해양 환경 하에서 16.7Cr-10Ni-2Mo 스테인리스강의 표면 손상에 미치는 캐비테이션의 영향
Effect of cavitation on surface damage of 16.7Cr-10Ni-2Mo stainless steel in marine environment
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Stainless steel is generally known to have characteristics of excellent corrosion resistance and durability, but in a marine environment it can suffer from localized corrosion due to the breakdown of passivity film due to chloride ion in seawater. Furthermore, the damage behaviors are sped up under a cavitation environment because of complex damage from electrochemical corrosion and cavitation-erosion. In this study the characteristics of electrochemical corrosion and cavitation erosion behavior were evaluated on 16.7Cr-10Ni-2Mo stainless steel under a cavitation environment in natural seawater. The electrochemical experiments have been conducted at both static conditions and dynamic conditions inducing cavitation with different current density parameters. The surface morphology and damage behaviors were compared after the experiment. After the cavitation test with time variables morphological examinations on damaged specimens were analyzed by using a scanning electron microscope and a 3D microscope. the galvanostatic experiment gave a cleaner surface morphology presented with less damage depth at high current density regions. It is due to the effect of water cavitation peening under the cavitation condition. In the cavitation experiment, with amplitude of 30 ㎛ and seawater temperature of 25 ℃, weight loss and cavitation-erosion damage depth were dramatically increased after 5 hours inducing cavitation.
Abstract
Stainless steel is generally known to have characteristics of excellent corrosion resistance and durability, but in a marine environment it can suffer from localized corrosion due to the breakdown of passivity film due to chloride ion in seawater. Furthermore, the damage behaviors are sped up under a cavitation environment because of complex damage from electrochemical corrosion and cavitation-erosion. In this study the characteristics of electrochemical corrosion and cavitation erosion behavior were evaluated on 16.7Cr-10Ni-2Mo stainless steel under a cavitation environment in natural seawater. The electrochemical experiments have been conducted at both static conditions and dynamic conditions inducing cavitation with different current density parameters. The surface morphology and damage behaviors were compared after the experiment. After the cavitation test with time variables morphological examinations on damaged specimens were analyzed by using a scanning electron microscope and a 3D microscope. the galvanostatic experiment gave a cleaner surface morphology presented with less damage depth at high current density regions. It is due to the effect of water cavitation peening under the cavitation condition. In the cavitation experiment, with amplitude of 30 ㎛ and seawater temperature of 25 ℃, weight loss and cavitation-erosion damage depth were dramatically increased after 5 hours inducing cavitation.
참고문헌 (20)
- T. Oshima, , ISIJ Inter, 47, pp.359~ (2007)
- G. Okamoto, , Corros. Sci, 13, pp.471~ (1973)
- T. Momma, , Wear, 186, pp.425~ (1995)
- A. J. Sedriks, "Corrosion of stainless steels", pp.115~ (1996), John Wiley & Sons
- D. A. Jones, "Principles and prevention of corrosion", pp.415~ (1996), Prentice Hall
- I. R. Jones, , J. Fluid Mech, 7, pp.596~ (1960)
- C. MaCaul, , Proceedings of the Corrosion 96 Research Topical Symposia, pp.24~ (1996), NACE
- 임명환, "해수와 청수환경에서 선박용 원심펌프 임펠러 재료의 캐비테이션 특성", CORROSION SCIENCE AND TECHNOLOGY, 10(6), pp.218~224 (2011), 한국부식방식학회
- "ASTM Standard G32-92, Standard Method of Vibratory Cavitation Erosion Test", Annual Book of ASTM Standards, ~ (1992)
- M. Qin, , Surf. Coat. Technol, 201, pp.1409~ (2006)
- 박재철, "해양환경 하에서 동합금의 캐비테이션-부식손상 방지를 위한 방식정전류 기법 연구", 한국표면공학회지, 45(1), pp.25~30 (2012), 한국표면공학회
- 김성종, "동합금의 워터캐비테이션피닝에 의한 내구성과 부식특성 평가", CORROSION SCIENCE AND TECHNOLOGY, 11(5), pp.184~190 (2012), 한국부식방식학회
- 김성종, "5052-O 알루미늄 합금의 워터 캐비테이션 피닝 시간에 따른 표면 경화와 부식 특성에 관한 연구", CORROSION SCIENCE AND TECHNOLOGY, 11(4), pp.151~156 (2012), 한국부식방식학회
- K. Sato, , Proceedings of 11th International Conference on Jet Cutting Technology (1992)
- P. Peyre, , Mater. Sci. Eng, A208, pp.294~ (2000)
- K. Masaki, , Mater. Sci. Res. Int, 4, pp.200~ (1998)
- S. J. Kim, , Curr. Appl. Phys, 12, pp.S24~ (2012)
- 장석기, "해수 환경 하에서 304 스테인리스강의 캐비테이션 조건에 따른 특성 평가", 한국표면공학회지, 45(6), pp.278~283 (2012), 한국표면공학회[DOI]
- H. Mochizuki, , Wear, 262, pp.522~ (2007)
- G. Bregliozzi, , Wear, 258, pp.503~ (2005)