W 및 Ti 박막 위에서 나노결정질 다이아몬드의 성장 거동

Growth of Nanocrystalline Diamond on W and Ti Films

2

조회

0

다운로드

3

인용

0

참고문헌

키워드

주제분류기계공학

초록

The growth behavior of nanocrystalline diamond (NCD) film has been studied for three different substrates,i.e. bare Si wafer, 1 μm thick W and Ti films deposited on Si wafer by DC sputter. The surface roughness values of the substrates measured by AFM were Si < W < Ti. After ultrasonic seeding treatment using nanometer sized diamond powder, surface roughness remained as Si < W < Ti. The contact angles of the substrates were Si (56o) > W (31o) > Ti (0o). During deposition in the microwave plasma CVD system, NCD particles were formed and evolved to film. For the first 0.5h, the values of NCD particle density were measured as Si < W < Ti. Since the energy barrier for heterogeneous nucleation is proportional to the contact angle of the substrate, the initial nucleus or particle densities are believed to be Si < W < Ti. Meanwhile, the NCD growth rate up to 2 h was W > Si > Ti. In the case of W substrate, NCD particles were coalesced and evolved to the film in the short time of 0.5 h, which could be attributed to the fact that the diffusion of carbon species on W substrate was fast. The slower diffusion of carbon on Si substrate is believed to be the reason for slower film growth than on W substrate. The surface of Ti substrate was observed as a vertically aligned needle shape. The NCD particle formed on the top of a Ti needle should be coalesced with the particle on the nearby needle by carbon diffusion. In this case, the diffusion length is longer than that of Si or W substrate which shows a relatively flat surface. This results in a slow growth rate of NCD on Ti substrate. As deposition time is prolonged, NCD particles grow with carbon species attached from the plasma and coalesce with nearby particles, leaving many voids in NCD/Ti interface. The low adhesion of NCD films on Ti substrate is related to the void structure of NCD/Ti interface.

Abstract

The growth behavior of nanocrystalline diamond (NCD) film has been studied for three different substrates,i.e. bare Si wafer, 1 μm thick W and Ti films deposited on Si wafer by DC sputter. The surface roughness values of the substrates measured by AFM were Si < W < Ti. After ultrasonic seeding treatment using nanometer sized diamond powder, surface roughness remained as Si < W < Ti. The contact angles of the substrates were Si (56o) > W (31o) > Ti (0o). During deposition in the microwave plasma CVD system, NCD particles were formed and evolved to film. For the first 0.5h, the values of NCD particle density were measured as Si < W < Ti. Since the energy barrier for heterogeneous nucleation is proportional to the contact angle of the substrate, the initial nucleus or particle densities are believed to be Si < W < Ti. Meanwhile, the NCD growth rate up to 2 h was W > Si > Ti. In the case of W substrate, NCD particles were coalesced and evolved to the film in the short time of 0.5 h, which could be attributed to the fact that the diffusion of carbon species on W substrate was fast. The slower diffusion of carbon on Si substrate is believed to be the reason for slower film growth than on W substrate. The surface of Ti substrate was observed as a vertically aligned needle shape. The NCD particle formed on the top of a Ti needle should be coalesced with the particle on the nearby needle by carbon diffusion. In this case, the diffusion length is longer than that of Si or W substrate which shows a relatively flat surface. This results in a slow growth rate of NCD on Ti substrate. As deposition time is prolonged, NCD particles grow with carbon species attached from the plasma and coalesce with nearby particles, leaving many voids in NCD/Ti interface. The low adhesion of NCD films on Ti substrate is related to the void structure of NCD/Ti interface.

참고문헌 (19)

  1. H. Guo, , J. Appl. Phys, 107, pp.033722~ (2010)
  2. V. G. Ralchenko, , Diamond Relat. Mater, 4, pp.754~ (1995)
  3. Q. H. Fan, , Diamond Relat. Mater, 7, pp.603~ (1998)
  4. N. N. Naguib, , Chem. Phys. Lett, 430, pp.345~ (2006)
  5. R. Polini, , Thin Solid Films, 515, pp.4~ (2006)
  6. L.-J. Chen, , J. Phys. Chem. C, 112, pp.3759~ (2008)
  7. L.-J. Chen, , J. Appl. Phys, 101, pp.064308~ (2007)
  8. N. A. Braga, , Diamond Relat. Mater, 17, pp.1891~ (2008)
  9. S. J. Askari, , Mater. Res. Bull, 43, pp.1086~ (2008)
  10. X. Xiao, , Diamond Relat. Mater, 18, pp.1114~ (2009)
  11. R. Polini, , Thin Solid Films, 519, pp.1629~ (2010)
  12. Y. Tang, , Diamond Relat. Mater, 19, pp.496~ (2010)
  13. Y. C. Chu, , Proc. 11th IEEE Intern. Conf. on Nanotechnology, pp.1367~ (2011)
  14. 나봉권, "초경합금에 나노결정질 다이아몬드 코팅 시 금속 중간층의 효과", 한국표면공학회지, 46(2), pp.68~74 (2013), 한국표면공학회
  15. 정두영, "A Kinetic Study on the Growth of Nanocrystalline Diamond Particles to Thin Film on Silicon Substrate", 한국표면공학회지, 44(4), pp.131~136 (2011), 한국표면공학회
  16. 김인섭, "마이크로웨이브 플라즈마 CVD에 의한 나노결정질 다이아몬드 박막 성장 시 DC 바이어스 효과", 한국표면공학회지, 46(1), pp.29~35 (2013), 한국표면공학회[DOI]
  17. J. P. Schaffer, "The Science and Design of Engineering Materials", pp.297~ (1999), McGraw-Hill Book Co.
  18. R. N. Wenzel, , Ind. Eng. Chem, 28, pp.988~ (1936)
  19. T.-S. Wong, , MRS Bull, 38, pp.366~ (2013)

이 간행물의 다른 논문 (6건)