NiO/camphene 슬러리의 동결건조 및 수소환원 공정에 의한 Ni 다공체 제조
Fabrication of Porous Ni by Freeze Drying and Hydrogen Reduction of NiO/Camphene Slurry
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this study, freeze drying of a porous Ni with unidirectionally aligned pore channels is accomplished by using a NiO powder and camphene. Camphene slurries with NiO content of 5 and 10 vol% are prepared by mixing them with a small amount of dispersant at 50oC. Freezing of a slurry is performed at -25oC while the growth direction of the camphene is unidirectionally controlled. Pores are generated subsequently by sublimation of the camphene during drying in air for 48 h. The green bodies are hydrogen-reduced at 400oC and then sintered at 800oC and 900oC for 1 h. X-ray diffraction analysis reveals that the NiO powder is completely converted to the Ni phase without any reaction phases. The sintered samples show large pores that align parallel pores in the camphene growth direction as well as small pores in the internal walls of large pores. The size of large and small pores decreases with increasing powder content from 5 to 10 vol%. The influence of powder content on the pore structure is explained by the degree of powder rearrangement in slurry and the accumulation behavior of powders in the interdendritic spaces of solidified camphene.
Abstract
In this study, freeze drying of a porous Ni with unidirectionally aligned pore channels is accomplished by using a NiO powder and camphene. Camphene slurries with NiO content of 5 and 10 vol% are prepared by mixing them with a small amount of dispersant at 50oC. Freezing of a slurry is performed at -25oC while the growth direction of the camphene is unidirectionally controlled. Pores are generated subsequently by sublimation of the camphene during drying in air for 48 h. The green bodies are hydrogen-reduced at 400oC and then sintered at 800oC and 900oC for 1 h. X-ray diffraction analysis reveals that the NiO powder is completely converted to the Ni phase without any reaction phases. The sintered samples show large pores that align parallel pores in the camphene growth direction as well as small pores in the internal walls of large pores. The size of large and small pores decreases with increasing powder content from 5 to 10 vol%. The influence of powder content on the pore structure is explained by the degree of powder rearrangement in slurry and the accumulation behavior of powders in the interdendritic spaces of solidified camphene.
참고문헌 (15)
- P. S. Liu, , J. Mater. Sci, 36, pp.5059~ (2001)
- J. Banhart, , Prog. Mater. Sci, 46, pp.559~ (2001)
- 김남훈, "In-situ 환원", 소결법을 이용한 다공성 니켈 멤브레인 가스필터의 제조 및 평가, 2009, pp.16(4), 262~267[DOI]
- Z. -Y. Deng, , J. Am. Ceram. Soc, 85, pp.1961~ (2002)
- T. Fukasawa, , J. Am. Ceram. Soc, 84, pp.230~ (2001)
- S. -T. Oh, , Trans. Nonferrous Met. Soc. China, 22, pp.s688~ (2012)
- 김주형, "CuO-SnO2", camphene 슬러리의 동결 및 소결조건이 Cu-Sn 다공체의 기공구조에 미치는 영향, 2016, pp.23(1), 49~53[DOI]
- S. -T. Oh, , Mater. Lett, 139, pp.268~ (2015)
- S. -K. Ryi, , J. Membr. Sci, 299, pp.174~ (2007)
- S. D. Robertson, , J. Catal, 37, pp.424~ (1975)
- M. Wi niewska, , Powder Technol, 198, pp.258~ (2010)
- B. Jankovi, , Chem. Eng. Sci, 63, pp.567~ (2008)
- D. R. Uhlmann, , J. Appl. Phys, 35, pp.2986~ (1964)
- S. Deville, , Nature Mater, 8, pp.966~ (2009)
- K. Araki, , J. Am. Ceram. Soc, 87, pp.2014~ (2004)