Fabrication of Equiatomic CoCrFeMnNi High-Entropy Alloy by Metal Injection Molding Process Using Coarse-Sized Powders
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
High-entropy alloys (HEAs) are attracting attention because of their excellent properties and functions; however, they are relatively expensive compared with commercial alloys. Therefore, various efforts have been made to reduce the cost of raw materials. In this study, MIM is attempted using coarse equiatomic CoCrFeMnNi HEA powders. The mixing ratio (powder:binder) for HEA feedstock preparation is explored using torque rheometer. The block-shaped green parts are fabricated through a metal injection molding process using feedstock. The thermal debinding conditions are explored by thermogravimetric analysis, and solvent and thermal debinding are performed. It is densified under various sintering conditions considering the melting point of the HEA. The final product, which contains a small amount of non-FCC phase, is manufactured at a sintering temperature of 1250oC.
Abstract
High-entropy alloys (HEAs) are attracting attention because of their excellent properties and functions; however, they are relatively expensive compared with commercial alloys. Therefore, various efforts have been made to reduce the cost of raw materials. In this study, MIM is attempted using coarse equiatomic CoCrFeMnNi HEA powders. The mixing ratio (powder:binder) for HEA feedstock preparation is explored using torque rheometer. The block-shaped green parts are fabricated through a metal injection molding process using feedstock. The thermal debinding conditions are explored by thermogravimetric analysis, and solvent and thermal debinding are performed. It is densified under various sintering conditions considering the melting point of the HEA. The final product, which contains a small amount of non-FCC phase, is manufactured at a sintering temperature of 1250oC.
참고문헌 (16)
- D. B. Miracle, , Nat. Commun, 10, pp.1805~ (2019)
- R. B. Mane, , Powder Metallurgy, 61, pp.131~ (2018)
- F. Otto, , Acta Mater, 112, pp.40~ (2016)
- H. Luo, , Corros. Sci, 136, pp.403~ (2018)
- B. Gludovatz, , Science, 345, pp.1153~ (2014)
- J. Moon, , Acta Mater, 193, pp.71~ (2020)
- J. H. Kim, , Mater. Sci. Eng. A, 712, pp.108~ (2018)
- S. H. Joo, , J. Alloys Compd, 698, pp.591~ (2017)
- R. Savinov, , Procedia Manuf, 53, pp.435~ (2021)
- J. M. Park, , Mater. Res. Lett, 8, pp.1~ (2020)
- Z. Xu, , Addit. Manuf, 35, pp.101441~ (2020)
- Y. Zhang, , J. Alloys Compd, 868, pp.158711~ (2021)
- A. Araoyinbo, "Overview of powder metallurgy process and its advantages", AIP Conference Proceedings, pp.020153~ (2022), AIP Publishing LLC
- D. F. Heaney, "Handbook of metal injection molding" (2018), Woodhead Publishing
- Injection Molding of Metals and Ceramics, "S. V. Atre", SAE, ~ (1998)
- P. P. Bhattacharjee, , J. Alloys Compd, 587, pp.544~ (2014)