2종 전해질에서의 전기화학적 수소주입조건에 따른 680 MPa DP 박강판의 수소취성
Hydrogen Embrittlement of 680 MPa DP sheet steel with Electrochemical Hydrogen charging conditions of Two Electrolytes
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
In this paper, the behavior of hydrogen embrittlement of 680MPa DP sheet steel according to hydrogen charging conditions in acid and alkali electrolytes atmosphere was investigated. At this time, 0.5 M H2SO4 and 0.5M NaOH was used for electrolytes atmosphere and the effect on embrittlemnet of 680MPa DP sheet steel according to current density and charging time was evaluated by the change of subsurface microhardness in DP specimens chared hydrogen. As a result of this experiment, the microhardness of the layer directly below the surface was increased more than the microhardness of the subsurface zone in both electrolytes cases, but the change of the subsurface microhardness in both electrolytes was more affected by the increase of charging time than the increase of current density. The microhardness of subsurface zone in 0.5 M H2SO4 acid electrolyte was increased more than the microhardness in 0.5M NaOH alkali electrolyte. It was supposed that acid atmosphere was more sensitive to hydrogen embrittlement than alkali atmosphere on electrolyte atmosphere of hydrogen charge.
Abstract
In this paper, the behavior of hydrogen embrittlement of 680MPa DP sheet steel according to hydrogen charging conditions in acid and alkali electrolytes atmosphere was investigated. At this time, 0.5 M H2SO4 and 0.5M NaOH was used for electrolytes atmosphere and the effect on embrittlemnet of 680MPa DP sheet steel according to current density and charging time was evaluated by the change of subsurface microhardness in DP specimens chared hydrogen. As a result of this experiment, the microhardness of the layer directly below the surface was increased more than the microhardness of the subsurface zone in both electrolytes cases, but the change of the subsurface microhardness in both electrolytes was more affected by the increase of charging time than the increase of current density. The microhardness of subsurface zone in 0.5 M H2SO4 acid electrolyte was increased more than the microhardness in 0.5M NaOH alkali electrolyte. It was supposed that acid atmosphere was more sensitive to hydrogen embrittlement than alkali atmosphere on electrolyte atmosphere of hydrogen charge.
참고문헌 (8)
- 강계명, "수소주입에 따른 590 MPa급 DP강 표면층의 미소경도와 조직특성", 한국재료학회지, 20(11), pp.581~585 (2010), 한국재료학회
- 최종운, "미소경도 측정에 의한 590DP강 Subsurface Zone 내 수소취성 평가", 한국재료학회지, 21(11), pp.581~586 (2011), 한국재료학회
- 이철치, "고강도 DP강과 TRIP강의 표면 수소 주입량에 따른 수소취성평가", 한국표면공학회지, 45(3), pp.130~135 (2012), 한국표면공학회
- 박재우, "소형펀치시험을 이용한 자동차용 고강도강 수소취성 평가", 한국재료학회지, 22(1), pp.29~34 (2012), 한국재료학회
- 강계명, "수소주입시킨 다상조직강의 Subsurface Zone 내 취성화 거동", 한국표면공학회지, 46(1), pp.48~53 (2013), 한국표면공학회
- 최종운, "수소장입시킨 590 MPa DP강의 표면층 물성변화에 관한 수소의 영향", 한국표면공학회지, 46(3), pp.126~132 (2013), 한국표면공학회
- L. Marchetti, , Int. J. Hydrogen Energy, 36, pp.15880~ (2011)
- H. Luo, , Mater. Corr, 64, pp.26~ (2013)