고강도 Fe계 합금의 고온 변형 특성
High Temperature Deformation Behavior of Fe-base High Strength Alloys
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Fe-base amorphous alloy and two crystalline phases composite were fabricated. The effect of temperature and strain rate on mechanical properties was evaluated utilizing compression test. Mixture of non-crystalline and crystalline phases were found using X-ray diffraction (XRD) and differential thermal analysis (DTA) tests. Based on glass transition temperature and crystallization temperature, compression tests were performed in the temperature ranging from 560℃ to 700℃ with 20℃ interval. Relationship between microstructure, including fracture surface morphology, and mechanical behavior was studied. The peak stress of Fe-base amorphous alloy was over 2GPa and expected to have a good wear resistance, but it is expected hard to deform because of low ductility. The peak stress and elongation of two crystalline phases composite was over 1GPa and about 20%, therefore it is possible to deform high strength wear resistant materials such as engine valve.
Abstract
Fe-base amorphous alloy and two crystalline phases composite were fabricated. The effect of temperature and strain rate on mechanical properties was evaluated utilizing compression test. Mixture of non-crystalline and crystalline phases were found using X-ray diffraction (XRD) and differential thermal analysis (DTA) tests. Based on glass transition temperature and crystallization temperature, compression tests were performed in the temperature ranging from 560℃ to 700℃ with 20℃ interval. Relationship between microstructure, including fracture surface morphology, and mechanical behavior was studied. The peak stress of Fe-base amorphous alloy was over 2GPa and expected to have a good wear resistance, but it is expected hard to deform because of low ductility. The peak stress and elongation of two crystalline phases composite was over 1GPa and about 20%, therefore it is possible to deform high strength wear resistant materials such as engine valve.
참고문헌 (31)
- A. Inoue, , Mater Trans JIM, 35(2), pp.85~ (1994)
- Hays CC, , hys Rev Lett, 84(13), pp.2901~ (2000)
- Hashimoto K, "Current topics in amorphous materials: physics and technology", pp.167~ (1993), Elsevier Science Publishers
- Wang JG, , J Mater Res, 15(4), pp.913~ (2000)
- Inoue A, , Mater Trans JIM, 36(5), pp.689~ (1995)
- Das J, , Phys Rev Lett, 94 (2005)
- Yao KF, , Appl Phys Lett, 88 (2006)
- A. Inoue, , Metals, 3, pp.51~ (1993)
- A. Inoue, , Mater. Trans. JIM, 37, pp.1337~ (1996)
- F. Spaepen, , Acta Metall, 25, pp.407~ (1977)
- Schroers J, , Phys Rev Lett, 93 (2004)
- Inoue A, , Philos Mag Lett, 85, pp.221~ (2005)
- A.Inoue,T, , Mater. Trans. JIM, 30, pp.965~ (1989)
- A. Inoue, , Acta Mater, 48, pp.279~ (2000)
- A. Inoue, , Mater. Trans. JIM, 33, pp.937~ (1992)
- A. Inoue, , Mater. Trans. JIM, 36, pp.866~ (1995)
- A. Inoue, , Mater. Trans. JIM, 34, pp.1234~ (1993)
- A. Inoue, , J. Appl Phys, 83 (1998)
- Spaepen, F, "A microscopic mechanism for steady state inhomogeneous flow in metallic glasses", Acta Metall, 25(407) (1977)
- Masumoto T, , Mater Sci Eng, 19, pp.1~ (1975)
- Pampilo CA, , Scripta Met, 6, pp.915~ (1972)
- R. Busch, , J. Appl. Phys, 83, pp.4134~ (1998)
- Y. Kawamura, , Mater. Trans. JIM, 40, pp.794~ (1999)
- A. Masuhr, , Phys. Rev. Lett, 82, pp.2290~ (1999)
- Y. Kawamura, , Appl. Phys. Lett, 77, pp.1114~ (2000)
- 이광석, "Zr계 벌크 비정질 합금의 과냉 액상 영역에서의 변형 거동과 구조 완화의 상관 관계" (2004)
- D.W. Xing, , Materials Letters, 62, pp.44~ (2008)
- W.J. Wright, "Nix, Mater. Sci. Eng., A Struc. Mater.: Prop. Microstruct. Process 319-321 2001.", 319~321 (2001)
- C.T. Liu, , Metal. Mater. Trans, 29A, pp.1811~ (1998)
- Z.F. Zhang, , Acta Mater, 51, pp.1167~ (2003)
- M. Stoica, "Intermetallics 13 ; 764", ~ (2005)