Effects of process temperature on the microstructure and magnetic properties of electrodeposited Co-Pt alloy thin films
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Co-Pt alloy thin films were galvanostatically electrodeposited on Ru (30 nm)/Ta (5 nm)/Si (100) substrates from a amino-citrate based electrolyte. We used Ru(0002)-oriented buffer layers to control the crystallinity and orientation of the Co-Pt alloy thin films. The effect of solution temperature on the microstructure and magnetic properties of the Co-Pt alloy thin film was investigated. The samples were characterized by EDS, FESEM, XRD diffractometer using Cu Kα radiation. The magnetic properties of these films were analyzed by a VSM and torque magnetometer. The Co-Pt alloy thin films were exhibited very high out-of-plane coercivity and squareness of the multilayer were 6527 Oe and 0.93, respectively, without heat treatment.
Abstract
Co-Pt alloy thin films were galvanostatically electrodeposited on Ru (30 nm)/Ta (5 nm)/Si (100) substrates from a amino-citrate based electrolyte. We used Ru(0002)-oriented buffer layers to control the crystallinity and orientation of the Co-Pt alloy thin films. The effect of solution temperature on the microstructure and magnetic properties of the Co-Pt alloy thin film was investigated. The samples were characterized by EDS, FESEM, XRD diffractometer using Cu Kα radiation. The magnetic properties of these films were analyzed by a VSM and torque magnetometer. The Co-Pt alloy thin films were exhibited very high out-of-plane coercivity and squareness of the multilayer were 6527 Oe and 0.93, respectively, without heat treatment.
참고문헌 (8)
- R.L. White, "Patterned media: A viable route to 50 Gbit", in and up for magnetic recording?, 1997, pp.33, 990~
- R. Skomski, "Permanent magnetism", Bristol U.K. Institute Physics, 5 (1999)
- H.S. Nalwa, "Magnetic nanostructures", pp.68~ (2002), American Scientific Publisher
- Y. Yamada, "Magnetic properties of electron beam evaporated CoPt alloy thin films", IEEE Trans. Magn, 34, pp.343~ (1998)
- Y. Yamada, "Magnetic properties of electron beam evaporated CoPt alloy thin films", IEEE Trans. Magn, 33, pp.3622~ (1997)
- Y. Yamada, "The origin of large perpendicular magnetic anisotropy observed in Co3Pt alloy thin films", IEEE Trans. Magn, 35, pp.2988~ (1999)
- G. Zangari, "Magnetic properties of electroplated Co-Pt films", J. Magn. Magn. Mater, 157-158, pp.256~ (1996)
- I. Zana, "Magnetic properties of electrodeposited Co-Pt thin films with very high perpendicular magnetic anisotropy", J. Magn. Magn. Mater, 272- 276, pp.1698~ (2004)