고속 화염 용사 공정으로 제조된 BCuP-5 필러 금속 코팅층/Ag 기판 클래드 소재의 후열처리에 따른 미세조직 및 기계적 특성 변화
Effect of Post Heat Treatment on the Microstructure and Mechanical Properties of BCuP-5 Filler Metal Coating Layers Fabricated by High Velocity Oxygen Fuel Thermal Spray Process on Ag Substrate
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
A Cu-15Ag-5P filler metal (BCuP-5) is fabricated on a Ag substrate using a high-velocity oxygen fuel (HVOF) thermal spray process, followed by post-heat treatment (300oC for 1 h and 400oC for 1 h) of the HVOF coating layers to control its microstructure and mechanical properties. Additionally, the microstructure and mechanical properties are evaluated according to the post-heat treatment conditions. The porosity of the heat-treated coating layers are significantly reduced to less than half those of the as-sprayed coating layer, and the pore shape changes to a spherical shape. The constituent phases of the coating layers are Cu, Ag, and Cu-Ag-Cu3P eutectic, which is identical to the initial powder feedstock. A more uniform microstructure is obtained as the heat-treatment temperature increases. The hardness of the coating layer is 154.6 Hv (as-sprayed), 161.2 Hv (300oC for 1 h), and 167.0 Hv (400oC for 1 h), which increases with increasing heat-treatment temperature, and is 2.35 times higher than that of the conventional cast alloy. As a result of the pull-out test, loss or separation of the coating layer rarely occurs in the heat-treated coating layer.
Abstract
A Cu-15Ag-5P filler metal (BCuP-5) is fabricated on a Ag substrate using a high-velocity oxygen fuel (HVOF) thermal spray process, followed by post-heat treatment (300oC for 1 h and 400oC for 1 h) of the HVOF coating layers to control its microstructure and mechanical properties. Additionally, the microstructure and mechanical properties are evaluated according to the post-heat treatment conditions. The porosity of the heat-treated coating layers are significantly reduced to less than half those of the as-sprayed coating layer, and the pore shape changes to a spherical shape. The constituent phases of the coating layers are Cu, Ag, and Cu-Ag-Cu3P eutectic, which is identical to the initial powder feedstock. A more uniform microstructure is obtained as the heat-treatment temperature increases. The hardness of the coating layer is 154.6 Hv (as-sprayed), 161.2 Hv (300oC for 1 h), and 167.0 Hv (400oC for 1 h), which increases with increasing heat-treatment temperature, and is 2.35 times higher than that of the conventional cast alloy. As a result of the pull-out test, loss or separation of the coating layer rarely occurs in the heat-treated coating layer.
참고문헌 (25)
- 강현구, "Ag 코팅한 W-Ag 전기접점", Cu 모재간의 브레이징 접합 특성, 2006, pp.13(1), 18~24[DOI]
- F. Findik, , Mater. Des, 24, pp.489~ (2003)
- J. H. Zhu, , Int. J. Hydrog. Energy, 42, pp.24278~ (2017)
- Y. Zhang, , Nano Mater. Sci, 1, pp.208~ (2019)
- H. J. Kim, "Korea, KR No. 1019970035472", ~ (1997)
- H. Yu, , J. Mater. Sci, 50, pp.324~ (2015)
- Y. Li, , Trans. Nonferrous Met. Soc. China, 21, pp.394~ (2011)
- G. Straffelini, , Coat, 10, pp.886~ (2020)
- J. Yu, , Coat, 12, pp.828~ (2022)
- 주연아, "고속 화염 용사 공정을 이용한 스위칭 소자용 BCuP-5 filler 금속", Ag 기판 클래드 소재의 제조, 미세조직 및 접합 특성, 2022, pp.29(3), 226~232[DOI]
- Y. Lu, , Mater. Sci. Technol, 34, pp.862~ (2018)
- D. W. Sul, , Mater. Sci. Technol, 56, pp.113~ (2018)
- ASM Intl, "Metals Handbook Vol. 8: Metallography, Structures and Phase Diagrams", ASM Intl, pp.435~ (1973)
- D. Janovszky, , J. Alloys Compd, 586, pp.194~ (2014)
- H. G. Scott, , J. Mater. Sci, 10, pp.1527~ (1975)
- P. Bansal, , J. Therm. Spray Technol, 15, pp.570~ (2006)
- S. Itoh, , MSF, 465-466, pp.427~ (2004)
- G. Ynag, , Opt. Soc. Am. B, 30, pp.282~ (2013)
- C. J. Kong, , Mater. Sci. Eng. A, 403, pp.205~ (2005)
- D. Zhang, , Mater. Sci. Eng. A, 344, pp.45~ (2003)
- I. Yamauchi, , J. Mater. Sci, 33, pp.371~ (1998)
- G. Radnóczi, , Acta Mater, 123, pp.82~ (2017)
- S. J. Harris, , Mater. Sci. Forum, 331-337, pp.519~ (2000)
- P. Coddet, , Mater. Sci. Eng. A, 637, pp.40~ (2015)
- M. B. Karamis, , J. Mater. Process. Tech, 141, pp.302~ (2003)