산화물 복합분말 첨가 Camphene 슬러리의 동결건조 공정에 의한 Cu-Co 복합계 다공체 제조
Synthesis of Porous Cu-Co using Freeze Drying Process of Camphene Slurry with Oxide Composite Powders
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Porous Cu-14 wt% Co with aligned pores is produced by a freeze drying and sintering process. Unidirectional freezing of camphene slurry with CuO-Co3O4 powders is conducted, and pores in the frozen specimens are generated by sublimation of the camphene crystals. The dried bodies are hydrogen-reduced at 500oC and sintered at 800oC for 1 h. The reduction behavior of the CuO-Co3O4 powder mixture is analyzed using a temperature-programmed reduction method in an Ar-10% H2 atmosphere. The sintered bodies show large and aligned parallel pores in the camphene growth direction. In addition, small pores are distributed around the internal walls of the large pores. The size and fraction of the pores decrease as the amount of solid powder added to the slurry increases. The change in pore characteristics according to the amount of the mixed powder is interpreted to be due to the rearrangement and accumulation behavior of the solid particles in the freezing process of the slurry.
Abstract
Porous Cu-14 wt% Co with aligned pores is produced by a freeze drying and sintering process. Unidirectional freezing of camphene slurry with CuO-Co3O4 powders is conducted, and pores in the frozen specimens are generated by sublimation of the camphene crystals. The dried bodies are hydrogen-reduced at 500oC and sintered at 800oC for 1 h. The reduction behavior of the CuO-Co3O4 powder mixture is analyzed using a temperature-programmed reduction method in an Ar-10% H2 atmosphere. The sintered bodies show large and aligned parallel pores in the camphene growth direction. In addition, small pores are distributed around the internal walls of the large pores. The size and fraction of the pores decrease as the amount of solid powder added to the slurry increases. The change in pore characteristics according to the amount of the mixed powder is interpreted to be due to the rearrangement and accumulation behavior of the solid particles in the freezing process of the slurry.
참고문헌 (17)
- M. -J. Suk, , J. Korean Powder Metall. Inst, 8, pp.215~ (2001)
- P. S. Liu, , J. Mater. Sci, 36, pp.5059~ (2001)
- H. Nakajima, , Prog. Mater. Sci, 52, pp.1091~ (2007)
- T. Ohji, , Intern. Mater. Rev, 57, pp.115~ (2012)
- T. Fukasawa, , J. Am. Ceram. Soc, 84, pp.230~ (2001)
- B. -H. Yoon, , J. Am. Ceram. Soc, 90, pp.1753~ (2007)
- 정재헌, "NiO", camphene 슬러리의 동결건조 및 수소환원 공정에 의한 Ni 다공체 제조, 2019, pp.26(1), 6~10[DOI]
- A. E. Berkowitz, , Phys. Rev. Lett, 68, pp.3745~ (1992)
- 박유세, "Sol-Gel법을 이용한 CuxCo3-xO4 산소 발생 촉매의 합성 및 전기화학 특성 분석", 한국재료학회지, 29(2), pp.92~96 (2019), 한국재료학회[DOI]
- 한주연, "볼 밀링한 CuO-Co3O4 혼합분말의 수소환원 거동과 미세조직 특성", 한국분말재료학회지, 26(5), pp.410~414 (2019), 한국분말재료학회[DOI]
- S. D. Robertson, , J. Cataly, 37, pp.424~ (1975)
- J. A. Rodriguez, , Cataly. Lett, 85, pp.247~ (2003)
- H. -Y. Lin, , Mater. Chem. Phys, 85, pp.171~ (2004)
- D. -G. Kim, , Mater. Sci. Eng. A, 399, pp.326~ (2005)
- T. Nishizawa, , Bull. Alloy Phase Diagrams, 5, pp.161~ (1984)
- K. Araki, , J. Am Ceram. Soc, 88, pp.1108~ (2005)
- S. Deville, , Adv. Eng. Mater, 10, pp.155~ (2008)