수소장입시킨 590 MPa DP강의 표면층 물성변화에 관한 수소의 영향
The Effect of Hydrogen on the Variation of Properties at the Surface Layers of 590 MPa DP Steels Charged with Hydrogen
1
조회
0
다운로드
5
인용
0
참고문헌
키워드
초록
It was investigated that the effects of hydrogen charging on the properties of 590 MPa Dual Phase(DP)steels at the surface layers. The hydrogen-charging time was changed from 5 to 50 hours and current densities from 100, 150, and 200 mA/cm2, respectively. It was found that the hydrogen content in the specimen was increased with as the charging time and the current density. The microvickers hardness of the subsurface zone was increased from 215.3 HV to 239.5 HV due to the increase in current density and charging time. The comparison of the absorbed energies tested by a small-punch (SP) test showed that the absorbed energy of the specimen was greatly reduced from 436 to 283 kgf-mm2 because of hydrogen embrittlement. It was confirmed that bulb aspects of fracture surface became more brittle with increasing hydrogen content.
Abstract
It was investigated that the effects of hydrogen charging on the properties of 590 MPa Dual Phase(DP)steels at the surface layers. The hydrogen-charging time was changed from 5 to 50 hours and current densities from 100, 150, and 200 mA/cm2, respectively. It was found that the hydrogen content in the specimen was increased with as the charging time and the current density. The microvickers hardness of the subsurface zone was increased from 215.3 HV to 239.5 HV due to the increase in current density and charging time. The comparison of the absorbed energies tested by a small-punch (SP) test showed that the absorbed energy of the specimen was greatly reduced from 436 to 283 kgf-mm2 because of hydrogen embrittlement. It was confirmed that bulb aspects of fracture surface became more brittle with increasing hydrogen content.
참고문헌 (16)
- R. Kot, , TMS, 1979, pp.362~
- R. G. Davies, , J. Met, 31, pp.17~ (1979)
- G. Katano, , J. Mater. Sci, 36, pp.2277~ (2001)
- J. P. Hirth, , Metall. Trans., 11A, pp.861~ (1980)
- R. G. Davies, , Metall. Trans., 12A, pp.1668~ (1981)
- W. Y. Choo, , Metall. Trans., 13A, pp.135~ (1982)
- A. R. Troiano, , ASM Trans, 52, pp.54~ (1960)
- 최종운, "미소경도 측정에 의한 590DP강 Subsurface Zone 내 수소취성 평가", 한국재료학회지, 21(11), pp.581~586 (2011), 한국재료학회
- 박재우, "소형펀치시험을 이용한 자동차용 고강도강 수소취성 평가", 한국재료학회지, 22(1), pp.29~34 (2012), 한국재료학회
- 강계명, "수소주입시킨 다상조직강의 Subsurface Zone 내 취성화 거동", 한국표면공학회지, 46(1), pp.48~53 (2013), 한국표면공학회[DOI]
- H. Matsui, , Mater. Sci. Eng, 40, pp.227~ (1979)
- "Standard Test Method for Ball Punch Deformation of Metallic Sheet Material", ASTM E643-84, ~ (2000)
- M. Wang, , Corros. Sci, 49, pp.4081~ (2007)
- 이철치, "고강도 DP강과 TRIP강의 표면 수소 주입량에 따른 수소취성평가", 한국표면공학회지, 45(3), pp.130~135 (2012), 한국표면공학회[DOI]
- T. Zhang, , Mater. Sci. Eng., A347, pp.291~ (2003)
- Y. Z. Liu, , Scripta Mater, 52, pp.821~ (2005)