Strength Increase of Medium Temperature-carbonized PAN Nano Fibers Made by Mechano-electrospinning
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, the effect of phosphoric acid (PA) as a fiber spinning aid on the strength increase of polyacrylonitrile (PAN) nano-fibers by using modified mechano-electrospinning technologies has been analyzed. The medium carbonization temperature of 800°C has been selected for the future economic production of these new materials. The concentration of PAN in dimethyl sulfoxide (DMSO) was fixed as 5 wt%. The weight fraction of PA was selected as being 2%, 4%, 6%, and 8% in comparison to PAN. These solutions have been used to make the nanofibers. The mechano-electrospinning apparatus installed in KRICT was made by our own design. By using this apparatus the continous and highly aligned precursor nano-fibers have been obtained. The bundle of 50 well aligned nano diameter continuous fibers with the diametr of 10 microns with 6 wt% phosphoric acid for addition showed maximum mechanical properties of 1.6 GPa as tensile strength and 300 GPa as Young’s modulus. The weight of final product can be increased 19%, which can improve the economical benefits for the application of these new materials.
Abstract
In this study, the effect of phosphoric acid (PA) as a fiber spinning aid on the strength increase of polyacrylonitrile (PAN) nano-fibers by using modified mechano-electrospinning technologies has been analyzed. The medium carbonization temperature of 800°C has been selected for the future economic production of these new materials. The concentration of PAN in dimethyl sulfoxide (DMSO) was fixed as 5 wt%. The weight fraction of PA was selected as being 2%, 4%, 6%, and 8% in comparison to PAN. These solutions have been used to make the nanofibers. The mechano-electrospinning apparatus installed in KRICT was made by our own design. By using this apparatus the continous and highly aligned precursor nano-fibers have been obtained. The bundle of 50 well aligned nano diameter continuous fibers with the diametr of 10 microns with 6 wt% phosphoric acid for addition showed maximum mechanical properties of 1.6 GPa as tensile strength and 300 GPa as Young’s modulus. The weight of final product can be increased 19%, which can improve the economical benefits for the application of these new materials.
참고문헌 (27)
- Morgan, P., "Carbon Fibers and Their Composites" (2005), Taylor & Francis
- He, J. H., "Electrospun Nanofibers and Their Application", pp.6~7 (2008), Smither
- Greiner, A., "Electrospinning : A Fascinating Method for the Preparation of Ultrathin Fibers", Angewandte Chemie International Edition, 46, pp.5670~5703 (2007)
- Gu, S. Y., "Process Optimization and Empirical Modeling for Electrospun Polyacrylonitrile (PAN) Nanofiber Precursor of Carbon Nanofibers", European Polymer Journal, 41, pp.2259~2568 (2005)
- Yeo, L. Y., "Electrospinning Carbon Nanotube Polymer Composite Nanofibers", Journal of Experimental Nanoscience, 1(2), pp.177~209 (2006)
- Baumgarten, P. K., "Electrostatic Spinning of Acrylic Microfibers", Journal of Colloid Interface Science, 36, pp.71~ (1971)
- Fromhals, A., "Process and Apparatus for Preparing Artificial Threads, US Patent No. 1,975,504", ~ (1934)
- Gladding, E. K., "Apparatus for the Production of Filaments, Threads and the Like, US Patent No. 2,168,027", ~ (1939)
- Yarin, A. L., "Bending Instability in Electrospinning of Nanofibers", Journal of Applied Physics, 89, pp.3018~3026 (2001)
- Ramakrishna, S., "Electrospun Nanofibers : Solving Golbal Issues", Materials Today, 9(3), pp.40~50 (2006)
- Kong, C. S., "Nano-web Formation by the Electrospinning at Various Electric Fields", Journal of Materials Science, 42, pp.8106~8112 (2007)
- Im, J. S., "Preparation of PAN-based electrospun nanofiber webs containing TiO2 for photocatalytic degradation", MATERIALS LETTERS, 62, pp.3652~3655 (2008), ELSEVIER SCIENCE BV
- Dzenis, Y., "Spinning Continuous Fibers for Nanotechnology", Science, 304(25), pp.1917~1919 (2004)
- Fennessey, S. F., "Fabrication of Aligned and Molecularly Oriented Electrospun Polyacrylonitrile Nanofibers and the Mechanical Behavior of Their Twisted Yarns", Polymer, 45, pp.4217~4225 (2004)
- Zhou, Z., "Development of Carbon Nanofibers from Aligned Electrospun Polyacrylonitrile Nanofiber Bundles and Characterization of Their Microstructural, Electrical, and Mechanical Properties", Polymer, 50, pp.2999~3006 (2009)
- Smit, E., "Continuous Yarns From Electron Fibers", Polymer, 46, pp.2419~2423 (2005)
- 박수진, "전기방사 공정을 이용한 극세 PAI 연속사 제조 방법에 관한 연구", 공업화학, 17(3), pp.331~334 (2006), 한국공업화학회
- Lee, S. H., "Processing of continuous poly(amide-imide) nanofibers by electrospinning", POLYMER INTERNATIONAL, 59, pp.212~217 (2010), JOHN WILEY & SONS LTD
- Rahaman, M. S. A., "A Review of Heat Treatment on Polyacrylonitrile Fiber", Polymer Degradation and Stability, 92, pp.1421~1432 (2007)
- Moon, S. C., "Strong Electrospun Nanometerdiameter Polyacrylonitrile Carbon Fiber Yarns", Carbon, 47, pp.2829~2839 (2009)
- Wu, S., "Preparation of PAN-based Carbon Nanofibers by Hot-stretching", Composite Interfaces, 15(7), pp.671~677 (2008)
- Chen, J. C., "Modification of Polyacrylonitrile(PAN)Carbon Fiber Precursor Via Post-spinning Plasticization and Stretching in Dimethyl Formamide(DMF)", Carbon, 40, pp.25~45 (2002)
- Nataraj, S. K., "Effect of Added Nickel Nitrate on the Physical, Thermal and Morphological Charateristics of Polyacrylonitrile-based Carbon Nanofibers", Materials Science and Engineering B, 162, pp.75~81 (2009)
- Nataraj, S. K., "Morphological Characterization of Electronspun Carbon Nanofiber Mats of Polyacrylonitrile Containing Heteropolyacids", Synthetic Metals, 157, pp.1496~1504 (2009)
- Zhou, Z., "Graphitic Carbon Nanofibers Developed From Bundles of Aligned Electrospun Polyacrylonitrile Nanofibers Containing Phosphoric Acid", Polymer, 51, pp.2360~2367 (2010)
- Park, S. J., "Effect of Acidic Anode Treatment on Carbon Fibers for Increasing Fiber-matrix Adhesion and Its Relationship to Interlaminar Shear Strength of Composites", Journal of Materials Science, 35, pp.1901~1905 (2000)
- Lu, W., "Oxidation Protection of Carbon Materials by Acid Phosphate Impregnation", Carbon, 40, pp.1249~1254 (2002)