초경합금에 나노결정질 다이아몬드 코팅 시 금속 중간층의 효과
Effect of Metal Interlayers on Nanocrystalline Diamond Coating over WC-Co Substrate
2
조회
0
다운로드
5
인용
0
참고문헌
키워드
초록
For the coating of diamond films on WC-Co tools, a buffer interlayer is needed because Co catalyzes diamond into graphite. W and Ti were chosen as candidate interlayer materials to prevent the diffusion of Co during diamond deposition. W or Ti interlayer of 1 μm thickness was deposited on WC-Co substrate under Ar in a DC magnetron sputter. After seeding treatment of the interlayer-deposited specimens in an ultrasonic bath containing nanometer diamond powders, 2 μm thick nanocrystalline diamond (NCD) films were deposited at 600oC over the metal layers in a 2.45 GHz microwave plasma CVD system. The crosssectional morphology of films was observed by FESEM. X-ray diffraction and visual Raman spectroscopy were used to confirm the NCD crystal structure. Micro hardness was measured by nano-indenter. The coefficient of friction (COF) was measured by tribology test using ball on disk method. After tribology test, wear tracks were examined by optical microscope and alpha step profiler. Rockwell C indentation test was performed to characterize the adhesion between films and substrate. Ti and W were found good interlayer materials to act as Co diffusion barriers and diamond nucleation layers. The COFs on NCD films with W or Ti interlayer were measured as less than 0.1 whereas that on bare WC-Co was 0.6~1.0. However, W interlayer exhibited better results than Ti in terms of the adhesion to WC-Co substrate and to NCD film. This result is believed to be due to smaller difference in the coefficients of thermal expansion of the related films in the case of W interlayer than Ti one. By varying the thickness of W interlayer as 1, 2, and 4 μm with a fixed 2 μm thick NCD film, no difference in COF and wear behavior but a significant change in adhesion was observed. It was shown that the thicker the interlayer, the stronger the adhesion. It is suggested that thicker W interlayer is more effective in relieving the residual stress of NCD film during cooling after deposition and results in stronger adhesion.
Abstract
For the coating of diamond films on WC-Co tools, a buffer interlayer is needed because Co catalyzes diamond into graphite. W and Ti were chosen as candidate interlayer materials to prevent the diffusion of Co during diamond deposition. W or Ti interlayer of 1 μm thickness was deposited on WC-Co substrate under Ar in a DC magnetron sputter. After seeding treatment of the interlayer-deposited specimens in an ultrasonic bath containing nanometer diamond powders, 2 μm thick nanocrystalline diamond (NCD) films were deposited at 600oC over the metal layers in a 2.45 GHz microwave plasma CVD system. The crosssectional morphology of films was observed by FESEM. X-ray diffraction and visual Raman spectroscopy were used to confirm the NCD crystal structure. Micro hardness was measured by nano-indenter. The coefficient of friction (COF) was measured by tribology test using ball on disk method. After tribology test, wear tracks were examined by optical microscope and alpha step profiler. Rockwell C indentation test was performed to characterize the adhesion between films and substrate. Ti and W were found good interlayer materials to act as Co diffusion barriers and diamond nucleation layers. The COFs on NCD films with W or Ti interlayer were measured as less than 0.1 whereas that on bare WC-Co was 0.6~1.0. However, W interlayer exhibited better results than Ti in terms of the adhesion to WC-Co substrate and to NCD film. This result is believed to be due to smaller difference in the coefficients of thermal expansion of the related films in the case of W interlayer than Ti one. By varying the thickness of W interlayer as 1, 2, and 4 μm with a fixed 2 μm thick NCD film, no difference in COF and wear behavior but a significant change in adhesion was observed. It was shown that the thicker the interlayer, the stronger the adhesion. It is suggested that thicker W interlayer is more effective in relieving the residual stress of NCD film during cooling after deposition and results in stronger adhesion.
참고문헌 (20)
- D. M. Gruen, , Annu. Rev. Mater. Sci, 29, pp.211~ (1999)
- S. H. Choi, , MRS Proc (2007)
- 정두영, "ZnO", 나노결정다이아몬드 적층 박막 SAW 필터, 2009, pp.42(5), 216~219[DOI]
- 정두영, "A Kinetic Study on the Growth of Nanocrystalline Diamond Particles to Thin Film on Silicon Substrate", 한국표면공학회지, 44(4), pp.131~136 (2011), 한국표면공학회
- 김인섭, "마이크로웨이브 플라즈마 CVD에 의한 나노결정질 다이아몬드 박막 성장 시 DC 바이어스 효과", 한국표면공학회지, 46(1), pp.29~35 (2013), 한국표면공학회[DOI]
- J. E. Butler, , Chem. Vap. Deposition, 14, pp.145~ (2008)
- J. M. Dasch, , Surf. Coat. Technol, 200, pp.2970~ (2006)
- T. B. Massalski, "Binary Alloy Phase Diagrams, vol. 1", pp.835~ (1997), ASM International
- B. S. Park, , Diamond Relat. Mater, 2, pp.910~ (1993)
- M. G. Peters, "European Patent 0519587", A1~ (1992)
- V. G. Ralchenko, , Diamond Relat. Mater, 4, pp.754~ (1995)
- Q. H. Fan, , Diamond Relat. Mater, 7, pp.603~ (1998)
- R. Polini, , Thin Solid Films, 515, pp.4~ (2006)
- X. Xiao, , Diamond Relat. Mater, 18, pp.1114~ (2009)
- R. Polini, , Thin Solid Films, 519, pp.1629~ (2010)
- Y. Tang, , Diamond Relat. Mater, 19, pp.496~ (2010)
- P. K. Chu, , Mater. Chem. Phys, 96, pp.253~ (2006)
- M. Ohring, "Materials Science of Thin Films : Deposition & Structure", pp.732~ (2002), Academic Press
- David R. Lide, "Handbook of Chemistry and Physics" (2008), CRC Press
- H. Guo, , J. Appl. Phys, 107, pp.033722~ (2010)