안정화 원소 Ti 첨가에 따른 스테인리스강의 해수 내 캐비테이션-침식 특성
Cavitation-erosion characteristics of the stainless steel with adding Ti stabilizer element in sea water
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Stainless steel is widely applied in many industrial fields due to its excellent anti-corrosion and durability characteristics. However, stainless steel is very vulnerable to cavitation attack caused by high speed flow of fluid in the chloride environments such as marine environment. These conditions promote intergranular corrosion and cavitation-erosion, leading to degradation of the structural integrity and service life. In order to prevent these problems, the stabilized stainless steel is applied to the offshore and shipbuilding industries. In this study, Ti was added to 19%Cr-9%Ni as the stabilizer element with different concentrations (0.26%, 0.71%), and their durabilities were evaluated with cavitation-erosion experiment by a modified ASTM G32 method. The microstructural change was observed with the stabilizer element contents. The result of the observation indicated that the amount of carbide precipitation was decreased and its size became finer with increasing Ti content. In the cavitation-erosion experiment, both weight loss and surface damage depth represented an inverse proportional relationship with the amount of Ti element. Consequently, the stainless steel containing 0.71% of Ti had excellent durability characteristics.
Abstract
Stainless steel is widely applied in many industrial fields due to its excellent anti-corrosion and durability characteristics. However, stainless steel is very vulnerable to cavitation attack caused by high speed flow of fluid in the chloride environments such as marine environment. These conditions promote intergranular corrosion and cavitation-erosion, leading to degradation of the structural integrity and service life. In order to prevent these problems, the stabilized stainless steel is applied to the offshore and shipbuilding industries. In this study, Ti was added to 19%Cr-9%Ni as the stabilizer element with different concentrations (0.26%, 0.71%), and their durabilities were evaluated with cavitation-erosion experiment by a modified ASTM G32 method. The microstructural change was observed with the stabilizer element contents. The result of the observation indicated that the amount of carbide precipitation was decreased and its size became finer with increasing Ti content. In the cavitation-erosion experiment, both weight loss and surface damage depth represented an inverse proportional relationship with the amount of Ti element. Consequently, the stainless steel containing 0.71% of Ti had excellent durability characteristics.
참고문헌 (16)
- K. R. Kim, "A Surface Study of 304 and 316 Stainless Steel Oxidized Between 300℃ and 500℃", J. Kor. Inst. Surf. Eng, 32(1), pp.43~48 (1999)
- D. Pecker, "Handbook of Stainless Steel", pp.15~ (1987), McGraw-Hill
- 최한철, "Shot-peening 표면처리된 Ti함유 스테인리스강의 응력균열부식", 한국표면공학회지, 37(6), pp.350~359 (2004), 한국표면공학회
- W. H. Kearnes, "Welding Hand book: Metals and Their Weldability", pp.104~ (1982), American Welding Society
- E. R. Hwang, "A Study on the Intergranular Corrosion Behavior of Stainless Steels in Molten Carbonate Salt by EPR Test", J. Kor. Inst. Surf. Eng, 31(4), pp.223~230 (1998)
- "Standard ASTM A240", A240M: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications, 2010, pp.1~14
- 최용원, "해수 내 캐비테이션-침식 저항성에 미치는 스테인리스강의 Nb 첨가의 영향", 한국표면공학회지, 49(3), pp.274~279 (2016), 한국표면공학회[DOI]
- "Annual Book of ASTM standards G32-92, Standard Method of Vibratory Cavitation Erosion Test", ASTM International, 119~ (2004)
- J. E. Spruiell, "Microstructural Stability of Thermal-Mechanically Pretreated Type 316 Austenitic Stainless Steel", Metall. Mater. Trans. A, 4(6), pp.1533~1544 (1973)
- G. Bregliozzi, "Cavitation Wear Behaviour of Austenitic Stainless Steels with Different Grain Sizes", Wear, 258, pp.503~510 (2005)
- G. R. Wang, "Weld Thermal Cycle and Precipitation Effects in Ti-V-Containing HSLA Steels", Metall. Mater. Trans. A, 20(10), pp.2093~2100 (1989)
- W. C. Leith, "Some Corrosion Effects in Accelerated Cavitation Damage", J. Basic Eng, 82(4), pp.795~802 (1960)
- J. F. Santa, "Slurry Erosion of Thermal Spray Coatings and Stainless Steels for Hydraulic Machinery", Wear, 263, pp.258~264 (2007)
- 김성종, "5000계열 Al 합금의 캐비테이션 특성에 관한 워터 캐비테이션 피닝의 영향", 해양환경안전학회지, 18(5), pp.481~487 (2012), 해양환경안전학회[DOI]
- O. Takakuwa, "Estimation of the Depth of Surface Modification Layer Induced by Cavitation Peening", J. Mater. Process. Technol, 212(8), pp.5268~5276 (2013)
- 이승준, "해양환경 하에서 Ni-Cr계 자용성 합금 코팅된 ALBC3 합금의 캐비테이션 특성 평가", 해양환경안전학회지, 19(5), pp.538~544 (2013), 해양환경안전학회[DOI]