Kinetic Spray 공정을 이용한 벌크형 탄탈륨 소재의 제조및 미세조직/물성
Fabrication and Microstructure/Properties of Bulk-type Tantalum Material by a Kinetic Spray Process
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
A bulk-type Ta material is fabricated using the kinetic spray process and its microstructure and physical properties are investigated. Ta powder with an angular size in the range 9-37 μm (purity 99.95%) is sprayed on a Cu plate to form a coating layer. As a result, ~7 mm-sized bulk-type high-density material capable of being used as a sputter material is fabricated. In order to assess the physical properties of the thick coating layer at different locations, the coating material is observed at three different locations (surface, center, and interface). Furthermore, a vacuum heat treatment is applied to the coating material to reduce the variation of physical properties at different locations of the coating material and improve the density. OM, Vickers hardness test, SEM, XRD, and EBSD are implemented for analyzing the microstructure and physical properties. The fabricated Ta coating material produces porosity of 0.11~0.12%, hardness of 311~327 Hv, and minor variations at different locations. In addition, a decrease in the porosity and hardness is observed at different locations upon heat treatment.
Abstract
A bulk-type Ta material is fabricated using the kinetic spray process and its microstructure and physical properties are investigated. Ta powder with an angular size in the range 9-37 μm (purity 99.95%) is sprayed on a Cu plate to form a coating layer. As a result, ~7 mm-sized bulk-type high-density material capable of being used as a sputter material is fabricated. In order to assess the physical properties of the thick coating layer at different locations, the coating material is observed at three different locations (surface, center, and interface). Furthermore, a vacuum heat treatment is applied to the coating material to reduce the variation of physical properties at different locations of the coating material and improve the density. OM, Vickers hardness test, SEM, XRD, and EBSD are implemented for analyzing the microstructure and physical properties. The fabricated Ta coating material produces porosity of 0.11~0.12%, hardness of 311~327 Hv, and minor variations at different locations. In addition, a decrease in the porosity and hardness is observed at different locations upon heat treatment.
참고문헌 (27)
- C. Deng, , J. Mater. Process. Technol., 214, pp.462~ (2014)
- M. Bischof, , Int. J. Refract. Met. Hard Mater., 24, pp.437~ (2006)
- S. H. Jang, , J. Korean Powder Metall. Inst., 18, pp.181~ (2008)
- V. B. Voitovich, , Oxid. Met., 43, pp.509~ (1995)
- T. Kjemi, , Bergvesen og Mettallurgi, 6, pp.23~ (1963)
- D. C. Carter, , Society of Vacuum Coaters 51st Annual Technical Conference Proceedings, pp.380~385 (2008), Society of Vacuum Coaters
- J. W. Lim, , Surf. Coat. Technol., 201, pp.1899~ (2006)
- J. Sarkar, , Thin Solid Films, 517, pp.1970~ (2009)
- M. Moriyama, , Mater. Trans., 46, pp.1036~ (2005)
- J. K. Kardokus, "United States of America, US6645427 B1", ~ (2003)
- C. F. LO, , J. Eelectro. Mater., 34, pp.1468~ (2005)
- A. Parapin, "Cold spray technology", pp.49~ (2001), Elsevier
- T. H. V. Steenkiste, , Key Eng. Mater, 197, pp.59~ (2001)
- H. J. Kim, , J. Weld. Join., 20, pp.459~ (2006)
- J. Voyer, , 2003 International Thermal Spray Conference, pp.71~ (2003), ASM International
- R. C. McCone, , 2003 International Thermal Spray Conference, pp.63~ (2003), ASM International
- T. Van Steenkiste, , J. Therm. Spray Technol., 13, pp.265~ (2004)
- H. Koivuluoto, , J. Therm. Spray Technol., 18, pp.75~ (2009)
- H. Koivuluoto, , Surf. Coat. Technol., 204, pp.2353~ (2010)
- 최병철, "스퍼터링 타겟용 저온 분사 Cu-15 at.%Ga 코팅 소재의 특성에 미치는 열처리 분위기의 영향", 한국분말야금학회지, 18(6), pp.552~561 (2011), 한국분말야금학회
- 유지상, "저온 분사 공정으로 제조된 티타늄 코팅층의 치밀화에 미치는 열처리 분위기의 영향", 한국분말야금학회지, 19(2), pp.110~116 (2012), 한국분말야금학회[DOI]
- Jin-Hyeon Cho, "Manufacture and Properties of Cold Spray Deposited Large Thickness Cu Coating Material for Sputtering Target", Metals and Materials International, 17(1), pp.157~166 (2011), 대한금속·재료학회
- T. Stoltenhoff, , Surf. Coat. Technol., 200, pp.4947~ (2006)
- C. J. Li, , Trans. Nonferrous Met. Soc. China, 14, pp.49~ (2004)
- Y. Zou, , Scripta Materialia, 62, pp.395~ (2010)
- 전민광, "Kinetic spray 공정을 이용한 Cu repair 코팅 소재 제조및 열처리에 따른 미세조직과 물성 변화", 한국분말야금학회지, 21(5), pp.349~354 (2014), 한국분말야금학회
- 전민광, "Warm Spray 공정과 Cu-Ga 및 Cu-In 혼합 분말을 이용한 CGI계 복합 코팅층의 제조 및 특성", 한국분말야금학회지, 21(3), pp.229~234 (2014), 한국분말야금학회