Hybrid PVD로 제조된 Ti-Me-N (Me=V, Si 및 Nb) 나노 박막의 미세구조와 마모특성
Microstructure and Wear Resistance of Ti-Me-N (Me=V, Nb and Si) Nanofilms Prepared by Hybrid PVD
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Ti based nanocomposite films including V, Si and Nb (Ti-Me-N, Me=V, Si and Nb) were fabricated by hybrid physical vapor deposition (PVD) method consisting of unbalanced magnetron (UBM) sputtering and arc ion plating (AIP). The pure Ti target was used for arc ion plating and other metal targets (V, Si and Nb) were used for sputtering process at a gas mixture of Ar/N2 atmosphere. Mostly all of the films were grown with textured TiN (111) plane except the Si doped Ti-Si-N film which has strong (200) peak. The microhardness of each film was measured using the nanoindentation method. The minimum value of removal rate (0.5×10^(−15) m^2/N) was found at Nb doped Ti-Nb-N film which was composed of Ti-N and Nb-N nanoparticles with small amount of amorphous phases.
Abstract
Ti based nanocomposite films including V, Si and Nb (Ti-Me-N, Me=V, Si and Nb) were fabricated by hybrid physical vapor deposition (PVD) method consisting of unbalanced magnetron (UBM) sputtering and arc ion plating (AIP). The pure Ti target was used for arc ion plating and other metal targets (V, Si and Nb) were used for sputtering process at a gas mixture of Ar/N2 atmosphere. Mostly all of the films were grown with textured TiN (111) plane except the Si doped Ti-Si-N film which has strong (200) peak. The microhardness of each film was measured using the nanoindentation method. The minimum value of removal rate (0.5×10^(−15) m^2/N) was found at Nb doped Ti-Nb-N film which was composed of Ti-N and Nb-N nanoparticles with small amount of amorphous phases.
참고문헌 (28)
- C. C. Koch, , MRS Bul., 24, pp.146~ (1999)
- A. A. Voevodin, , Thin Solid Films, 370, pp.223~ (2000)
- K. H. Kim, , Surf. Coat. Technol, 298, pp.243~ (2002)
- S. Veprek, , J. Vac. Sic. Technol. A, 17, pp.2401~ (1999)
- J. Musil, , Surf. Coat. Technol., 125, pp.322~ (2000)
- D. Yu, , Appl. Surf. Sci., 255, pp.1865~ (2008)
- I. W. Park, , Thin Solid Films, 447, pp.443~ (2004)
- K. L. Strong, , Thin Solid Films, 406, pp.174~ (2002)
- G. S. Kim, , Surf. Coat. Technol, 171, pp.83~ (2003)
- C. Mitterer, , Surf. Coat. Technol, 120, pp.405~ (1999)
- G. S. Kim, , Thin Solid Films, 506, pp.128~ (2006)
- A. A. Voevodin, , Thin Solid Films, 401, pp.187~ (2001)
- J. Lin, , Acta Mater., 58, pp.1554~ (2010)
- D. V. Shtansky, , J. Mater. Synth. Proc, 6, pp.61~ (1998)
- J. Karch, , Nature, 330, pp.556~ (1987)
- O. D. Sherby, , Progr. Mater. Sci, 33, pp.169~ (1989)
- T. P. Mollart, , Surf. Coat. Technol, 86, pp.231~ (1996)
- P. J. Martina, , Surf. Coat. Technol, 200, pp.2228~ (2005)
- A. A. Voevodin, , Thin Solid Films, 298, pp.107~ (1997)
- A. A. Voevodin, , Wear, 203, pp.51~ (1997)
- D. Depla, "Handbook of Deposition Technologies for Films and Coatings", pp.253~294 (2010), Elsevier
- E. Ribeiro, , Surf. Coat. Technol, 188, pp.351~ (2004)
- "파인 세라믹스－단일체 세라믹스의 볼.온.디스크법에 의한 마찰.마모 시험 방법", KS L 1606 한국표준협회, ~ (2003)
- B. V. Crist, "XPS Handbook of the Elements and Native Oxides", pp.458~ (2000), John Wiley & Sons
- G. V. Samsonov, "Physico-chemical Properties of Oxides" (1976), Metallurgy
- G. V. Samsonov, , Powder Metall. Met. Ceram., 7(2), pp.107~ (1968)
- G. S. Fox-Rabinovich, , Surf. Coat. Technol, 202, pp.2015~ (2008)
- H. J. Holleck, , J. Vac. Sci. Technol., 4, pp.2661~ (1986)