방전플라즈마소결법 적용 승온속도 변화에 따라 제조된 Fe-20Cu-1C 소결체 제조 및 특성평가
Fabrication and Mechanical Property of Fe-20Cu-1C Compacts by SPS process with Different Heating Rate
0
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
In this study, Fe-Cu-C alloy is sintered by spark plasma sintering (SPS). The sintering conditions are 60 MPa pressure with heating rates of 30, 60 and 9oC/min to determine the influence of heating rate on the mechanical and microstructure properties of the sintered alloys. The microstructure and mechanical properties of the sintered Fe-Cu-C alloy is investigated by X-ray diffraction (XRD) and field-emission scanning electron microscopy (FE-SEM). The temperature of shrinkage displacement is changed at 450oC with heating rates 30, 60, and 90oC/min. The temperature of the shrinkage displacement is finished at 650oC when heating rate 30oC/min, at 700oC when heating rate 60oC/min and at 800oC when heating rate 90oC/min. For the sintered alloy at heating rates of 30, 60, and 90oC/min, the apparent porosity is calculated to be 3.7%, 5.2%, and 7.7%, respectively. The hardness of the sintered alloys is investigated using Rockwell hardness measurements. The objective of this study is to investigate the densification behavior, porosity, and mechanical properties of the sintered Fe-Cu-C alloys depending on the heating rate.
Abstract
In this study, Fe-Cu-C alloy is sintered by spark plasma sintering (SPS). The sintering conditions are 60 MPa pressure with heating rates of 30, 60 and 9oC/min to determine the influence of heating rate on the mechanical and microstructure properties of the sintered alloys. The microstructure and mechanical properties of the sintered Fe-Cu-C alloy is investigated by X-ray diffraction (XRD) and field-emission scanning electron microscopy (FE-SEM). The temperature of shrinkage displacement is changed at 450oC with heating rates 30, 60, and 90oC/min. The temperature of the shrinkage displacement is finished at 650oC when heating rate 30oC/min, at 700oC when heating rate 60oC/min and at 800oC when heating rate 90oC/min. For the sintered alloy at heating rates of 30, 60, and 90oC/min, the apparent porosity is calculated to be 3.7%, 5.2%, and 7.7%, respectively. The hardness of the sintered alloys is investigated using Rockwell hardness measurements. The objective of this study is to investigate the densification behavior, porosity, and mechanical properties of the sintered Fe-Cu-C alloys depending on the heating rate.
참고문헌 (19)
- R. Verghese, , Key Eng. Mater., 29-31, pp.457~ (1989)
- A. G. Kostornov, , Powder Metall. Met. Ceram., 46, pp.503~ (2007)
- T. Kameoka, , J. Jpn. Soc. Powder Powder Metall., 19, pp.281~ (1972)
- R. Annamalai, , Bull. Mater. Sci., 36, pp.447~ (2013)
- S. M. Sharma, , Tribol. ind., 38, pp.138~ (2016)
- 장준호, "펄스전류활성소결법을 이용한 스퍼터링 타겟용 Cu-Mn 소결체 제조 및 특성평가", 한국분말야금학회지, 23(1), pp.1~7 (2016), 한국분말야금학회
- A. A. Sorour, "Microstructure and tribology of Fe-Cu-B-Based alloy", Ph. D., pp.2014
- H. J. Kim, , Met. Mater. Int., 5, pp.63~ (1999)
- J. Do, , Metall. Mater. Trans. A, 43, pp.2237~ (2012)
- H. W. Jin, , Met. Mater. Int., 3, pp.60~ (1997)
- Hong-Hai Nguyen, "Spark Plasma Sintering of Fe-Ni-Cu-Mo-C Low Alloy Steel Powder", 한국분말야금학회지, 23(3), pp.207~212 (2016), 한국분말야금학회
- D. Smilgies, , Appl. Crystallogr., 42, pp.1030~ (2009)
- Hyun-Kuk Park, "Fabrication and mechanical properties of WC-10 wt.%Co hard materials for a friction stir welding tool application by a spark plasma sintering process", Journal of Ceramic Processing Research, 13(6), pp.705~712 (2012), 세라믹공정연구센터
- H. K. Park, , Mater. Trans., 53, pp.1056~ (2012)
- 박현국, "급속소결 방법을 이용한 마찰교반 접합 툴용 WC-Co 소결체 제조 및 특성 평가", 대한용접접합학회지, 30(6), pp.578~583 (2012), 대한용접접합학회
- K. Chokethawai, , J. Alloys Compd., 480, pp.351~ (2009)
- R. Watanabe, , Trans. Jpn. Inst. Met., 14, pp.320~ (1973)
- U. Cavdar, , Mater. tehnol., 48, pp.977~ (2014)
- C. Teisanu, "Liquid Phase Sintering of Fe-Cu-Sn-Pb System for Tribological Applications" (2012), InTech press