해수 내 아크 아연 용사코팅 층의 전기화학적 특성
Electrochemical Characteristics of Arc Zn Thermal Spray Coating Layer in Sea Water
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this paper, arc Zn thermal spray coating was carried out on the SS400 steel, and then various electrochemical characteristics and surface damage behavior of Zn thermal spray coating layer were analyzed. As the results, the potential of Zn thermal spray coating layer presented driving voltage above 300 mV compare to that of SS400 steel. The passivity characteristic in anodic polarization curve was not presented. It was adequate to as sacrificial anode material. In the surface damage after galvanostatic experiments, uniform corrosion tendency of Zn thermal spray coating layer was clearly observed with acceleration of the dissolution reaction. In conclusion, Zn thermal spray coating could be determined to represent the corrosion protection effect by stable sacrificial anodic cathodic protection method in seawater because it had sufficient driving voltage and uniform corrosion damage tendency for the SS400 steel.
Abstract
In this paper, arc Zn thermal spray coating was carried out on the SS400 steel, and then various electrochemical characteristics and surface damage behavior of Zn thermal spray coating layer were analyzed. As the results, the potential of Zn thermal spray coating layer presented driving voltage above 300 mV compare to that of SS400 steel. The passivity characteristic in anodic polarization curve was not presented. It was adequate to as sacrificial anode material. In the surface damage after galvanostatic experiments, uniform corrosion tendency of Zn thermal spray coating layer was clearly observed with acceleration of the dissolution reaction. In conclusion, Zn thermal spray coating could be determined to represent the corrosion protection effect by stable sacrificial anodic cathodic protection method in seawater because it had sufficient driving voltage and uniform corrosion damage tendency for the SS400 steel.
참고문헌 (22)
- 이진호, "해양구조물의 방식을 위한 알루미늄 합금의 희생양극적 부식 특성의 전기화학적 평가", 한국표면공학회지, 48(2), pp.68~72 (2015), 한국표면공학회[DOI]
- 김희산, "희생양극 하에서 알루미늄의 해수 부식 거동", 한국표면공학회지, 39(1), pp.25~34 (2006), 한국표면공학회
- Y. H. Jeong, , J. Kor. Inst. Surf. Eng, 47, pp.232~ (2014)
- A. R. Cook, , Anti-Corros. Methods Mater, 23, pp.5~ (1976)
- Y. Liu, , Trans. Nonferrous Met. Soc. China, 14, pp.443~ (2004)
- Y. X. Xiao, , Procedia Eng, 27, pp.1644~ (2012)
- E. Calla, , Trans. Met. Finish. Assoc. India, 10, pp.21~ (2001)
- S. Kuroda, , Corrosion, 62, pp.635~ (2006)
- Q. Jiang, , Electrochim. Acta, 115, pp.644~ (2014)
- Q. Jiang, , Trans. Nonferrous Met. Soc. China, 24, pp.2713~ (2014)
- H. Y. Li, , Surf. Coat. Technol, 235, pp.259~ (2013)
- J. R. Daesen, , Proceeding of the 2nd International Congress on Metallic Corrosion, pp.686~ (1963)
- G. A. El-Mahdy, , Corros. Sci, 42, pp.183~ (2000)
- A. P. Yadav, , Corros. Sci, 46, pp.361~ (2004)
- 문경만, "용사 도막의 내식성에 관한 전기화학적 평가", 한국마린엔지니어링학회지, 34(5), pp.670~677 (2010), 한국마린엔지니어링학회
- 신중하, "용사 도막의 내식성에 관한 전기화학적 평가", CORROSION SCIENCE AND TECHNOLOGY, 9(6), pp.325~330 (2010), 한국부식방식학회
- R. A. Gummow, , Mater. Perform, 32, pp.21~ (1993)
- H. R. Lee, "Corrosion of Metals", Yeunkyung cultural history, 221~ (2011)
- W. von Baeckmann, "Handbook of Cathodic Corrosion Protection", pp.397~ (1997), Gulf publishing
- M. Pourbaix, "Atlas of Electrochemical Equilibria in Aqueous Solution", pp.139~ (1974), NACE
- D. A. Jones, "Principles and Prevention of Corrosion", pp.462~ (1995), Prentice Hall
- S. J. Kim, , Trans. Nonferrous Met. Soc. China, 23, pp.1002~ (2013)