STS 316L 소결체의 대기중 고온산화 거동
The Oxidation Behavior of Sintered STS 316L at High-Temperature in the Air
1
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
In this study, analysis on the oxidation behavior was conducted by a series of high-temperature oxidation tests at both 800oC, 900oC and 1000 in the air with sintered STS 316L. The weight gain of each oxidized specimen was measured, the oxidized surface morphologies and composition of oxidation layer were analyzed with Scanning Electron Microscope-Energy Dispersive x-ray Spectroscopy (SEM-EDS), finally, the phase change and composition of the oxidized specimen were shown by X-Ray Diffraction (XRD). As a result, the weight gain increased sharply at 1000oC when oxidation test was conducted for 210 hours. Also, a plentiful of pores were observed in the surface oxidation layers at 900oC for 210 hours. In addition, the following conclusions on oxidation behavior of sintered STS 316L can be obtained: Cr2O3 can be formed on pores by influxing oxygen through open-pores, (Fe0.6Cr0.4)2O3 can be generated on the inner oxidation layer, and Fe2O3 was on the outer oxidation layer. Also, NiFe2O4 could be precipitated if the oxidation time was kept longer.
Abstract
In this study, analysis on the oxidation behavior was conducted by a series of high-temperature oxidation tests at both 800oC, 900oC and 1000 in the air with sintered STS 316L. The weight gain of each oxidized specimen was measured, the oxidized surface morphologies and composition of oxidation layer were analyzed with Scanning Electron Microscope-Energy Dispersive x-ray Spectroscopy (SEM-EDS), finally, the phase change and composition of the oxidized specimen were shown by X-Ray Diffraction (XRD). As a result, the weight gain increased sharply at 1000oC when oxidation test was conducted for 210 hours. Also, a plentiful of pores were observed in the surface oxidation layers at 900oC for 210 hours. In addition, the following conclusions on oxidation behavior of sintered STS 316L can be obtained: Cr2O3 can be formed on pores by influxing oxygen through open-pores, (Fe0.6Cr0.4)2O3 can be generated on the inner oxidation layer, and Fe2O3 was on the outer oxidation layer. Also, NiFe2O4 could be precipitated if the oxidation time was kept longer.
참고문헌 (14)
- 이동복, "Fe-16Cr-6Ni-6Mn-1.7Mo 스테인리스 합금의 700~900℃에서의 대기중 산화", 대한금속·재료학회지, 49(2), pp.153~160 (2011), 대한금속·재료학회
- 장희진, "반응표면분석법을 활용한 Fe-18Cr 스테인리스강의 부식 및 산화 저항성에 미치는 Ti, Si, Mo의 영향 분석", 대한금속·재료학회지, 48(8), pp.741~748 (2010), 대한금속·재료학회
- 이인섭, "AISI 316L강의 저온 플라즈마침질탄화처리 시 가스조성과 처리시간이 표면특성에 미치는 영향", 대한금속·재료학회지, 47(11), pp.716~721 (2009), 대한금속·재료학회
- I. Y. Son., "A Study on the formation of oxide scale on the stainless steels at high temperature", Jr. of the Korea Institute of Surface Eng, 27, pp.123~ (1994)
- S. Y. Chen., "Effect of water vapor on annealing scale formation on 316 SS", Corros. Sci, 48, pp.634~ (2006)
- A. V. C. Sobral., "Oxidation of injection molding 316L stainless steel at high temperature", Mater. Corros, 51, pp.791~ (2000)
- Thuan Dinh Nguyen, "STS 304 스테인리스강의 대기중 1050~1200˚C, 1시간 동안의 산화", 대한금속·재료학회지, 47(4), pp.235~241 (2009), 대한금속·재료학회
- R. L. Sands., "The Corrosion Resistance of Sintered Austenitic Stainless Steel", Mordern Develop. in Powder Met, 2, pp.73~ (1966)
- N. Tosangthum., "Density and Strength Improvement of Sintered 316L Stainlee Steel", Ching Mai. J. Sci, 33(1), pp.53~66 (2006)
- C. J. Wang., "The effect of carbon on the high temperature oxidation of Fe-31 Mn-9Al-0. 87 C alloy", J. Mater. Sci, 23, pp.3447~ (1988)
- Y. Y. Lee., "High temperature oxidation of 316L Stainless steel in Dry Oxygen Environments", Kor. J. Met. Mater, 3, pp.2~ (1994)
- G. C. Wood., "The oxidation of iron-chromium alloys and stainless steels at high temperatures", Corrosion Sci, 2, pp.173~ (1962)
- H. J. Yearian., "Structure of Oxide Scales on Nickel-Chromium Steels", Corrosion, 12, pp.45~ (1956)
- A. Bautista., "Oxidation Behavior at 900°C of Austenitic, Ferritic, and Duplex Stainless Steels Manufactured By Powder Metallurgy", Oxidation of Metals, 5, pp.9~ (2003)