4 μm. Through the utilization of a warm spray process, a CIG-based composite coating layer of 180 μm thicknesscould be manufactured on a pure Al matrix. To analyze the microstructure and phase, the warm sprayed coating layerunderwent XRD, SEM/EDS and EMPA analyses. In addition, to improve the physical properties of the coating layer, anannealing heat treatment was conducted at temperatures of 200oC, 400oC and 600oC for 1 hour each. The microstructureanalysis identified α-Cu, Cu4In and Cu3Ga phases in the early mixed powder, while Cu4In disappeared, and additionalCu9In4 and Cu9Ga4 phases were identified in the warm sprayed coating layer. Porosity after annealing heat treatmentreduced from 0.75% (warm sprayed coating layer) to 0.6% (after 600oC/1 hr. heat treatment), and hardness reducedfrom 288 Hv to 190 Hv. No significant phase changes were found after annealing heat treatment.
참고문헌 (23)
- 최병철, "스퍼터링 타겟용 저온 분사 Cu-15 at.%Ga 코팅 소재의 특성에 미치는 열처리 분위기의 영향", 한국분말야금학회지, 18(6), pp.552~561 (2011), 한국분말야금학회
- M. Kaelin, , Thin Solid Films, 431, pp.58~ (2003)
- M. Nouiri, , Mater. Sci. Eng. C, 27, pp.1002~ (2007)
- K. Sakurai, , Thin Solid Films, 431, pp.6~ (2003)
- T. Nakano, , Thin Solid Films, 334, pp.192~ (1998)
- J. W. Lim, , Surf. Coat. Tech., 201, pp.1899~ (2006)
- J. Sarkar, , Thin Solid Films, 517, pp.1970~ (2009)
- 조경식, "CP-Ti 분말로부터 스파크 플라즈마 소결한 타이타늄의 미세구조와 기계적 성질에 미치는 소결 온도의 영향", 한국분말야금학회지, 17(5), pp.365~372 (2010), 한국분말야금학회
- G. Bertrand, , Solid State Electron, 48, pp.505~ (2004)
- M. Moritama, , Mater. Trans., 46, pp.1036~ (2005)
- K. J. Kardokus, "Copper Sputtering Target Assembly and Method of Making Same", Patent 6,645,427, ~ (2003)
- C. F. Lo, , J. Electro. Mater., 34, pp.1468~ (2005)
- 진영민, "Manufacturing and Macroscopic Properties of Cold Sprayed Cu-Ga Coating Material for Sputtering Target", 한국분말야금학회지, 20(4), pp.245~252 (2013), 한국분말야금학회
- Y. M. Jin, , J. Therm. Spray Technol., 20, pp.497~ (2011)
- J. Kawakita, , Surf. Coat. Tech., 202, pp.4369~ (2008)
- P. Chivavibul, , J. Therm. Spray Technol., 17, pp.750~ (2008)
- K. H. Kim, , J. Therm. Spray Technol., 21, pp.550~ (2012)
- J. Kawakita, , Mater. Trans., 49, pp.317~ (2008)
- J. Onizawa, , J. Solid Mech. Mater. Eng., 2, pp.156~ (2008)
- P. Chivavibul, , J. Therm. Spray Technol., 19, pp.81~ (2010)
- P. R. Subramanian, , Acta Materila, 36, pp.937~ (1988)
- Z. Bahari, , Termocimica Acta, 401, pp.131~ (2003)
- 황재남, "저온 분사 티타늄 코팅층의 특성 및 적층 거동에 미치는 분말 형상과 분말 예열의 영향", 한국분말야금학회지, 19(5), pp.348~355 (2012), 한국분말야금학회