Inconel 625로 아크 용사코팅된 SS400강의 해수 내 전기화학적 특성
Electrochemical Characteristics of Arc Thermal Sprayed Inconel 625 Coating on SS400 Steel in Seawater
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
In this paper, various electrochemical experiments were conducted in seawater solution to evaluate corrosion damage behavior of arc thermal sprayed Inconel 625 coating on SS400 steel in marine environment. As a result, corrosion damages of thermal sprayed Inconel 625 coating preferentially occurred at the defect area, and they were observed as a form of pitting corrosion in the galvanostatic experiments. In Tafel analysis, corrosion current density of Inconel 625 coating was relatively high due to influence of interconnected pores and Cr oxides in the thermal spray coating layer. On the other hand, the result of the potential measurement, thermal sprayed Inconel 625 coating should need the post-treatment which can compensate the defects like pores and cracks because Inconel 625 coating presented a higher potential of about 290 mV than that of the SS400 steel.
Abstract
In this paper, various electrochemical experiments were conducted in seawater solution to evaluate corrosion damage behavior of arc thermal sprayed Inconel 625 coating on SS400 steel in marine environment. As a result, corrosion damages of thermal sprayed Inconel 625 coating preferentially occurred at the defect area, and they were observed as a form of pitting corrosion in the galvanostatic experiments. In Tafel analysis, corrosion current density of Inconel 625 coating was relatively high due to influence of interconnected pores and Cr oxides in the thermal spray coating layer. On the other hand, the result of the potential measurement, thermal sprayed Inconel 625 coating should need the post-treatment which can compensate the defects like pores and cracks because Inconel 625 coating presented a higher potential of about 290 mV than that of the SS400 steel.
참고문헌 (24)
- A. Neville, "Study of Passive Film on Stainless Steels and High Grade Nickel Base Alloy Using X-Ray Photoelectron Spectroscopy", J. Br. Corrosion, 35, pp.183~188 (2000)
- H. Y. Al-Fadhli, "The Erosion–Corrosion Behaviour of High Velocity Oxy-Fuel(HVOF)Thermally Sprayed Inconel 625 Coatings on Different Metallic Surfaces", Surf. Coat. Technol, 200, pp.5782~5788 (2006)
- V. Higuera, "Influence of the Thermal-Spray Procedure on the Properties of a Nickel-Chromium Coating", J. Mater. Sci, 37, pp.649~654 (2002)
- L. Gil, "Effects of HVOF Parameters on Adhesion and Microstructure of Thermal Sprayed NiWCrBSi Coatings", J. Surf. Eng, 18, pp.309~315 (2002)
- T. Y. Cho, "Friction Behavior of High Velocity Oxygen Fuel (HVOF) Thermal Spray Coating Layer of Nano WC-Co Powder", 한국표면공학회지, 40(4), pp.170~174 (2007), 한국표면공학회
- 김길수, "초고속 스핀들의 내구성 향상을 위한 WC-Co 분말의 HVOF 용사 코팅", 한국표면공학회지, 39(4), pp.179~189 (2006), 한국표면공학회
- 조동율, "Comparison of HVOF Thermal Spray Coatings of T800 and WC-Co Powders", 한국표면공학회지, 39(6), pp.295~301 (2006), 한국표면공학회
- A. A. Boudi, "HVOF Coating of Inconel 625 onto Stainless and Carbon Steel Surfaces: Corrosion and Bond Testing", J. Mater. Process. Technol, 155, pp.2051~2055 (2004)
- D. Zhang, "Microstructure Formation and Corrosion Behaviour in HVOF-Sprayed Inconel 625 Coatings", Mater. Sci. Eng. A, 344, pp.45~56 (2003)
- H. Herman, "Thermal Spray: Current Status and Future Trends", MRS Bull, 25, pp.17~25 (2000)
- S. Gu, "Computational Fluid Dynamic Modeling of Gas Flow Characteristics in a High-Velocity Oxy-Fuel Thermal Spray System", J. Thermal Spray Tech, 10, pp.461~469 (2001)
- C. H. Chang, "Numerical Simulation of Gas and Particle Flow in a High-Velocity Oxygen-Fuel (HVOF) Torch", J. Thermal Spray Tech, 4, pp.358~365 (1995)
- N. Ahmed, "The Effects of Microstructural Features on the Performance Gap in Corrosion Resistance between Bulk and HVOF Sprayed Inconel 625", Surf. Coat. Technol, 204, pp.2294~2301 (2010)
- H. R. Lee, "Corrosion of Metals", pp.62~ (2011), Yeunkyung Publishing Company
- 문경만, "용접재료별 단강 피스톤 크라운 용접부위의 부식특성에 대한 평가", 한국마린엔지니어링학회지, 38(4), pp.409~417 (2014), 한국마린엔지니어링학회[DOI]
- K. H. Baik, "Spray-Formed Tooling Process by Arc Spraying", Trans. Mater. Process, 14, pp.595~600 (2005)
- T. Rayment, "Phase Transformations and Control of Residual Stresses in Thick Spray-Formed Steel Shells", Metall. Mater. Trans. B, 35B, pp.1113~1122 (2004)
- D. A. Jones, "Control of Temperature Profile for a Spray Deposition Process", IEEE Trans. Control. Syst. Technol, 11, pp.656~667 (2003)
- M. L. Thorpe, "Spray Metal Composite Tooling", Proceeding of the 26th National SAMPE Symposium, pp.374~ (1981)
- W. A. Zanchunk, "The Use of Spray Metal Tooling for Metal Injection Molding", Metal Powder Industries Federation, 25~ (1989)
- Z. Liu, "Improving Corrosion and Wear Performance of HVOF-Sprayed Inconel 625 and WC-Inconel 625Coatings by High Power Diode Laser Treatments", Surf. Coat. Technol, 201, pp.7149~7158 (2007)
- S. J. Kim, "Cavitation and Electrochemical Characteristics of Thermal Spray Coating with Sealing Material", Trans. Nonferrous Met. Soc. China, 23, pp.1002~1010 (2013)
- 박일초, "아크 용사법을 이용한 Inconel 625 코팅 층의 해수 내 캐비테이션 손상 거동", 한국표면공학회지, 48(6), pp.349~353 (2015), 한국표면공학회[DOI]
- D. A. Walsh, "Visualisation of the Local Electrochemical Activity of Thermal Sprayed Anti-Corrosion Coatings Using Scanning Electrochemical Microscopy", Electrochim. Acta, 54, pp.4647~4654 (2009)