해수 환경에서 슈퍼 오스테나이트 스테인리스강의 전기화학적 거동에 미치는 캐비테이션 진폭의 영향
Effect of Cavitation Amplitude on the Electrochemical Behavior of Super Austenitic Stainless Steels in Seawater Environment
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The cavitation and potentiodynamic polarization experiments were conducted simultaneously to investigate the effect of cavitation amplitude on the super austenitic stainless steel (UNS N08367) electrochemical behavior in seawater. The results of the potentiodynamic polarization experiment under cavitation condition showed that the corrosion current density increased with cavitation amplitude increase. Above oxygen evolution potential, the current density in a static condition was the largest because the anodic dissolution reaction by intergranular corrosion was promoted. In the static condition, intergranular corrosion was mainly observed. However, damage caused by erosion was observed in the cavitation environment. The micro-jet generated by cavity collapse destroyed the corrosion product and promoted the repassivation. So, weight loss occurred the most in static conditions. After the experiment, wave patterns were formed on the surface due to the compressive residual stress caused by the impact pressure of the cavity. Surface hardness was improved by the water cavitation peening effect, and the hardness value was the highest at 30 μm amplitude. UNS N08367 with excellent mechanical performance due to its high hardness showed that cavitation inhibited corrosion damage.
Abstract
The cavitation and potentiodynamic polarization experiments were conducted simultaneously to investigate the effect of cavitation amplitude on the super austenitic stainless steel (UNS N08367) electrochemical behavior in seawater. The results of the potentiodynamic polarization experiment under cavitation condition showed that the corrosion current density increased with cavitation amplitude increase. Above oxygen evolution potential, the current density in a static condition was the largest because the anodic dissolution reaction by intergranular corrosion was promoted. In the static condition, intergranular corrosion was mainly observed. However, damage caused by erosion was observed in the cavitation environment. The micro-jet generated by cavity collapse destroyed the corrosion product and promoted the repassivation. So, weight loss occurred the most in static conditions. After the experiment, wave patterns were formed on the surface due to the compressive residual stress caused by the impact pressure of the cavity. Surface hardness was improved by the water cavitation peening effect, and the hardness value was the highest at 30 μm amplitude. UNS N08367 with excellent mechanical performance due to its high hardness showed that cavitation inhibited corrosion damage.
참고문헌 (28)
- Kevin Li, "Determinants of ship operators’ options for compliance with IMO 2020", Transportation Research Part D: Transport and Environment, 86, pp.102459~ (2020), Elsevier BV[DOI]
- Nader R. Ammar, "Eco-environmental analysis of ship emission control methods: Case study RO-RO cargo vessel", Ocean Engineering, 137, pp.166~173 (2017), Elsevier BV[DOI]
- L. Dahl, "Corrosion in flue gas desulfurization plants and other low temperature equipment", Materials and Corrosion, 1992, pp.43(6), 292~[DOI]
- 황현규, "슈퍼오스테나이트 스테인리스강의 해수환경에서 온도에 따른 전기화학적 특성", CORROSION SCIENCE AND TECHNOLOGY, 20(6), pp.391~402 (2021), 한국부식방식학회[DOI]
- S. Ghosh, "Effect of Chloride and Phosphoric Acid on the Corrosion of Alloy C-276, UNS N08028, and UNS N08367", CORROSION, 61(6), pp.609~619 (2005), NACE International[DOI]
- James D. Fritz, "Chloride stress corrosion cracking resistance of 6% Mo stainless steel alloy (UNS N08367)", Desalination, 135, pp.93~ (2001), Elsevier BV[DOI]
- Ahmad Ivan Karayan, "Transpassivity characterization of the alloy UNS N08367 in a chloride-containing solution", Journal of Solid State Electrochemistry, 18(11), pp.3191~3202 (2014), Springer Science and Business Media LLC[DOI]
- 황현규, "Al 6061-T6 합금의 해수 내 캐비테이션 진폭에 따른 캐비테이션-침식 조건하에서 전기화학적 특성", CORROSION SCIENCE AND TECHNOLOGY, 19(6), pp.318~325 (2020), 한국부식방식학회[DOI]
- D.M. García-García, "Effect of cavitation on the corrosion behaviour of welded and non-welded duplex stainless steel in aqueous LiBr solutions", Corrosion Science, 48(9), pp.2380~2405 (2006), Elsevier BV[DOI]
- R.M. Fernández-Domene, "Repassivation of the damage generated by cavitation on UNS N08031 in a LiBr solution by means of electrochemical techniques and Confocal Laser Scanning Microscopy", Corrosion Science, 52(10), pp.3453~3464 (2010), Elsevier BV[DOI]
- 장익준, "Ultrasonic Cavitation Behavior and its Degradation Mechanism of Epoxy Coatings in 3.5 % NaCl at 15 oC", CORROSION SCIENCE AND TECHNOLOGY, 20(1), pp.26~36 (2021), 한국부식방식학회[DOI]
- R. Sriram, "Pitting Corrosion of Duplex Stainless Steels", CORROSION, 45(10), pp.804~810 (1989), NACE International[DOI]
- R. Magnabosco, "Pit Morphology and Its Relation to Microstructure of 850°C Aged Duplex Stainless Steel", CORROSION, 61(2), pp.130~136 (2005), NACE International[DOI]
- Masao Sakashita, "The effect of molybdate anion on the ion-selectivity of hydrous ferric oxide films in chloride solutions", Corrosion Science, 17(6), pp.473~486 (1977), Elsevier BV[DOI]
- 김영식, "Synergistic Effect of Nitrogen and Molybdenum on Localized Corrosion of Stainless Steels", CORROSION SCIENCE AND TECHNOLOGY, 9(1), pp.20~28 (2010), 한국부식방식학회
- Hyun Young Chang, "Compatibility Evaluation for Application of Lean Duplex Stainless Steels to Seawater Systems in Nuclear Power Plants", Materials Science Forum, 654-656, pp.382~385 (2010), Trans Tech Publications, Ltd.[DOI]
- M.D. Asaduzzaman, "Effects of concentration of sodium chloride solution on the pitting corrosion behavior of AISI 304L austenitic stainless steel", Chemical Industry and Chemical Engineering Quarterly, 17(4), pp.477~483 (2011), National Library of Serbia[DOI]
- Seong-Jong Kim, "Effects of water cavitation peening on electrochemical characteristic by using micro-droplet cell of Al–Mg alloy", Current Applied Physics, 12, pp.S24~S30 (2012), Elsevier BV[DOI]
- Seong-Jong Kim, "Electrochemical characteristics under cavitation-erosion for STS 316L in seawater", Materials Research Bulletin, 58, pp.244~247 (2014), Elsevier BV[DOI]
- 김성종, "동합금의 워터캐비테이션피닝에 의한 내구성과 부식특성 평가", CORROSION SCIENCE AND TECHNOLOGY, 11(5), pp.184~190 (2012), 한국부식방식학회
- Osamu Takakuwa, "Suppression of fatigue crack propagation with hydrogen embrittlement in stainless steel by cavitation peening", Strength, Fracture and Complexity, 7(1), pp.79~85 (2011), IOS Press[DOI]
- P.Veerabhadra Rao, "Evaluation of epoxy resins in flow cavitation erosion", Wear, 122(1), pp.77~96 (1988), Elsevier BV[DOI]
- A. Karimi, "Cavitation erosion of materials", International Metals Reviews, 31(1), pp.1~26 (1986), Informa UK Limited[DOI]
- B.N. Mordyuk, "Effect of structure evolution induced by ultrasonic peening on the corrosion behavior of AISI-321 stainless steel", Materials Science and Engineering: A, 458(1-2), pp.253~261 (2007), Elsevier BV[DOI]
- Siaw Foon Lee, "Pitting corrosion induced on high-strength high carbon steel wire in high alkaline deaerated chloride electrolyte", Nanotechnology Reviews, 11(1), pp.973~986 (2022), Walter de Gruyter GmbH[DOI]
- R. Wang, "Effect of ultrasound on initiation, growth and repassivation behaviours of pitting corrosion of SUS 304 steel in NaCl aqueous solution", Corrosion Engineering, Science and Technology, 51(3), pp.201~210 (2016), Maney Publishing[DOI]
- Daoming Sun, "Pitting corrosion behavior of stainless steel in ultrasonic cell", Electrochimica Acta, 54(5), pp.1558~1563 (2009), Elsevier BV[DOI]
- Georgii S. Vasyliev, "Pitting Suppression of AISI 316 Stainless Steel Plates in Conditions of Ultrasonic Vibration", International Journal of Chemical Engineering, 2020, pp.1~7 (2020), Hindawi Limited[DOI]