철강 위에 SiC 중간층을 사용한 나노결정질 다이아몬드 코팅
Nanocrystalline Diamond Coating on Steel with SiC Interlayer
2
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
Nanocrystalline diamond(NCD) films on steel(SKH51) has been investigated using SiC interlayer film. SiC was deposited on SKH51 or Si wafer by RF magnetron sputter. NCD was deposited on SiC at 600oC for 0.5~4 h employing microwave plasma CVD. Film morphology was observed by FESEM and FIB. Film adherence was examined by Rockwell C adhesion test. The growth rate of NCD on SiC/Si substrate was much higher than that on SiC/SKH51. During particle coalescence, NCD growth rate was slow since overall rate was determined by the diffusion of carbon on SiC surface. After completion of particle coalescence, NCD growth became faster with the reaction of carbon on NCD film controlling the whole process. In the case of SiC/SKH51 substrate, a complete NCD film was not formed even after 4 h of deposition. The adhesion test of NCD/SiC/SKH51 samples revealed a delamination of film whereas that of SiC/SKH51 showed a good adhesion. Many voids of less than 0.1 μm were detected on NCD/SiC interface. These voids were believed as the reason for the poor adhesion between NCD and SiC films. The origin of voids was due to the insufficient coalescence of diamond particles on SiC surface in the early stage of deposition.
Abstract
Nanocrystalline diamond(NCD) films on steel(SKH51) has been investigated using SiC interlayer film. SiC was deposited on SKH51 or Si wafer by RF magnetron sputter. NCD was deposited on SiC at 600oC for 0.5~4 h employing microwave plasma CVD. Film morphology was observed by FESEM and FIB. Film adherence was examined by Rockwell C adhesion test. The growth rate of NCD on SiC/Si substrate was much higher than that on SiC/SKH51. During particle coalescence, NCD growth rate was slow since overall rate was determined by the diffusion of carbon on SiC surface. After completion of particle coalescence, NCD growth became faster with the reaction of carbon on NCD film controlling the whole process. In the case of SiC/SKH51 substrate, a complete NCD film was not formed even after 4 h of deposition. The adhesion test of NCD/SiC/SKH51 samples revealed a delamination of film whereas that of SiC/SKH51 showed a good adhesion. Many voids of less than 0.1 μm were detected on NCD/SiC interface. These voids were believed as the reason for the poor adhesion between NCD and SiC films. The origin of voids was due to the insufficient coalescence of diamond particles on SiC surface in the early stage of deposition.
참고문헌 (13)
- D. M. Gruen, , Annu. Rev. Mater. Sci, 29, pp.211~ (1999)
- J. E. Butler, , Chem. Vap. Deposition, 14, pp.145~ (2008)
- V. G. Ralchenko, , Diamond Relat. Mater, 4, pp.754~ (1995)
- Q. H. Fan, , Diamond Relat. Mater, 7, pp.603~ (1998)
- Y. S. Li, , Appl. Mater. Interf, 2, pp.335~ (2010)
- R. Polini, , Thin Solid Films, 515, pp.4~ (2006)
- X. Xiao, , Diamond Relat. Mater, 18, pp.1114~ (2009)
- R. Polini, , Thin Solid Films, 519, pp.1629~ (2010)
- Y. Tang, , Diamond Relat. Mater, 19, pp.496~ (2010)
- 나봉권, "초경합금에 나노결정질 다이아몬드 코팅 시 금속 중간층의 효과", 한국표면공학회지, 46(2), pp.68~74 (2013), 한국표면공학회
- 박동배, "W 및 Ti 박막 위에서 나노결정질 다이아몬드의 성장 거동", 한국표면공학회지, 46(4), pp.145~152 (2013), 한국표면공학회
- 정두영, "A Kinetic Study on the Growth of Nanocrystalline Diamond Particles to Thin Film on Silicon Substrate", 한국표면공학회지, 44(4), pp.131~136 (2011), 한국표면공학회
- 김인섭, "마이크로웨이브 플라즈마 CVD에 의한 나노결정질 다이아몬드 박막 성장 시 DC 바이어스 효과", 한국표면공학회지, 46(1), pp.29~35 (2013), 한국표면공학회