황산 용액에서 Al6061 합금의 아노다이징 피막 형성거동
Formation Behavior of Anodic Oxide Films on Al 6061 Alloy in Sulfuric Acid Solution
1
조회
0
다운로드
10
인용
0
참고문헌
키워드
초록
Formation behavior of aluminum anodic oxide (AAO) films on Al6061 alloy was studied in view of thickness, morphology and defects in the anodic films in 20 vol.% sulfuric acid solution at a constant current density of 40 mA/cm2, using voltage-time curve, observation of anodized specimen colors and surface and cross-sectional morphologies of anodic films with anodization time. With increasing anodizing time, voltage for film formation increased exponentially after about 12 min and its increasing rate decreased after 25 min, followed by a rapid decrease of the voltage after about 28 min. Surface color of anodized specimen became darker with increasing anodizing time up to about 20 min 20 vol.% sulfuric acid solution, while it appeared to be brighter with increasing anodizing time after 20 min. The darkened and brightened surfaces with anodizing time are attributed to an increase in thickness of porous anodic oxide film and a chemical damage of the films due to heat generated by increased resistance of the film, respectively. Cross-sectional observation of AAO films revealed the formation of defects of crack shape at the metal/oxide interface after 15 min which prevents the growth of AAO films. Width and length of the crack-like defect increased with anodizing time up to 25 min of anodizing, and finally the outer part of AAO films was partly dissolved or detached after 30 min of anodizing, resulting in non-uniform surface structures of the AAO films.
Abstract
Formation behavior of aluminum anodic oxide (AAO) films on Al6061 alloy was studied in view of thickness, morphology and defects in the anodic films in 20 vol.% sulfuric acid solution at a constant current density of 40 mA/cm2, using voltage-time curve, observation of anodized specimen colors and surface and cross-sectional morphologies of anodic films with anodization time. With increasing anodizing time, voltage for film formation increased exponentially after about 12 min and its increasing rate decreased after 25 min, followed by a rapid decrease of the voltage after about 28 min. Surface color of anodized specimen became darker with increasing anodizing time up to about 20 min 20 vol.% sulfuric acid solution, while it appeared to be brighter with increasing anodizing time after 20 min. The darkened and brightened surfaces with anodizing time are attributed to an increase in thickness of porous anodic oxide film and a chemical damage of the films due to heat generated by increased resistance of the film, respectively. Cross-sectional observation of AAO films revealed the formation of defects of crack shape at the metal/oxide interface after 15 min which prevents the growth of AAO films. Width and length of the crack-like defect increased with anodizing time up to 25 min of anodizing, and finally the outer part of AAO films was partly dissolved or detached after 30 min of anodizing, resulting in non-uniform surface structures of the AAO films.
참고문헌 (10)
- 문성모, "금속의 양극산화처리 기술", 한국표면공학회지, 51(1), pp.1~11 (2018), 한국표면공학회[DOI]
- Carmen Mijangos, "A review on the progress of polymer nanostructures with modulated morphologies and properties using nanoporous AAO templates", Progress in Polymer Science, 54–55, pp.148~182 (2016)
- 정용수, "실용표면처리기술시리즈 제 5권 양극산화", pp.3~ (2014), 화신문화(주)
- Abel Santos, "Nanoporous anodic aluminum oxide for chemical sensing and biosensors", TrAC Trends in Analytical Chemistry, 44, pp.25~38 (2013)
- Chen-Un Yu, "Pore-size dependence of AAO films on surface roughness of Al-1050 sheets controlled by electropolishing coupled with fractional factorial design", Surface and Coatings Technology, 201, pp.7259~7265 (2007)
- S.-M. Moon, "Growth Mechanism of Anodic Oxide Film on Pure Aluminium in Acidic and Alkaline Solutions", J. of Solid State Electrochemistry, 2, pp.156~161 (1998)
- S.-M. Moon, "A review of Al anodizing", J. Corros. Sci. Soc. of Korea, 26, pp.498~508 (1997)
- Y.-S. Kim, "The Effects of Applied Potential and pH on the Electrochemical Dissolution of Barrier Layer in Porous Anodic Oxide Film on Pure Aluminium", Corrosion Science, 38, pp.329~336 (1996)
- Tim Aerts, , Electrochim. Acta, 54, pp.270~ (2008)
- 문성모, "황산용액에서 Al7075 합금 표면의 양극산화피막 형성거동", 한국표면공학회지, 47(4), pp.155~161 (2014), 한국표면공학회[DOI]