아크 용사법을 이용한 Inconel 625 코팅 층의 해수 내 캐비테이션 손상 거동
Cavitation Damage Behavior of Inconel 625 Coating Layer by Arc Thermal Spraying Method in Sea Water
0
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
In this paper, arc thermal spray coating was conducted onto the SS400 steel using Inconel 625 wires in order to improve the durability of marine steel structures, and then investigated cavitation damage behavior of Inconel 625 coating layer in sea water. For the Inconel 625 coating layer, surface hardness appeared similar to that of existing high velocity oxy-fuel coating technology with 380~480 HV, but the porosity of about 6 % was larger relatively. During the cavitation experiment, pit damages were originated and grown at the rough surface and pore defect area of Inconel 625 coating layer. And, after the 72 hours of experimental time, weight loss of Inconel 625 coating layer exhibited gradually increasing tendency due to surface damage effect of the undercut.
Abstract
In this paper, arc thermal spray coating was conducted onto the SS400 steel using Inconel 625 wires in order to improve the durability of marine steel structures, and then investigated cavitation damage behavior of Inconel 625 coating layer in sea water. For the Inconel 625 coating layer, surface hardness appeared similar to that of existing high velocity oxy-fuel coating technology with 380~480 HV, but the porosity of about 6 % was larger relatively. During the cavitation experiment, pit damages were originated and grown at the rough surface and pore defect area of Inconel 625 coating layer. And, after the 72 hours of experimental time, weight loss of Inconel 625 coating layer exhibited gradually increasing tendency due to surface damage effect of the undercut.
참고문헌 (18)
- H. Y. Al-Fadhli, , Surf. Coat. Technol, 200, pp.5782~ (2006)
- G. Bolelli, , Surf. Coat. Technol, 202, pp.4793~ (2008)
- D. A. Walsha, , Electrochim. Acta, 54, pp.4647~ (2009)
- V. Higuera, , J. Mater. Sci, 37, pp.649~ (2002)
- L. Gil, , J. Surf. Eng, 18, pp.309~ (2002)
- L. Pawlowski, "The science and engineering of thermal spray coatings", pp.79~ (2008), John Wiley & Sons
- J. S. Kim, , Corros. Sci. Technol, 1, pp.320~ (2002)
- T. O. Kim, , J. Kor. Inst. Surf. Eng, 33, pp.329~ (2000)
- P. Poza, , Surf. Coat. Technol, 243, pp.51~ (2014)
- A. A. Boudi, , J. Mater. Process. Technol, 173, pp.44~ (2006)
- A. A. Boudi, , J. Mater. Process. Technol, 155–156, pp.2051~ (2004)
- S. J. KIM, , Trans. Nonferrous Met. Soc. China, 21, pp.2798~ (2011)
- 문경만, "용사 도막의 내식성에 관한 전기화학적 평가", 한국마린엔지니어링학회지, 34(5), pp.670~677 (2010), 한국마린엔지니어링학회
- H. M. Hawthorne, , Wear, 225–229, pp.825~ (1999)
- H. Y. Al-Fadhli, , Surf. Coat. Technol, 200, pp.5782~ (2006)
- 한민수, "구리합금에 대한 WC-27NiCr 초고속화염용사 코팅층의 해수내 캐비테이션 특성 평가", CORROSION SCIENCE AND TECHNOLOGY, 11(6), pp.263~269 (2012), 한국부식방식학회
- S. Matthew, , Corros. Sci, 70, pp.203~ (2013)
- J. H. Hwang, , J. Korean Soc. Fish. Technol, 32, pp.302~ (1996)