In order to improve the high-temperature oxidation stability, sintered 434L stainless steel is studied, focusing on the effect of the addition of metallic oxides to form stable oxide films on the inner particle surface. The green compacts of Fecralloy powder or amorphous silica are added on STS434L and oxidized at 950oC up to 210 h. The weight change ratio of 434L with amorphous silica is higher than that of 434L mixed with Fecralloy, and the weight increase follows a parabolic law, which implies that the oxide film grows according to oxide diffusion through the densely formed oxide film. In the case of 434L mixed with Fecralloy, the elements in the matrix diffuse through the grain boundaries and form Al2O3 and Fe-Cr oxides. Stable high temperature corrosion resistance and electrical resistivity are obtained for STS434L mixed with Fecralloy.
Abstract
In order to improve the high-temperature oxidation stability, sintered 434L stainless steel is studied, focusing on the effect of the addition of metallic oxides to form stable oxide films on the inner particle surface. The green compacts of Fecralloy powder or amorphous silica are added on STS434L and oxidized at 950oC up to 210 h. The weight change ratio of 434L with amorphous silica is higher than that of 434L mixed with Fecralloy, and the weight increase follows a parabolic law, which implies that the oxide film grows according to oxide diffusion through the densely formed oxide film. In the case of 434L mixed with Fecralloy, the elements in the matrix diffuse through the grain boundaries and form Al2O3 and Fe-Cr oxides. Stable high temperature corrosion resistance and electrical resistivity are obtained for STS434L mixed with Fecralloy.
참고문헌 (16)
- W. Howard, , J. Electrochem. Soc., 119, pp.641~ (1972)
- F. H. Stott, , Oxid. Met., 31, pp.369~ (1989)
- A. V. C. Sobral, , Mater. Corros., 51, pp.791~ (2000)
- 이인섭, "AISI 316L강의 저온 플라즈마침질탄화처리 시 가스조성과 처리시간이 표면특성에 미치는 영향", 대한금속·재료학회지, 47(11), pp.716~721 (2009), 대한금속·재료학회
- R. K. Wild, , Corros. Sci., 17, pp.87~ (1977)
- J. T. Bittel, , Corros. Sci., 25, pp.7~ (1969)
- S. C. Kuiry, , ISIJ Int., 34, pp.599~ (1994)
- R. L. Klueh, , J. Nucl. Mater., 773, pp.307~ (2002)
- I. -S. Kim, , Met. Mater. Int., 6, pp.513~ (2000)
- J. H. Ryu, , J. Corros. Sci. Soc. of Kor., 21, pp.69~ (1992)
- 김혜성, "STS 316L 소결체의 대기중 고온산화 거동", 한국분말야금학회지, 20(6), pp.432~438 (2013), 한국분말야금학회
- A. Tiziani, , Corros. Sci., 45, pp.672~ (1990)
- A. Sharon, , Mater. Sci. Eng. A., 224, pp.177~ (1997)
- S. Y. Chen, , Corros. Sci., 48, pp.634~ (2006)
- A. Bautista, , Corros. Sci., 45, pp.1343~ (2002)
- F. A. Golightly, , Oxid. Met., 10, pp.163~ (1976)