Dielectric Breakdown Behavior of Anodic Oxide Films Formed on Pure Aluminum in Sulfuric Acid and Oxalic Acid Electrolytes
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
This work studies dielectric breakdown behavior of AAO (anodic aluminum oxide) films formed on pure aluminum at a constant current density in 5 ~ 20 vol.% sulfuric acid (SA) and 2 ~ 8 wt.% oxalic acid (OA) solutions. It was observed that dielectric breakdown voltage of AAO film with the same thickness increased with increasing concentration of both SA and OA solutions up to 15 vol.% and 6 wt.%, respectively, above which it decreased slightly. The dielectric breakdown resistance of the OA films appeared to be superior to that of SA films. After dielectric breakdown test, cracks and a hole were observed. The crack length increased with increasing SA film thickness but it did not increase with increasing OA film thickness. To explain the reason why shorter cracks formed on the OA films than the SA films after dielectric breakdown test, the generation of tensile stresses at the oxide/ metal interface was discussed in relation to porosity of AAO films obtained from cross-sectional morphologies.
Abstract
This work studies dielectric breakdown behavior of AAO (anodic aluminum oxide) films formed on pure aluminum at a constant current density in 5 ~ 20 vol.% sulfuric acid (SA) and 2 ~ 8 wt.% oxalic acid (OA) solutions. It was observed that dielectric breakdown voltage of AAO film with the same thickness increased with increasing concentration of both SA and OA solutions up to 15 vol.% and 6 wt.%, respectively, above which it decreased slightly. The dielectric breakdown resistance of the OA films appeared to be superior to that of SA films. After dielectric breakdown test, cracks and a hole were observed. The crack length increased with increasing SA film thickness but it did not increase with increasing OA film thickness. To explain the reason why shorter cracks formed on the OA films than the SA films after dielectric breakdown test, the generation of tensile stresses at the oxide/ metal interface was discussed in relation to porosity of AAO films obtained from cross-sectional morphologies.
참고문헌 (24)
- J. M. Runge, "The metallurgy of anodizing aluminum", pp.65~ (2018), Springer
- W. Lee, "Porous anodic aluminum oxide: anodization and templated synthesis of functional nanostructures", Chem. Rev, 114, pp.7487~7556 (2014)
- M. Kim, "Improvement of corrosion properties of plasma in an aluminum alloy 6061-T6 by phytic acid anodization temperature", J. Mater. Res. Technol, 11, pp.219~226 (2021)
- T. C. Cheng, "The electrical and mechanical properties of porous anodic 6061-T6 aluminum alloy oxide film", J. Nanomater, 16, pp.141~ (2015)
- O. E. Tchufistov, "Breakdown voltage and electrical strength of oxide coatings formed on aluminum alloys by electrolytic oxidation methods", Mater. Today : Proc, 38, pp.1728~1731 (2021)
- S. Wei, "Improving insulation and thermal conductivity of anodic coating by plasma discharge treatment", AIP Adv, 11, pp.025334~ (2021)
- S. M. Moon, "A review of anodizing of aluminium", J. Corros. Sci. Soc. of Kor, 26, pp.498~508 (1997)
- S. M. Moon, "Growth of anodic oxide films on AC2A alloy in sulphuric acid solution", Corros. Sci, 53, pp.1547~1553 (2011)
- 문상혁, "Al6061 합금의 정전압 아노다이징 피막의 형성거동 및 버닝에 대한 연구", 한국표면공학회지, 53(1), pp.15~21 (2020), 한국표면공학회
- S. M. Moon, "Behavior of second-phase particles in Al5052 alloy during anodizing in a sulfuric acid solution: CSLM observation", J. Electrochem. Soc, 151, pp.B399~B405 (2004)[DOI]
- S. M. Moon, "The mechanism of stress generation during the growth of anodic oxide films on pure aluminium in acidic solutions", Electrochim. Acta, 43, pp.3117~3126 (1998)
- M. Ue, "Anodic", ~
- 문상혁, "6xxx계 알루미늄 합금의 경질 아노다이징 피막 형성 특성 연구", 한국표면공학회지, 52(4), pp.203~210 (2019), 한국표면공학회[DOI]
- 문성모, "황산 용액에서 Al6061 합금의 아노다이징 피막 형성거동", 한국표면공학회지, 51(6), pp.393~399 (2018), 한국표면공학회[DOI]
- 문성모, "황산용액에서 Al7075 합금 표면의 양극산화피막 형성거동", 한국표면공학회지, 47(4), pp.155~161 (2014), 한국표면공학회[DOI]
- A. P. Leontiev, "Complex influence of temperature on oxalic acid anodizing of aluminium", Electrochim. Acta, 319, pp.88~94 (2019)
- H. Asoh, "Forming hard anodic films on aluminum by anodization in oxalic acid and alcohol", J. Electrochem. Soc, 168, pp.103506~ (2021)
- K. Chernyakova, "Formation of ordered anodic alumina nanofibers during aluminum anodizing in oxalic acid at high voltage and electrical power", Surf. Coat. Technol, 394, pp.125813~ (2020)
- A. G. Owens, "Large-pores anodizing of 5657 aluminum alloy in phosphoric acid : An in-situ electrochemical study", Electrochim. Acta, 382, pp.138303~ (2021)
- M. R. Nickel, "The effect of chemical additives in phosphoric acid anodization of aluminum-tantalum thin films", Thin Solid Films, 685, pp.245~253 (2019)
- T. Kikuchi, "Self-ordering of porous anodic alumina fabricated by anodizing in chromic acid at high temperature", J. Electrochem. Soc, 168, pp.093501~ (2021)
- D. Elabar, "Effect of sulphate impurity in chromic acid anodizing of aluminium", Corros. Sci, 100, pp.377~385 (2015)
- Z. Ding, "Morphology perspective on chromic acid anodizing replacement by thin film sulfuric acid anodizing", Surf. Coat. Technol, 350, pp.31~39 (2018)
- T. Kikuchi, "Porous aluminum oxide formed by anodizing in various electrolyte species", Curr. Nanosci, 11, pp.560~571 (2015)