In this study, Al and Zn arc thermal spray coatings were carried out onto the substrate of SS400 steel to improve corrosion resistance and durability of hull structural steel for ship in marine environment. Therefore cavitation-erosion test was conducted to evaluate the durability of painted and thermal spray coated specimens. And then the damaged surface morphology and weight loss were obtained to compare with each other, respectively. As a result, the painted specimen was the poorest cavitation resistance characteristics because surface damage behavior appeared to be exfoliated in bulk shape during the cavitation experiment. And Zn thermal spray coating layer presented the significant surface damage depth due to relatively low surface hardness and local cavitation damage tendency. On the other hand, as a result of the weight loss analysis, the painting layer presented the poorest cavitation resistance and the Al thermal spray coating layer relatively showed the best results after cavitation experiment.
Abstract
In this study, Al and Zn arc thermal spray coatings were carried out onto the substrate of SS400 steel to improve corrosion resistance and durability of hull structural steel for ship in marine environment. Therefore cavitation-erosion test was conducted to evaluate the durability of painted and thermal spray coated specimens. And then the damaged surface morphology and weight loss were obtained to compare with each other, respectively. As a result, the painted specimen was the poorest cavitation resistance characteristics because surface damage behavior appeared to be exfoliated in bulk shape during the cavitation experiment. And Zn thermal spray coating layer presented the significant surface damage depth due to relatively low surface hardness and local cavitation damage tendency. On the other hand, as a result of the weight loss analysis, the painting layer presented the poorest cavitation resistance and the Al thermal spray coating layer relatively showed the best results after cavitation experiment.
참고문헌 (22)
- G. S. Kim, "A Study on Cavitation Erosion of Al and Zn Coating by Thermal Spray Method", J. Res. Inst. Adv. Tech, 14, pp.45~51 (2003)
- H. I. Lee, "Study on New Candidate Coating Materials to Challenge Rudder Cavitation Damage", CORROSION SCIENCE AND TECHNOLOGY, 7(5), pp.274~282 (2008), 한국부식방식학회
- 홍성모, "화염급냉 표면처리된 Cu0aAl-4.5Ni-4.5Fe 합금의 b' 마르텐사이트 형성에 의한 케비테이션 침식 저항성 향상에 관한 연구", 한국표면공학회지, 37(4), pp.234~241 (2004), 한국표면공학회
- U. J. Im, "A Study on the Behaviour of Erosion-Corrosion at the Bearing Metals by Cavitation(2)-for Influence of Sea Water at Marine Lubricating Oil-", J. Corros. Sci. Soc. of Korea, 22, pp.176~182 (1993)
- 신중하, "용사 도막의 내식성에 관한 전기화학적 평가", CORROSION SCIENCE AND TECHNOLOGY, 9(6), pp.325~330 (2010), 한국부식방식학회
- G. Jandin, "Correlations Between Operating Conditions, Microstructure and Mechanical Properties of Twin Wire Arc Sprayed Steel Coatings", Mater. Sci. Eng. A, 349, pp.298~305 (2003)
- W. M. Zhao, "Erosion–Corrosion of Thermally Sprayed Coatings in Simulated Splash Zone", Surf. Coat. Tech, 205, pp.2267~2272 (2010)
- F. Ahnia, "Evaluation of Aluminum Coatings in Simulated Marine Environment", Surf. Coat. Tech, 220, pp.232~236 (2013)
- G. Hou, "Cavitation Erosion of Several Oxy-fuel Sprayed Coatings Tested in Deionized Water and Artificial Seawater", Wear, 311, pp.81~92 (2014)
- A. Amirudin, "Application of Electrochemical Impedance Spectroscopy to Study the Degradation of Polymer-Coated Metals", J. Prog. Org. Coat, 26, pp.1~28 (1995)
- G. R. Kim, "Electrochemical Characterization of Epoxy Coated Steel under Cathodic Protection", J. Corros. Prot, 5, pp.52~58 (2006)
- S. J. Kim, "Effects of F−Si Sealer on Electrochemical Characteristics of 15%Al−85%Zn Alloy Thermal Spray Coating", J. Trans. Nonferrous Met. Soc. China, 21, pp.2798~2804 (2011)
- Y. Q. Zhang, "Performance Study of Nano Structured WC-Co Coatings Sprayed by HVOF", J. China Surf. Eng, 18, pp.25~29 (2005)
- 문경만, "용사 도막의 내식성에 관한 전기화학적 평가", 한국마린엔지니어링학회지, 34(5), pp.670~677 (2010), 한국마린엔지니어링학회
- C. T. Kwok, "Laser Surface Modification of UNS S31603 Stainless Steel. Part II : Cavitation Erosion Characteristics", J. Mater. Sci. & Eng. Struct. Mater, 290, pp.74~88 (2000)
- D. S. Won, "Cavitation Behavior of A 5083 Alloy by Vibratory Cavitation Tester", J. Corros. Sci. Soc. of Korea, 23, pp.215~225 (1994)
- J. F. Santa, "Slurry Erosion of Thermal Spray Coatings and Stainless Steels for Hydraulic Machinery", Wear, 263, pp.258~264 (2007)
- C. E. Correaa, "Wear Mechanisms of Epoxy-Based Composite Coatings Submitted to Cavitation", Wear, 271, pp.2274~2279 (2011)
- K. J. Kim, "A Study on the Cavitation Erosion of Polymeric Materials", Korean Chem. Eng. Res, 32, pp.72~78 (1984)
- L. A. Espitia, "Cavitation Resistance, Microstructure and Surface Topography of Materials Used for Hydraulic Components", J. Tribol. Int, 43, pp.2037~2045 (2010)
- P. V. Rao, "Evaluation of Epoxy Resins in Flow Cavitation Erosion", Wear, 122, pp.77~96 (1988)
- 이승준, "해양환경 하에서 Ni-Cr계 자용성 합금 코팅된 ALBC3 합금의 캐비테이션 특성 평가", 해양환경안전학회지, 19(5), pp.538~544 (2013), 해양환경안전학회[DOI]