Microstructural Study of Creep-Fatigue Crack Propagation for Sn-3.0Ag-0.5Cu Lead-Free Solder
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Crack propagation mechanisms of Sn-3.0Ag-0.5Cu solder were studied in strain controlled push-pull creepfatigue conditions using the fast-fast (pp) and the slow-fast (cp) strain waveforms at 313 K. Transgranular cracking was found in the pp strain waveform which led to the cycle-dominant crack propagation and intergranular cracking in the cp strain waveform that led to the time-dominant crack propagation. The time-dominant crack propagation rate was faster than the cycle-dominant crack propagation rate when compared with J-integral range which resulted from the creep damage at the crack tip in the cp strain waveform. Clear recrystallization around the crack was found in the pp and the cp strain waveforms, but the recrystallized grain size in the cp strain waveform was smaller than that in the pp strain waveform. The cycle-dominant crack propagated in the normal direction to the specimen axis macroscopically, but the time-dominant crack propagated in the shear direction which was discussed in relation with shear micro cracks formed at the crack tip.
Abstract
Crack propagation mechanisms of Sn-3.0Ag-0.5Cu solder were studied in strain controlled push-pull creepfatigue conditions using the fast-fast (pp) and the slow-fast (cp) strain waveforms at 313 K. Transgranular cracking was found in the pp strain waveform which led to the cycle-dominant crack propagation and intergranular cracking in the cp strain waveform that led to the time-dominant crack propagation. The time-dominant crack propagation rate was faster than the cycle-dominant crack propagation rate when compared with J-integral range which resulted from the creep damage at the crack tip in the cp strain waveform. Clear recrystallization around the crack was found in the pp and the cp strain waveforms, but the recrystallized grain size in the cp strain waveform was smaller than that in the pp strain waveform. The cycle-dominant crack propagated in the normal direction to the specimen axis macroscopically, but the time-dominant crack propagated in the shear direction which was discussed in relation with shear micro cracks formed at the crack tip.
참고문헌 (25)
- R. G. Ross Jr, "Solder Creep-Fatigue Interactions with Flexible Leaded Parts", J. Electron. Packag., 113, pp.185~ (1992)
- R. M. V. Pidaparti, "Fatigue Crack Propagation Life Analysis of Solder Joints under Thermal Cyclic Loading", Theo. Appl. Fract. Mech, 24, pp.157~ (1996)
- J. Zhao, "Fatigue Crack-Growth Behavior of Sn-Ag-Cu and Sn-Ag-Cu-Bi Lead-Free Solders", J. Electron. Mater.,, 31(8), pp.879~ (2002)
- C. Kanchanomai, "Low-Cycle Fatigue Behavior of Sn-Ag, Sn-Ag-Cu, and Sn-Ag-Cu-Bi Lead-Free Solders", J. Electron. Mater., 31(5), pp.456~ (2002)
- T. W. Woo, "Creep- Fatigue Crack Propagation Behavior of Sn-3.0Ag-0.5Cu Lead-Free Solder", Proc. Asian Pacific Conference for Materials and Mechanics (APCMM) (2009), The Japan Society of Mechanical Engineers (JSME)
- M. Nozaki, "Creep-Fatigue Life Evaluation for Sn-3.5Ag Solder", J. Eng. Mater. Tech., 128, pp.142~ (2006)
- M. Nozaki, "Crack Propagation Behavior of Sn-3.5Ag Solder in Low Cycle Fatigue", Int. J. Fatigue, 30, pp.1729~ (2008)
- 최재경, "무연 솔더바에 대한 신뢰성 평가기준에 관한 연구", 마이크로전자 및 패키징학회지, 14(2), pp.23~34 (2007), 한국마이크로전자및패키징학회
- 채규상, "Practical Application of Sn-3.0Ag-0.5Cu Lead Free Solder in Electronic Production", 마이크로전자 및 패키징학회지, 12(1), pp.65~71 (2005), 한국마이크로전자및패키징학회
- D. R. Frear, "The Mechanics of Solder Alloy Interconnects" (1994), Van Nostrand Reinhold
- H. Nose, "Crack Initiation and Propagation Behavior of Three Types of Solders in Torsion Low Cycle Fatigue (in Japanese)", Trans. Jpn. Soc. Mech. Eng.: A, 69(684), pp.1222~ (2003)
- C. Kanchanomai, "Strain-Rate Effects on Low Cycle Fatigue Mechanism of Eutectic Sn-Pb Solder", Int. J. Fatigue, 24, pp.987~ (2002)
- X. Q. Shi, "Low Cycle Fatigue Analysis of Temperature and Frequency Effects in Eutectic Solder Alloy", Int. J. Fatigue, 22, pp.217~ (2000)
- C. K. Lin, "Effects of Strain Ratio and Tensile Hold Time on Low-Cycle Fatigue of Lead-Free Sn- 3.5Ag-0.5Cu Solder", J. Electron. Mater., 35(2), pp.292~ (2006)
- M. L. Huang, "Creep Resistance of Tin-based Lead-Free Solder Alloys", J. Electron. Mater., 34(11), pp.1373~ (2005)
- H. G. Song, "The Creep Properties of Lead-Free Solder Joints", JOM, 54, pp.30~ (2002)
- 유진, "미세조직이 Sn계 무연솔더의 크리프 특성에 미치는 영향", 마이크로전자 및 패키징학회지, 10(3), pp.29~ (2003), 한국마이크로전자및패키징학회
- V. I. Igoshev, "Microstructure Changes in Sn-3.5Ag Solder Alloy during Creep", J. Electron. Mater., 27(12), pp.1367~ (1998)
- JSMS Committee on High Temperature Strength of Materials, "Low Cycle Fatigue Standard for Solder Testing (in Japanese)" (2000), The Japan Society of Material Science
- "Wikipedia,Wikipedia Foundation.Inc.June(2010)from" (2010)[URL]
- T. W. Woo, "The Studies on the Creep-Fatigue Crack Growth Behavior of Sn- 3.0Ag-0.5Cu Solder", Proc. Korean Society of Mechanical Engineers Fall Conference, pp.354~ (2009), The Koran Society of Mechanical Engineers (KSME)
- S. Taira, "J-Integral Approach to Crack Propagation under Combined Creep and Fatigue Condition", J. Soc. Mater. Sci., 28(308), pp.414~ (1979)
- V. Raman, "Dynamic Recrystallization during High Temperature Fatigue", Scripta Metall., 20, pp.1343~ (1986)
- Z. Mei, "Effects of Cooling Rate on Mechanical Properties of Near- Eutectic Tin-Lead Solder Joints", J. Electron. Mater, 20, pp.599~ (1991)
- M. Sakane, "Biaxial Low Cycle Fatigue for Notched, Cracked and Smooth Specimens at High Temperatures", J. Eng. Mater. Tech., 110, pp.48~ (1988)