다양한 유무연 도금 리드프레임에 적용된 Sn-8Zn-3Bi 솔더접합부의 열충격 신뢰성 평가
Reliability of Sn-8Zn-3Bi Solder Paste Applied to Lead andLead-free Plating on Lead-frame under Thermal Shock Test
0
조회
0
다운로드
2
인용
0
참고문헌
초록
Abstract
The pull strength and fracture mechanism were investigated to evaluate the reliability and compatibility of Sn-8Zn-3Bi joints, the solder paste on lead and lead-free plating under thermal shock conditions. At the Sn-8Zn-3Bi solder joint, no crack initiation was observed during thermal shock test. After 1000 cycles, the strength of the solder joint decreased not sharply but reduced gradually compared with initial conditions. The decrement of strength was affected by g-Cu5Zn8 IMC growth which caused the IMC fracture on the fracture surface and a change in fracture mode and initial crack point. Clearly, the Sn8Zn-3Bi solder shows good reliability properties and compatibility with lead-free plated Cu LF under thermal shock temperatures between 248K and 423K.
참고문헌 (13)
- "RoHS Regulations (UK) Government Guidance Notes" (2005), RoHS Regulations (UK) Government Guidance Notes
- "Lead-Free Electronics" (2006), John Wiley Publishing, New York
- "Long term mechanical reliability with lead-free solders", 16, pp.13~ (2004)
- "Lead-free Soldering An Analysis of the Current Status" (1999)
- "Lead-free solders in microelectronics", 27, pp.95~ (2000)
- "-free solders for electronic packing. J Electron Mater" (1994)
- "The reliability study of selected Sn-Zn based lead-free solders on Au", Ni-P, pp.2003, 43(3)[DOI]
- "Fundamental of Microsystems Packaging" (2001), McGraw-Hill
- "Microstructure and soldering properties of CSP solder joints using Sn-Zn-Bi solder", 87 (2003), Kohala Coast, HI, USA
- "Wetting and interfacial reactions of Sn-Zn based lead-free solder alloys as replacement of Sn-Pb solder", 178 (2005), Shanghai, China
- "Influence of P content in electroless plated Ni-P alloy film on interfacial structures and strength between Sn-Zn solder and plated Au", Ni-P alloy film, 2002, pp.43, 1887~
- "Properties of quad flat package joints using Sn-Zn-Bi solder with varying lead-plating materials", pp.1540~ (2003), San Diego, CA, USA
- "Influence of Interfacial Reaction on Reliability of QFP Joints with Sn-Ag Based Pb Free Solders", 42, pp.794~ (2001)