다른 크기의 분말 적층을 통해 얻은 Fe-6%Mn합금의 경사 미세조직과 기계적 특성
Gradient Microstructure and Mechanical Properties of Fe-6%Mn Alloy by Different Sized Powder Stacking
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
A typical trade-off relationship exists between strength and elongation in face-centered cubic metals. Studies have recently been conducted to enhance strength without ductility reduction through surface-treatment-based ultrasonic nanocrystalline surface modification (UNSM), which creates a gradient microstructure in which grains become smaller from the inside to the surface. The transformation-induced plasticity effect in Fe-Mn alloys results in excellent strength and ductility due to their high work-hardening rate. This rate is achieved through strain-induced martensitic transformation when an alloy is plastically deformed. In this study, Fe-6%Mn powders with different sizes were prepared by high-energy ball milling and sintered through spark plasma sintering to produce Fe-6%Mn samples. A gradient microstructure was obtained by stacking the different-sized powders to achieve similar effects as those derived from UNSM. A compressive test was performed to investigate the mechanical properties, including the yielding behavior. The deformed microstructure was observed through electron backscatter diffraction to determine the effects of gradient plastic deformation.
Abstract
A typical trade-off relationship exists between strength and elongation in face-centered cubic metals. Studies have recently been conducted to enhance strength without ductility reduction through surface-treatment-based ultrasonic nanocrystalline surface modification (UNSM), which creates a gradient microstructure in which grains become smaller from the inside to the surface. The transformation-induced plasticity effect in Fe-Mn alloys results in excellent strength and ductility due to their high work-hardening rate. This rate is achieved through strain-induced martensitic transformation when an alloy is plastically deformed. In this study, Fe-6%Mn powders with different sizes were prepared by high-energy ball milling and sintered through spark plasma sintering to produce Fe-6%Mn samples. A gradient microstructure was obtained by stacking the different-sized powders to achieve similar effects as those derived from UNSM. A compressive test was performed to investigate the mechanical properties, including the yielding behavior. The deformed microstructure was observed through electron backscatter diffraction to determine the effects of gradient plastic deformation.
참고문헌 (26)
- W. Shi, , Mater. Sci. Eng. A, 429, pp.247~ (2006)
- S. J. Lee, , Scr. Mater, 64, pp.649~ (2011)
- B. C. De Cooman, , Curr. Opin. Solid State Mater. Sci, 8, pp.285~ (2004)
- S. C. Baik, , ISIJ Int, 41, pp.290~ (2001)
- Y. Kang, , Appl. Mech. Mater, 876, pp.41~ (2017)
- K. Kim, , Mater. Sci. Eng. A, 698, pp.183~ (2017)
- D. Park, , Arch. Metall. Mater, 53, pp.1477~ (2018)
- S. J. L ee, , Mater . Sci. F orum, 475-479, pp.3169~ (2005)
- S. J. Lee, , Int. J. Mater. Res, 104, pp.423~ (2013)
- S. J. Lee, , Metall. Mater. Trans. A, 44A, pp.3423~ (2013)
- 오승진, "나노결정 FeMnNiC합금의 오스테나이트 안정성", 한국분말재료학회지, 26(5), pp.389~394 (2019), 한국분말재료학회[DOI]
- J. Mahieu, , Metall. Mater. Trans. A, 33A, pp.2573~ (2002)
- C. Suryanarayana, , Porg. Mater. Sci, 46, pp.1~ (2001)
- E. Bączek, , J. Mater. Eng. Perform, 27, pp.1475~ (2018)
- F. Deirmina, , Mater. Sci. Eng. A, 743, pp.349~ (2019)
- 박정빈, "방전플라즈마소결로 제조된 나노결정 FeNiCrMoMnSiC 합금의 오스테나이트 안정성과 기계적 특성", 한국분말재료학회지, 28(4), pp.336~341 (2021), 한국분말재료학회
- 김광훈, "소성유기마르텐사이트 변태에 의한 나노결정 FeCrC 소결합금의 기계적 강도 향상", 한국분말재료학회지, 28(3), pp.246~252 (2021), 한국분말재료학회
- B. Song, , Mater. Sci. Eng. A, 689, pp.78~ (2017)
- J. Zhang, , Scr. Mater, 218, pp.114790~ (2022)
- J. W. Bae, , Mater. Sci. Eng. A, 826, pp.141966~ (2021)
- S. J. Oh, , Mater. Sci. Eng. A, 725, pp.382~ (2018)
- B. Averbach, , Trans. AIME, 176, pp.60~ (1948)
- 최승규, "철계 소결합금의 오스테나이트 안정성", 한국분말재료학회지, 27(5), pp.414~419 (2020), 한국분말재료학회
- X. Y. Wang, , J. Mater. Res. Technol, 10, pp.643~ (2020)
- G. Adam, , Solid State Phenom, 203-204, pp.34~ (2013)
- M. Azuma, , Mater. Sci. Technol, 28, pp.9~ (2012)