Effect of surface-treatments on flexibility and guided bone regeneration of titanium barrier membrane
0
조회
0
다운로드
5
인용
0
참고문헌
키워드
초록
Titanium barrier membranes are prepared to investigate the effect of surface-treatments, such as machining, electropolishing, anodizing, and electropolishing + TiN coating, on the biocompatibility and physical properties of the membranes. The surface roughness (Ra) of the membrane decreases from machining (0.37 ± 0.09 μm), TiN coating (0.22 ± 0.09 μm), electropolishing (0.20 ± 0.03 μm), to anodizing (0.15 ± 0.03 μm). The highest ductility (24.50 %) is observed for the electropolished Ti membrane. No evidence of causing cell lysis or toxicity is found for the membranes regardless of the surface-treatments. Cell adhesion results of L-929 and MG-63 show that the machined Ti membrane exhibits the highest cell adhesion while the electropolished membrane is the best membrane for the L-929 cell proliferation after 7 days. However, no appreciable difference in MG-63 cell proliferation among variously surface-treated membranes is detected, suggesting that the electropolished Ti membrane is likely to be the best membrane due to the synergic combination of tailored flexibility and excellent fibroblast proliferation.
Abstract
Titanium barrier membranes are prepared to investigate the effect of surface-treatments, such as machining, electropolishing, anodizing, and electropolishing + TiN coating, on the biocompatibility and physical properties of the membranes. The surface roughness (Ra) of the membrane decreases from machining (0.37 ± 0.09 μm), TiN coating (0.22 ± 0.09 μm), electropolishing (0.20 ± 0.03 μm), to anodizing (0.15 ± 0.03 μm). The highest ductility (24.50 %) is observed for the electropolished Ti membrane. No evidence of causing cell lysis or toxicity is found for the membranes regardless of the surface-treatments. Cell adhesion results of L-929 and MG-63 show that the machined Ti membrane exhibits the highest cell adhesion while the electropolished membrane is the best membrane for the L-929 cell proliferation after 7 days. However, no appreciable difference in MG-63 cell proliferation among variously surface-treated membranes is detected, suggesting that the electropolished Ti membrane is likely to be the best membrane due to the synergic combination of tailored flexibility and excellent fibroblast proliferation.
참고문헌 (16)
- C.N. Elias, "Biomedical applications of titanium and its alloys", JOM, 46 (2008)
- Y. Okazaki, "A new Ti-15Zr-4Nb-4Ta alloy for medical applications", Curr. Opinion Solid State Mater. Sci, 5, pp.45~ (2001)
- C.E. Wen, "Processing and mechanical properties of autogenous titanium implant materials", J. Mater. Sci.: Mater. Med, 13, pp.397~ (2002)
- F. Watzinger, "Guided bone regeneration with titanium membranes: A clinical study", British J. Oral. Mixillofac. Surg, 38, pp.312~ (2000)
- E. Kfir, "Immediate bone aug-mentation after infected tooth extraction using titanium membranes", J. Oral. Implantol, 33, pp.133~ (2007)
- B.S. McAllister, "Bone augmentation techniques", J. Periodontol, 78, pp.377~ (2007)
- M. Hong, "Capillary action: Enrichment of retention and habitation of cells via micro-channeled scaffolds for massive bone defect regeneration", J. Mater. Sci.: Mater. Med, 25, pp.1991~ (2014)
- D.S. Oh, "Bone marrow absorption and retention properties of engineered scaffolds with micro-channels and nano-pores for tissue engineering:A proof of concept", Ceram. Intl, 39, pp.8401~ (2013)
- 셀칸 터커, "The Effect of Gamma Radiation Sterilization on Dental Biomaterials", 조직공학과 재생의학, 11(5), pp.341~349 (2014), 한국조직공학과 재생의학회[DOI]
- 김중현, "Rat Defect Models for Bone Grafts and Tissue Engineered Bone Constructs", 조직공학과 재생의학, 10(6), pp.310~316 (2013), 한국조직공학과 재생의학회
- 김진태, "Biocompatibility of Hyaluronic Acid Hydrogels Prepared by Porous Hyaluronic Acid Microbeads", Metals and Materials International, 20(3), pp.555~563 (2014), 대한금속·재료학회[DOI]
- K. Chae, "Application of taguchi method and orthogonal arrays for characterization of corrosion rate of IrO2-RuO2film", J. Mater. Sci, 37, pp.3515~ (2002)
- Y. Song, "Microstructure and chemical properties of c-BN films prepared by ME-ARE", Mater. Sci. Forum, 449-452, pp.465~ (2004)
- E. Kfir, "Immediate bone augmentation after infected tooth extraction using titanium membranes", J. Oral. Implantol, 33, pp.133~ (2007)
- J. Torres, "Platelet-rich plasma may prevent titaniummesh exposure in alveolar ridge augmentation with anorganic bovine bone", J. Clin. Periodontol, 37, pp.943~ (2010)
- W. Zhong, "Augmentation of peri-implant bone defects with different bone grafts and guided bone regeneration: a pilot experimental study in the dog", J. Hard. Tissue Bio, 15, pp.82~ (2006)