6xxx계 알루미늄 합금의 경질 아노다이징 피막 형성 특성 연구
Formation Characteristics of Hard Anodizing Films on 6xxx Aluminum Alloys
1
조회
0
다운로드
10
인용
0
참고문헌
키워드
초록
In this work, anodizing behavior of 6xxx series aluminum alloys was studied under constant current density and constant voltage conditions in 20% sulfuric acid solution by V-t curves, I-t curves, thickness measurement, observations of surface appearance and cross-sectional observation of anodizing films. The film growth rate of the anodizing films on Al6063, Al6061 and Al6082 obtained at 20 V were 0.63㎛/min. 0.46㎛/min and 0.38㎛/min, respectively. Time to the initiation of imperfections at the oxide/substrate interface under constant current condition was shortened and colors of anodizing films became darker with the amount of alloying elements in 6xxx series aluminum alloys. Based upon the experimental results obtained in this work, it is concluded that maximum anodizing film thickness without interfacial defects is reduced with increasing amount of alloying elements and brighter anodizing films can be obtained by decreasing amount of alloying elements in the aluminum alloys.
Abstract
In this work, anodizing behavior of 6xxx series aluminum alloys was studied under constant current density and constant voltage conditions in 20% sulfuric acid solution by V-t curves, I-t curves, thickness measurement, observations of surface appearance and cross-sectional observation of anodizing films. The film growth rate of the anodizing films on Al6063, Al6061 and Al6082 obtained at 20 V were 0.63㎛/min. 0.46㎛/min and 0.38㎛/min, respectively. Time to the initiation of imperfections at the oxide/substrate interface under constant current condition was shortened and colors of anodizing films became darker with the amount of alloying elements in 6xxx series aluminum alloys. Based upon the experimental results obtained in this work, it is concluded that maximum anodizing film thickness without interfacial defects is reduced with increasing amount of alloying elements and brighter anodizing films can be obtained by decreasing amount of alloying elements in the aluminum alloys.
참고문헌 (10)
- 문성모, "금속의 양극산화처리 기술", 한국표면공학회지, 51(1), pp.1~11 (2018), 한국표면공학회[DOI]
- 정용수, "실용표면처리기술시리즈 제 5권 양극산화", pp.3~ (2014), 화신문화
- S. -M. Moon, "Growth Mechanism of Anodic Oxide Film on Pure Aluminium in Acidic and Alkaline Solutions", J. of Solid State Electrochemistry, 2, pp.156~161 (1998)
- S. -M. Moon, "A review of Al anodizing", J. Corros. Sci. Soc. of Korea, 26, pp.498~508 (1997)
- Y. -S. Kim, "The Effects of Applied Potential and pH on the Electrochemical Dissolution of Barrier Layer in Porous Anodic Oxide Film on Pure Aluminium", Corrosion Science, 38, pp.329~336 (1996)
- 문성모, "황산 용액에서 Al6061 합금의 아노다이징 피막 형성거동", 한국표면공학회지, 51(6), pp.393~399 (2018), 한국표면공학회[DOI]
- 문성모, "황산용액에서 Al7075 합금 표면의 양극산화피막 형성거동", 한국표면공학회지, 47(4), pp.155~161 (2014), 한국표면공학회[DOI]
- Y. Ma, "Discontinuities in the porous anodic film formed on AA2099-T8 aluminium alloy", Corrosion Science, 53, pp.4141~4151 (2011)
- S. Moon, "Growth of anodic oxide films on AC2A alloy in sulphuric acid solution", Corrosion Science, 53, pp.1547~1553 (2011)
- X. Zhou, "Film formation and detachment during anodizing of Al–Mg alloys", Corrosion Science, 41, pp.1599~1613 (1999)