Effect of exposure energy dose on lateral resolution and flexural strength of threedimensionally printed dental zirconia
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Purpose. This study aims to evaluate the effects of exposure energy on the lateral resolution and mechanical strength of dental zirconia manufactured using digital light processing (DLP). Materials and methods. A zirconia suspension and a custom top-down DLP printer were used for in-office manufacturing. The viscosity of the suspension and uniformity of the exposed light intensity were controlled. Based on the exposure energy dose delivered to each layer, the specimens were classified into three groups: low-energy (LE), medium-energy (ME), and high-energy (HE). For each energy group, a simplified molar cube was used to measure the widths of the outline (Xo and Yo) and isthmus (Xi and Yi), and a bar-shaped specimen of the sintered body was tested. A Kruskal–Wallis test for the lateral resolution and one-way analysis of variance for the mechanical strength were performed (α = .05). Results. The zirconia green bodies of the ME group showed better lateral resolution than those of the LE and HE groups (both P < .001). Regarding the flexural strength of the sintered bodies, the ME group had the highest mean value, whereas the LE group had the lowest mean value (both P < .05). The ME group exhibited fewer agglomerates than the LE group, with no distinctive interlayer pores or surface defects. Conclusion. Based on these findings, the lateral resolution of the green body and flexural strength of the sintered body of dental zirconia could be affected by the exposure energy dose during DLP. The exposure energy should be optimized when fabricating DLP-based dental zirconia.
Abstract
Purpose. This study aims to evaluate the effects of exposure energy on the lateral resolution and mechanical strength of dental zirconia manufactured using digital light processing (DLP). Materials and methods. A zirconia suspension and a custom top-down DLP printer were used for in-office manufacturing. The viscosity of the suspension and uniformity of the exposed light intensity were controlled. Based on the exposure energy dose delivered to each layer, the specimens were classified into three groups: low-energy (LE), medium-energy (ME), and high-energy (HE). For each energy group, a simplified molar cube was used to measure the widths of the outline (Xo and Yo) and isthmus (Xi and Yi), and a bar-shaped specimen of the sintered body was tested. A Kruskal–Wallis test for the lateral resolution and one-way analysis of variance for the mechanical strength were performed (α = .05). Results. The zirconia green bodies of the ME group showed better lateral resolution than those of the LE and HE groups (both P < .001). Regarding the flexural strength of the sintered bodies, the ME group had the highest mean value, whereas the LE group had the lowest mean value (both P < .05). The ME group exhibited fewer agglomerates than the LE group, with no distinctive interlayer pores or surface defects. Conclusion. Based on these findings, the lateral resolution of the green body and flexural strength of the sintered body of dental zirconia could be affected by the exposure energy dose during DLP. The exposure energy should be optimized when fabricating DLP-based dental zirconia.
참고문헌 (23)
- Alves MFRP, "Microstructural characteristics of 3Y-TZP ceramics and their effects on the flexural strength", Ceramics, 5, pp.798~813 (2022)
- Tunmise Ayode Otitoju, "Advanced ceramic components: Materials, fabrication, and applications", Journal of Industrial and Engineering Chemistry, 85, pp.34~65 (2020), 한국공업화학회[DOI]
- Chen F, "Microstructure and mechanical properties of 3Y-TZP dental ceramics fabricated by selective laser sintering combined with cold isostatic pressing", Int J Lightweight Mater Manuf, 1, pp.239~245 (2018)
- Methani MM, "The potential of additive manufacturing technologies and their processing parameters for the fabrication of all-ceramic crowns : A review", J Esthet Restor Dent, 32, pp.182~192 (2020)
- Cho JH, "Effect of maximum support attachment angle on intaglio surface trueness of anatomic contour monolithic prostheses manufactured by digital light processing and zirconia suspension", J Prosthet Dent, 129, pp.478~485 (2023)
- Meng J, "Crown fit and dimensional accuracy of zirconia fixed crowns based on the digital light processing technology", Ceram Int, 48, pp.17852~17863 (2022)
- Branco AC, "Recent advances on 3D-printed zirconia-based dental materials : a review", Materials(Basel), 16, pp.1860~ (2023)
- 김용규, "Comparative analysis on intaglio surface trueness, wear volume loss of antagonist, and fracture resistance of full-contour monolithic zirconia crown for single-visit dentistry under simulated mastication", The Journal of Advanced of Prosthodontics, 14(3), pp.173~181 (2022), 대한치과보철학회[DOI]
- Li R, "Accuracy of zirconia crowns manufactured by stereolithography with an occlusal full-supporting structure : An in vitro study", J Prosthet Dent, S0022-3913(22), pp.00064~00066 (2022)
- Mitteramskogler G, "Light curing strategies for lithography-based additive manufacturing of customized ceramics", Addit Manuf, 1(4), pp.110~118 (2014)
- Chaudhary R, "Additive manufacturing by digital light processing : a review", Prog Addit Manuf, 8, pp.331~351 (2023)
- Wu X, "Research progress of the defects and innovations of ceramic vat photopolymerization", Addit Manuf, 65, pp.103441~ (2023)
- Gentry SP, "Light scattering in absorbing ceramic suspensions : Effect on the width and depth of photopolymerized features", J European Ceram Soc, 35, pp.1895~1904 (2015)
- Sun J, "3D printing of zirconia via digital light processing : optimization of slurry and debinding process", J European Ceram Soc, 40, pp.5837~5844 (2020)
- Sun Y, "High-quality translucent alumina ceramic through digital light processing stereolithography method", Adv Eng Mater, 23, pp.2001475~ (2021)
- Yun Y, "Mechanism of ceramic slurry light scattering affecting contour accuracy and method of projection plane correction", Ceram Int, 49, pp.15024~15033 (2023)
- Zhang X, "Additive manufacturing of zirconia ceramics : a state-of-the-art review", J Mater Res Technol, 9, pp.9029~9048 (2020)
- Schweiger J, "3D printing of zirconia-what is the future?", Curr Oral Health Rep, 6, pp.339~343 (2019)
- Patil A, "Wear behaviour of lithography ceramic manufactured dental zirconia", BMC Oral Health, 23, pp.276~ (2023)
- Xiang D, "Dental zirconia fabricated by stereolithography: accuracy, translucency and mechanical properties in different build orientations", Ceram Int, 47, pp.28837~28847 (2021)
- Zandinejad A, "The flexural strength and flexural modulus of stereolithography additively manufactured zirconia with different porosities", J Prosthodont, 31, pp.434~440 (2022)
- Bove A, "Photopolymerization of ceramic resins by stereolithography process : a review", Appl Sci, 12, pp.3591~ (2022)
- Conti L, "Effects of the layer height and exposure energy on the lateral resolution of zirconia parts printed by lithography-based additive manufacturing", Materials(Basel), 13, pp.1317~ (2020)