V-벤딩 금형에서 박판 소재의 실험과 해석을 통한 스프링 백 비교 고찰
A comparative study of experiment and analysis of sheet matal in V-bending
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
When the product is removed from the mold after molding during the sheet metal molding process, elastic recovery causes a springback phenomenon. Much research has been done to minimize this phenomenon. In this study, V-bending experiments were conducted using galvanized steel sheets, stainless steel, and aluminum sheet materials, using a total of nine types of thin sheet materials of 1.0t, 1.5t, and 2.0t, respectively. Molding analysis and experimental data were compared and analyzed. In the case of galvanized steel sheets, it was considered that the springback phenomenon occurs more frequently in molding analysis than in experiments. It was considered that the springback phenomenon occurs greatly in the experiment, not the interpretation of the molding of the stainless steel plate and the aluminum plate. It was considered that the springback occurrence tendency of the molding analysis and the experiment was the same, and the springback occurrence error rate of the molding analysis and the experimental result was about 4.0%.
Abstract
When the product is removed from the mold after molding during the sheet metal molding process, elastic recovery causes a springback phenomenon. Much research has been done to minimize this phenomenon. In this study, V-bending experiments were conducted using galvanized steel sheets, stainless steel, and aluminum sheet materials, using a total of nine types of thin sheet materials of 1.0t, 1.5t, and 2.0t, respectively. Molding analysis and experimental data were compared and analyzed. In the case of galvanized steel sheets, it was considered that the springback phenomenon occurs more frequently in molding analysis than in experiments. It was considered that the springback phenomenon occurs greatly in the experiment, not the interpretation of the molding of the stainless steel plate and the aluminum plate. It was considered that the springback occurrence tendency of the molding analysis and the experiment was the same, and the springback occurrence error rate of the molding analysis and the experimental result was about 4.0%.
참고문헌 (6)
- S G Lee, "A springback analysis of LCD TV bottom chassis", Journal of the Korean Society for Mold Engineering, 6(1), pp.63~66 (2012)
- 문영훈, "박판재의 스프링백 해석(II)-해석모델의 실험적 검증", 소성∙가공, 16(7), pp.516~520 (2007), 한국소성∙가공학회
- 최민국, "U-bending에서의 DP780 강판의 스프링백 거동 연구", 소성∙가공, 21(6), pp.384~388 (2012), 한국소성∙가공학회
- 박정수, "금형변형을 고려한 성형 CAE에서의 스프링백 예측정확도 향상", 소성∙가공, 23(6), pp.380~385 (2014), 한국소성∙가공학회
- 윤재웅, "각통드로잉 제품의 모서리 재료두께 변화에 영향을 미치는 인자에 대한 해석 연구", Design & Manufacturing, 14(1), pp.22~29 (2020), 한국금형공학회[DOI]
- 전용준, "굴삭기 요소수 탱크 커버의 신규 모델 개발을 위한 CAE 기반 프레스 성형 공정 설계", Design & Manufacturing, 14(2), pp.49~55 (2020), 한국금형공학회[DOI]