리튬이온전지용 양극활물질 LiNi0.83 Co0.11Mn0.06O2의 전기화학적 특성에 미치는 Ce와 Nd 희토류 금속의 단독 혹은 이중 도핑효과
Effect of Single and Dual Doping of Rare Earth Metal Ce and Nd Elements on Electrochemical Properties of LiNi0.83 Co0.11Mn0.06O2 Cathode Lithium-ion Battery Material
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Layered LiNi0.83Co0.11Mn0.06O2 cathode materials single- and dual-doped by the rare-earth elements Ce and Nd are successfully fabricated by using a coprecipitation-assisted solid-phase method. For comparison purposes, nondoping pristine LiNi0.83Co0.11Mn0.06O2 cathode material is also prepared using the same method. The crystal structure, morphology, and electrochemical performances are characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) mapping, and electrochemical techniques. The XRD data demonstrates that all prepared samples maintain a typical α-NaFeO2-layered structure with the R-3m space group, and that the doped samples with Ce and/or Nd have lower cation mixing than that of pristine samples without doping. The results of SEM and EDS show that doped elements are uniformly distributed in all samples. The electrochemical performances of all doped samples are better than those of pristine samples without doping. In addition, the Ce/Nd dualdoped cathode material shows the best cycling performance and the least capacity loss. At a 10 C-rate, the electrodes of Ce/Nd dual-doped cathode material exhibit good capacity retention of 72.7, 58.5, and 45.2% after 100, 200, and 300 cycles, respectively, compared to those of pristine samples without doping (24.4, 11.1, and 8.0%).
Abstract
Layered LiNi0.83Co0.11Mn0.06O2 cathode materials single- and dual-doped by the rare-earth elements Ce and Nd are successfully fabricated by using a coprecipitation-assisted solid-phase method. For comparison purposes, nondoping pristine LiNi0.83Co0.11Mn0.06O2 cathode material is also prepared using the same method. The crystal structure, morphology, and electrochemical performances are characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) mapping, and electrochemical techniques. The XRD data demonstrates that all prepared samples maintain a typical α-NaFeO2-layered structure with the R-3m space group, and that the doped samples with Ce and/or Nd have lower cation mixing than that of pristine samples without doping. The results of SEM and EDS show that doped elements are uniformly distributed in all samples. The electrochemical performances of all doped samples are better than those of pristine samples without doping. In addition, the Ce/Nd dualdoped cathode material shows the best cycling performance and the least capacity loss. At a 10 C-rate, the electrodes of Ce/Nd dual-doped cathode material exhibit good capacity retention of 72.7, 58.5, and 45.2% after 100, 200, and 300 cycles, respectively, compared to those of pristine samples without doping (24.4, 11.1, and 8.0%).
참고문헌 (39)
- K. Mizushima, , Mater. Res. Bull, 15, pp.783~ (1980)
- B. Xu, , Mater. Sci. Eng., R, 73, pp.51~ (2012)
- W. Ahn, , J. Alloys Compd, 609, pp.143~ (2014)
- J. Xiao, , Chem. Mater, 22, pp.1180~ (2010)
- S. -T. Myung, , ACS Energy Lett, 2, pp.196~ (2017)
- W. Liu, , Angew. Chem. Int. Ed, 54, pp.4440~ (2015)
- M. Zhang, , Electrochim. Acta, 232, pp.80~ (2017)
- C.-C. Yang, , Electrochim. Acta, 134, pp.258~ (2014)
- Z. Huang, , J. Power Sources, 202, pp.284~ (2012)
- P. Hou, , J. Power Sources, 265, pp.174~ (2014)
- K. C. Kam, , J. Mater. Chem, 21, pp.9991~ (2011)
- H. -J. Noh, , J. Power Sources, 233, pp.121~ (2013)
- K. -K Lee, , J. Electrochem. Soc, 147, pp.1709~ (2000)
- M. Noh, , J. Electrochem. Soc, 160, pp.A105~ (2013)
- S. Sallis, , Appl. Phys. Lett, 108, pp.263902~ (2016)
- P. Oh, , J. Mater. Chem. A, 4, pp.5839~ (2016)
- D. Aurbach, , J. Power Sources, 89, pp.206~ (2000)
- S. Hwang, , Chem. Mater, 27, pp.6044~ (2015)
- O. Dolotko, , J. Power Sources, 255, pp.197~ (2014)
- K. Min, , J. Power Sources, 315, pp.111~ (2016)
- J. Zheng, , J. Am. Chem. Soc, 138, pp.13326~ (2016)
- K. Wu, , Electrochim. Acta, 75, pp.393~ (2012)
- H. Kuriyama, , J. Power Sources, 275, pp.99~ (2015)
- Y. Huang, , Electrochim. Acta, 231, pp.294~ (2017)
- D. -J. Lee, , J. Power Sources, 196, pp.7742~ (2011)
- Y. Dai, , J. Power Sources, 247, pp.365~ (2014)
- H. Xie, , J. Phys. Chem. C, 120, pp.3235~ (2016)
- G. Hu, , Electrochim. Acta, 190, pp.264~ (2016)
- B. Huang, , J. Power Sources, 252, pp.200~ (2014)
- I. M. Markus, , J. Phys. Chem. Lett, 5, pp.3649~ (2014)
- H. Zhu, , Electrochim. Acta, 135, pp.77~ (2014)
- D. Wang, , Electrochim. Acta, 188, pp.48~ (2016)
- Z. Yang, , J. Alloys Compd, 699, pp.358~ (2017)
- X. Li, , Electrochim. Acta, 174, pp.1122~ (2015)
- Nazanin Hamnabard, "Effectiveness of Nd doping and graphene oxide modification on electrochemical performance of CdSe nanorod material", Journal of Industrial and Engineering Chemistry, 49, pp.88~98 (2017), 한국공업화학회[DOI]
- S. Zhong, , J. Rare Earths, 29, pp.891~ (2011)
- 최웅희, "공기와 질소 분위기에서 공침법으로 합성된 Ni1", 3Co1, 3(OH)2 분말의 특성 비교, pp.한국분말재료학회지, 2016[DOI]
- H. -G. Jung, , Electrochim. Acta, 68, pp.153~ (2012)
- M. S. Whittingham, , Chem. Rev, 104, pp.4271~ (2004)