전기화학적 방법으로 수소장입시킨 자동차 강판재의 수소 영향
The Effect of Hydrogen in Automobile High Strength Steel Sheets Charged with Hydrogen by Using Electrochemical Method
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
High strength steel sheets used for automobile outer-panels have been intensively studied for developing a lightweight automobile under a strong pressure of the requirements for enhancing the mileage and energy saving in production of automobile parts. It is known that high strength steels are susceptible to hydrogen embrittlement, The susceptibility to hydrogen embrittlement increases with increasing its strength. However,the effect of hydrogen on the fracture behavior of high strength steels, though investigated extensively, has not been fully understood. In this paper, hydrogen was charged with 590DP steels by electrochemical method and its content was measured by hydrogen determinator with the different charging conditions. It was shown that the SP energy and maximum load decreased with increasing charging time. The results of SEM-fractography investigation for the hydrogen contained samples showed that a small portion of dimples on cleavagefractured surface were observed and the size of the dimples were decreased with increasing hydrogen charging time.
Abstract
High strength steel sheets used for automobile outer-panels have been intensively studied for developing a lightweight automobile under a strong pressure of the requirements for enhancing the mileage and energy saving in production of automobile parts. It is known that high strength steels are susceptible to hydrogen embrittlement, The susceptibility to hydrogen embrittlement increases with increasing its strength. However,the effect of hydrogen on the fracture behavior of high strength steels, though investigated extensively, has not been fully understood. In this paper, hydrogen was charged with 590DP steels by electrochemical method and its content was measured by hydrogen determinator with the different charging conditions. It was shown that the SP energy and maximum load decreased with increasing charging time. The results of SEM-fractography investigation for the hydrogen contained samples showed that a small portion of dimples on cleavagefractured surface were observed and the size of the dimples were decreased with increasing hydrogen charging time.
참고문헌 (13)
- R. O. Pocha, , Mater. Sci, Eng., 391A, pp.296~ (2005)
- K. Yokoyama, , J. Sakai, Acta Mater., 57, pp.1875~ (2009)
- 강계명, "수소주입에 따른 590 MPa급 DP강 표면층의 미소경도와 조직특성", 한국재료학회지, 20(11), pp.581~585 (2010), 한국재료학회
- J. Watanabe, , J. Iron Steel Inst. Jpn., 82, pp.947~ (1996)
- C. H. Yang, , J. Nucl. Mater., 335, pp.395~ (2004)
- "Standard Test Method for Ball Punch Deformation of Metallic Sheet Material", ASTM E643-84, ~ (2000)
- G. E. Lucas, , Metall. Mater. Trans., 21A, pp.1105~ (1990)
- 최종운, "미소경도 측정에 의한 590DP강 Subsurface Zone 내 수소취성 평가", 한국재료학회지, 21(11), pp.581~586 (2011), 한국재료학회
- 박재우, "소형펀치시험을 이용한 자동차용 고강도강 수소취성 평가", 한국재료학회지, 22(1), pp.29~34 (2012), 한국재료학회
- 강계명, "자동차 박강판용 고강도 DP강 표면층의 수소거동", 한국가스학회지, 14(6), pp.39~44 (2010), 한국가스학회
- 이철치, "고강도 DP강과 TRIP강의 표면 수소 주입량에 따른 수소취성평가", 한국표면공학회지, 45(3), pp.130~135 (2012), 한국표면공학회[DOI]
- T. Zhang, , Mater. Sci. Eng. A, 347, pp.291~ (2003)
- K. Murakami, , ASME, 6, pp.563~ (2006)