Hydroxyapatite를 대체하여 말뼈를 첨가한 Ti-20Mo-0.5EB의 미세조직과 기계적 특성
Microstructures and Mechanical Properties of Ti-20Mo-0.5EB Composites
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, Ti-Mo-EB composites are prepared by ball milling and spark plasma sintering (SPS) to obtain a low elastic modulus and high strength and to evaluate the microstructure and mechanical properties as a function of the process conditions. As the milling time and sintering temperature increased, Mo, as a β-Ti stabilizing element, diffused, and the microstructure of β-Ti increased. In addition, the size of the observed phase was small, so the modulus and hardness of α-Ti and β-Ti were measured using nanoindentation equipment. In both phases, as the milling time and sintering temperature increased, the modulus of elasticity decreased, and the hardness increased. After 12 h of milling, the specimen sintered at 1000oC showed the lowest values of modulus of elasticity of 117.52 and 101.46 GPa for α-Ti and β-Ti, respectively, confirming that the values are lower compared to the that in previously reported studies.
Abstract
In this study, Ti-Mo-EB composites are prepared by ball milling and spark plasma sintering (SPS) to obtain a low elastic modulus and high strength and to evaluate the microstructure and mechanical properties as a function of the process conditions. As the milling time and sintering temperature increased, Mo, as a β-Ti stabilizing element, diffused, and the microstructure of β-Ti increased. In addition, the size of the observed phase was small, so the modulus and hardness of α-Ti and β-Ti were measured using nanoindentation equipment. In both phases, as the milling time and sintering temperature increased, the modulus of elasticity decreased, and the hardness increased. After 12 h of milling, the specimen sintered at 1000oC showed the lowest values of modulus of elasticity of 117.52 and 101.46 GPa for α-Ti and β-Ti, respectively, confirming that the values are lower compared to the that in previously reported studies.
참고문헌 (29)
- M. S. Asl, , J. Mater. Res. Technol, 9, pp.10647~ (2020)
- S. Wu, , Surf. Coat. Technol, 233, pp.13~ (2013)
- J. M. Cordeiro, , J. Alloy. Compd, 770, pp.1038~ (2019)
- S. B. Gabriel, , J. Alloys Compd, 536, pp.S208~ (2012)
- H. C. Choe, , Adv. Mater. Res, 26, pp.825~ (2007)
- W. Österle, , Wear, 264, pp.505~ (2008)
- A. Farrahnoor, , Mater. Today Commun, 27, pp.102209~ (2021)
- D. Raza, , Mater.Today: Proc., 16, pp.665~ (2021)
- X. Wang, , Mater. Des, 49, pp.511~ (2013)
- L. Xia, , Chem. Eng. J, 347, pp.711~ (2018)
- A. Kar, , Surf. Coat. Technol, 201, pp.3723~ (2006)
- C. Vasilescu, , Corros. Sci, 53, pp.992~ (2011)
- O. A. Osuchukwu, , SN Appl. Sci, 3, pp.1~ (2021)
- T. Laonapakul, , J. Eng. Appl. Sci, 42, pp.269~ (2015)
- N. M. Pu'ad, , Heliyon, 5, pp.e01588~ (2019)
- K. Haberko, , J. Eur. Ceram. Soc, 26, pp.537~ (2006)
- W. Jeong, , Metals, 10, pp.581~ (2020)
- J. Singh, , Ceram. Int, 47, pp.782~ (2021)
- Q. Chen, , Ceram. Int, 45, pp.4526~ (2018)
- A. Rakngarm Nimkerdphol, , J. Mech. Behav. Biomed. Mater, 36, pp.98~ (2014)
- J. H. Lee, , J. Biomed. Mater. Res. Part B Appl. Biomater, 105, pp.647~ (2017)
- H. L. Yao, , J. Therm. Spray. Technol, 27, pp.924~ (2018)
- H. Farnoush, , J. Mech. Behav. Biomed. Mater, 46, pp.31~ (2015)
- B. A. Obadele, , J. Alloys Compd, 710, pp.825~ (2017)
- M. E. Maja, , Ceram. Int, 44, pp.4419~ (2018)
- J. L. Xu, , Mater. Sci. Eng. C, 97, pp.156~ (2019)
- C. Han, , Mater. Des, 141, pp.256~ (2018)
- W. Jeong, , Mater. Charact, 179, pp.111361~ (2021)
- M. Shahedi Asl, , Mater. Res. Technol, 9, pp.1064~ (2020)